Automobile paint cleaning and repair agent and preparation method thereof

A repair agent and car paint technology, applied in the field of paint repair, can solve problems such as very high requirements for operation skills, difficulty in balancing cleaning and repair functions, and difficulty for ordinary consumers to grasp, so as to ensure uniform quality and save repair costs and construction cost effects

Active Publication Date: 2019-08-09
陈丽瑜
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Most of the car paint cleaning and repairing agents currently on the market are oil-soluble and contain toxic solvents, and it is difficult to balance the cleaning and repairing functions
The existing technology mainly improves the self-drying and quick-drying of the paint film, but most of them require professional painting tools and use compressed air to spray; and it is necessary to match colors for different car paint colors, which requires very high operating skills. hard to master

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Automobile paint cleaning and repair agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A cleaning and repairing agent for automobile paint surface of the present embodiment is composed of the following components by weight: 6 parts of fatty alcohol polyoxyethylene ether, 10 parts of oleic acid diethanolamide borate, 1.8 parts of sodium alginate, 10 parts of xylene parts, 4 parts of dimethylformamide, 2 parts of dimethyl silicone oil, 2.7 parts of self-healing filler, 55 parts of diluent; wherein, the diluent consists of acetone, ethyl acetate, toluene, cyclopentanone according to the mass ratio of 3:2 :1:1 mixed and stirred.

[0039] The preparation method of the self-healing filler is as follows:

[0040] 1) In parts by weight, add 52 parts of mesoporous silica to 290 parts of deionized water, centrifuge for 4 minutes to obtain a dispersion of mesoporous silica, raise the temperature to 115°C, add 70 parts of hydroxyethyl chitosan, and Stir at -0.16MPa for 25 minutes to obtain a mixed solution; wherein, the particle size of mesoporous silica is 250-280n...

Embodiment 2

[0049] A cleaning and repairing agent for automobile paint surface of the present embodiment is composed of the following components by weight: 5 parts of fatty alcohol polyoxyethylene ether, 8 parts of oleic acid diethanolamide borate, 2.3 parts of sodium alginate, 12 parts of xylene parts, 5 parts of dimethylformamide, 3 parts of dimethyl silicone oil, 3 parts of self-healing filler, and 58 parts of diluent. Wherein, the diluent is formed by mixing and stirring acetone, ethyl acetate, toluene, and cyclopentanone according to a mass ratio of 3:2:1:1.

[0050] The preparation method of the self-healing filler is as follows:

[0051] 1) In parts by weight, add 53 parts of mesoporous silica to 300 parts of deionized water, centrifuge for 4.2 minutes to obtain a dispersion of mesoporous silica, raise the temperature to 120°C, add 72 parts of hydroxyethyl chitosan, and Stir for 30 minutes under vacuum degree -0.18MPa to obtain a mixed solution; among them, the particle size of me...

Embodiment 3

[0060] A cleaning and repairing agent for automobile paint surface of the present embodiment is composed of the following components by weight: 7 parts of fatty alcohol polyoxyethylene ether, 11 parts of oleic acid diethanolamide borate, 3 parts of sodium alginate, 12 parts of xylene parts, 6 parts of dimethylformamide, 4 parts of simethicone, 3.1 parts of self-healing filler, and 60 parts of diluent. Wherein, the diluent is formed by mixing and stirring acetone, ethyl acetate, toluene, and cyclopentanone according to a mass ratio of 3:2:1:1.

[0061] The preparation method of the self-healing filler is as follows:

[0062] 1) In parts by weight, add 58 parts of mesoporous silica to 305 parts of deionized water, centrifuge for 5 minutes to obtain a dispersion of mesoporous silica, heat up to 120°C, add 72 parts of hydroxyethyl chitosan, and Stir for 30min at -0.2MPa to obtain a mixed solution; wherein, the particle size of mesoporous silica is 250-280nm, and the specific surf...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Pore volumeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an automobile paint cleaning and repair agent and a preparation method thereof. The cleaning and repair agent is prepared from fatty alcohol-polyoxyethylene ether as a non-ionic surface active agent, diglycolamide oleate borate as a corrosion-inhibition repair agent, sodium alga acid as an excipient, xylene as a wax removal agent, dimethyl formamide as a purifying agent, simethicone as a defoaming agent, a diluent composed of multiple organic solvents and independently developed self-repair filler through mixing, stirring, vacuum defoamation and stirring. After the cleaning and repair agent is sprayed on scratches of an automobile, automobile paint is not damaged, the cleaning and repair agent is compatible with automobile surface varnish, after scratch pits are automatically filled with the automobile paint cleaning and repair agent and the automobile paint cleaning and repair agent is leveled to form a film, obvious stains and scratches cannot be seen by the eyes, the automobile paint is not damaged, one-time cleaning and repair of the automobile paint are completed, and the automobile scratch repair cost and the construction cost are saved.

Description

technical field [0001] The invention relates to the technical field of paint surface repair, in particular to an automobile paint surface cleaning and repairing agent and a preparation method thereof. Background technique [0002] With the rapid development of the automobile industry, the automobile-related maintenance industry continues to develop on a large scale. The automobile body generally has a paint film structure. Decorative effect. After the paint surface of the car is damaged, it usually needs to be repaired by spraying and drying with professional equipment in a professional auto repair shop, which requires high repair technology, and improper handling will cause particles, air bubbles, and sags. [0003] The Chinese patent application number 201410157926.1 discloses an automatic projectile paint surface repair agent, which is composed of a filling and film forming agent, a penetrating agent, a brightener, a wax remover, a purifying agent, a slip agent, a paint ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C11D1/72C11D3/00C11D3/12C11D3/18C11D3/20C11D3/22C11D3/32C11D3/37C11D3/60
CPCC11D1/72C11D3/0073C11D3/124C11D3/187C11D3/2072C11D3/2093C11D3/222C11D3/32C11D3/3707C11D3/373
Inventor 汪安源陈和平
Owner 陈丽瑜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com