Preparation method of ceramsite light water permeable brick road

A technology of permeable bricks and ceramsite, which is applied in the production of ceramic products, clay products, and ceramic materials. It can solve problems such as low mechanical strength, loose foundation, and poor water permeability, and achieve high water permeability, increased lubricity, and air permeability. enhanced effect

Inactive Publication Date: 2019-08-09
宜昌朗天新型建材有限公司
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the deficiencies of the prior art, and provide a preparation method of ceramsite lightweight permeable bricks, which solves the problem of poor water permeability and low mechanical strength of lightweight permeable bricks in the prior art, which is difficult for long-term use. Afterwards, it is easy to loose the foundation caused by the water permeability of the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of ceramsite light water permeable brick road

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A preparation method of ceramsite lightweight permeable brick, comprising the following steps,

[0027] S1 First mix 10kg cement, 5kg straw particles, 20kg high-alkaline shale ceramsite (density 700kg / m3), 5kg burnt lime powder, 0.2kg polycarboxylic acid, 0.5kg methylcellulose, and then add 50kg Part of sludge slurry (water content is 80%) was stirred for 2min, and then left to stand for 1h;

[0028] S2 Add 0.2kg of polyurethane particles to the product in S1, place it under 8MPa and pressurize it for 0.5h, then take it out and let it stand for 6h;

[0029] In S3, the product obtained in S2 is calcined at 600° C. for 2 hours, and then naturally cooled to 80° C. for 12 hours.

[0030] In the above steps, the particle size of straw particles is 2 mm, the particle size of ceramsite is 3 mm, and the particle size of polyurethane particles is 2 mm.

Embodiment 2

[0032] A preparation method of ceramsite lightweight permeable brick, comprising the following steps,

[0033] S1 First mix 15kg cement, 8kg straw granules, 30kg high alkali shale ceramsite (density 800kg / m3), 10kg burnt lime powder, 0.6kg melamine, 0.8kg carboxymethyl cellulose, and then add 60kg sludge The slurry (with a water content of 85%) was stirred for 4 minutes, and then left to stand for 2 hours;

[0034] In S2, add 0.6kg of polystyrene particles to the product in S1, place it under 10MPa and pressurize it for 1 hour, then take it out and let it stand for 7 hours;

[0035] In S3, the product obtained in S2 was calcined at 700°C for 2h, and then cooled naturally to 100°C for 18h.

[0036] In the above steps, the particle diameter of straw particles is 4mm, the particle diameter of high alkali shale ceramsite is 6mm, and the particle diameter of polystyrene particles is 4mm.

Embodiment 3

[0038] A preparation method of ceramsite lightweight permeable brick, comprising the following steps,

[0039] S1 Mix 20kg of cement, 10kg of straw particles, 35kg of high alkali shale ceramsite (density 900kg / m3), 15kg of burnt lime powder, 1kg of melamine, and 1kg of carboxypropyl methylcellulose, and then add 70kg of sludge The slurry (with a water content of 90%) was stirred for 6 minutes, and then left to stand for 3 hours;

[0040] S2 Add 1 kg of polyvinyl chloride particles to the product in S1, place it under 12MPa and pressurize it for 1.5 hours, then take it out and let it stand for 8 hours;

[0041] In S3, the product obtained in S2 was calcined at 800°C for 3h, and then naturally cooled to 120°C for 24h.

[0042] In the above steps, the grain size of straw particles is 6 mm, the grain size of high alkali shale ceramsite is 10 mm, and the grain size of polyvinyl chloride is 6 mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a ceramsite light water permeable brick road. The method comprises the following steps that S1, firstly, cement, straw particles, ceramsite, overburntlime, a water reducing agent and a water retaining agent are mixed to be uniform, then, mud is added for stirring for 2-6 min, and then standing is performed for 1-3 h; S2, foamed particles are addedinto the product obtained in S1, the mixture is placed under the pressure of 8-12 MPa for pressurizing treatment for 0.5-1.5 h, and then the mixture is taken out for standing under the temperature of90-120 DEG C for 6-8 h; S3, the product obtained in S2 is placed under the temperature of 600-800 DEG C for calcinating for 2-3 h, then, the product is taken out for natural cooling to 80-120 DEG C for maintaining for 12-24 h. The prepared light water permeable brick solves the problems that in the prior art, a light water permeable brick is poor in water permeability and low in mechanical strength, and a foundation is loose due to the fact that water is likely to permeate the material after long-term use.

Description

technical field [0001] The invention relates to the technical field of environmental protection building materials, in particular to a preparation method of ceramsite lightweight permeable bricks. Background technique [0002] Lightweight permeable brick is a new type of environmentally friendly building material. It is often used in squares, parking lots, sidewalks, and roads with small traffic volume and load, such as building and community roads, non-motorized lanes of municipal roads and other pavement projects. It has good water permeability and air permeability, which can quickly infiltrate rainwater into the ground, replenish soil water and groundwater, maintain soil moisture, improve the living conditions of urban ground plants and soil microorganisms, and can adjust the temperature and humidity of local space on the surface, which is very important for regulating urban microclimate. 1. It has a great effect on alleviating the urban heat island effect, and reduces th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B38/06C04B38/08
CPCC04B33/1321C04B33/1328C04B38/0675C04B38/08C04B38/067C04B2235/656C04B2235/6567C04B2235/3208C04B2235/96Y02P40/60
Inventor 易举然
Owner 宜昌朗天新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com