Preparation method of metal organic complex material for malachite green enrichment and sensing

A metal-organic, malachite green technology, applied in chemical instruments and methods, analytical materials, material excitation analysis, etc., can solve the problems of undiscovered patent publications, etc., achieve good thermal stability and chemical stability, and simple synthesis process. , the effect of strong adsorption performance

Active Publication Date: 2019-07-26
TIANJIN UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Through the search, no patent publications related to the patent application of the present invention have been found

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of metal organic complex material for malachite green enrichment and sensing
  • Preparation method of metal organic complex material for malachite green enrichment and sensing
  • Preparation method of metal organic complex material for malachite green enrichment and sensing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A method for preparing a metal-organic complex material for malachite green enrichment and sensing, the steps are as follows:

[0031] ⑴ Add copper nitrate, nitrogen-containing dicarboxylic acid ligand and 1,3,5-benzenetricarboxylic acid to the N,N-dimethylformamide solution, ultrasonically dissolve the reactants for 30 minutes, and then put them into a polytetrafluoroethylene container. In a stainless steel reactor, react at 80°C for 12h.

[0032] Wherein, the N,N-dimethylformamide:copper nitrate ratio mL:mol is 10-20:2.2, copper nitrate, nitrogen-containing dicarboxylic acid ligand and 1,3,5-trimellitic acid ligand The molar ratio of the body is 2.2:1:1;

[0033] (2) The material obtained by the reaction in step (1) is washed twice with N,N-dimethylformamide, washed three times with methanol, and dried at 100° C. overnight to obtain the metal-organic complex material.

[0034] The nitrogen-containing dicarboxylic acid ligands in the step (1) are 2,6-naphthalene dica...

Embodiment 2

[0036] A method for preparing a metal-organic complex material for malachite green enrichment and sensing, the steps are as follows:

[0037] ⑴Add cadmium nitrate, nitrogen-containing dicarboxylic acid ligand and 1,3,5-tris(4-carboxyphenyl)benzene to the N,N-dimethylformamide solution, and ultrasonically dissolve the reactants for 30 minutes before loading Put it into a polytetrafluoroethylene stainless steel reactor and react at 120°C for 36h.

[0038] Wherein, the N,N-dimethylformamide: cadmium nitrate ratio mL:mol is 10-20:3, cadmium nitrate, nitrogen-containing dicarboxylic acid ligand and 1,3,5-tri(4-carboxy The molar ratio of phenyl)benzene is 3:1:1;

[0039] (2) Wash the material obtained in step (1) with N,N-dimethylformamide for 3 times, methanol for 3 times, and dry at 80° C. overnight to obtain the metal-organic complex material.

[0040] The nitrogen-containing dicarboxylic acid ligands in the step (1) are 2,6-naphthalene dicarboxylic acid, azobenzene-3,3-dicarbo...

Embodiment 3

[0042] A method for preparing a metal-organic complex material for malachite green enrichment and sensing, the steps are as follows:

[0043] ⑴ Add cadmium nitrate, 2,6-naphthalene dicarboxylic acid and tricarboxylic acid ligands to the N,N-dimethylformamide solution, ultrasonicate for 30 minutes to completely dissolve the reactants, and then put them into a polytetrafluoroethylene stainless steel reactor , reacted at 130°C for 12h.

[0044] Wherein, the ratio of N,N-dimethylformamide:cadmium nitrate mL:mol is 10-20:4, and the molar ratio of cadmium nitrate, 2,6-naphthalene dicarboxylic acid and tricarboxylic acid ligand is 4 :1.5:1;

[0045] (2) Wash the material obtained in step (1) with N,N-dimethylformamide for 3 times, methanol for 3 times, and dry at 80° C. overnight to obtain the metal-organic complex material.

[0046] In the step (1), the tricarboxylic acid ligand is 1,3,5-tris(4-carboxyphenyl)benzene, 1,3,5-tris(4'-carboxy[1,1'-biphenyl]-4 -yl) benzene, 1,3,5-trim...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a metal organic complex material for malachite green enrichment and sensing. The preparation method comprises: adding a nitrate, a nitrogenous dicarboxylic acid ligand and a tricarboxylic acid ligand into N,N-dimethylformamide, ultrasonically treating for 10-50 min so that the reactive materials are fully dissolved, pouring into a polytetrafluoroethylene stainless steel reactor, and allowing to react at 80-130 DEG C for 12-36 h; washing the attained material, and drying to obtain the metal organic complex material. The metal organic complex material prepared via the preparation method is a mesoporous material, having high thermal stability and good aqueous stability, having mesopore features and surface special groups, having high adsorbingcapacity and many active sites, can highly adsorb malachite green, can greatly enrich malachite green, can still enrich malachite green after being placed in room-temperature dry environments, allowsproduction cost to be reduced greatly, and has a good application prospect.

Description

technical field [0001] The invention belongs to the technical field of preparation of functionalized materials, in particular to a method for preparing a metal-organic complex material used for enrichment and sensing of malachite green. Background technique [0002] Metal-organic complexes are one-dimensional, two-dimensional or three-dimensional coordination polymers composed of metal ions or clusters connected with organic ligands. In the past 20 years, metal-organic complex materials have attracted a large number of scientific researchers to continuously develop and innovate in their synthesis because of their various exquisite and interesting structures. At the same time, as a kind of porous material, the various structures of metal-organic complex materials make it widely used. Metal-organic complex materials cleverly combine inorganic and organic chemistry to produce properties that traditional porous materials do not have. [0003] Malachite Green (Malachite Green) ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/22B01J20/30G01N21/33G01N21/64C02F1/28C02F101/38
CPCB01J20/223C02F1/285G01N21/33G01N21/6402C02F2101/38
Inventor 邓启良吴晨李燕丽王硕
Owner TIANJIN UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com