Epoxy resin rubber clothes composition, epoxy resin composite board, and preparation method thereof

A technology of epoxy resin glue and epoxy resin, which is applied in the fields of epoxy resin gel coat composition and epoxy resin composite board

Active Publication Date: 2019-07-09
BYD CO LTD
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the gel coat requires an adhesion promoter to form good adhesion to the composite

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] 1) Epoxy resin gel coat composition:

[0067] Gel coat component A: liquid bisphenol A epoxy resin (NPEL-128): 100 parts by weight, defoamer (AFCONA-7201): 2 parts by weight, leveling agent (AFCONA-7300): 1 part, wetting Dispersant (BYK-W996): 0.66 parts by weight, filler (GR608A): 64 parts by weight, thixotropic agent (AEROSIL380): 2 parts by weight, thixotropic enhancer (AFCONA-7530): 0.4 parts by weight.

[0068] Gel coat component B: curing agent A (JH-5400): 10 parts by weight. Curing agent B (GG-6688): 14 parts by weight.

[0069] Stir the liquid bisphenol A epoxy resin, defoamer, leveling agent and wetting and dispersing agent in component A of the gel coat evenly; slowly add the filler and disperse evenly; then add the thixotropic agent and thixotropic enhancer and Stir evenly; then add to a three-roll mill for grinding to obtain component A of the gel coat.

[0070] Stir curing agent A and curing agent B evenly to obtain component B of the gel coat.

[0071...

Embodiment 2

[0078] 1) Epoxy resin gel coat composition:

[0079] Gel coat component A: liquid bisphenol A epoxy resin (NPEL-128): 100 parts by weight, defoamer (AFCONA-7201): 2.2 parts by weight, leveling agent (AFCONA-7300): 1.1 parts by weight, Wet dispersant (BYK-W996): 0.6 parts by weight, filler (GR608A): 110 parts by weight, thixotropic agent (AEROSIL 380): 1.8 parts by weight, thixotropic enhancer (AFCONA-7530): 1.4 parts by weight, titanium dioxide : 2 parts by weight, black paste (Stan-ToneTM90EPX50Black by PolyOne): 0.26 parts by weight.

[0080] Gel coat component B: curing agent A (JH-5400): 5 parts by weight, curing agent B (JH-5472): 20 parts by weight.

[0081]Stir the liquid bisphenol A epoxy resin, defoamer, leveling agent and wetting and dispersing agent in component A of the gel coat evenly; slowly add black color paste, titanium dioxide, and then the filler and disperse evenly; then add Stir the thixotropic agent and thixotropic enhancer evenly; then add it into a th...

Embodiment 3

[0090] 1) Epoxy resin gel coat composition:

[0091] Gel coat component A: liquid bisphenol A epoxy resin (NPEL-128): 100 parts by weight, defoamer (AFCONA-7201): 0.3 parts by weight, leveling agent (AFCONA-7300): 0.3 parts by weight, Wet dispersant (BYK-W996): 2.2 parts by weight, metal powder (aluminum from Hefei Xuyang Aluminum Pigment Co., Ltd., 200 mesh): 60 parts by weight, thixotropic agent (AEROSIL 380): 2.2 parts by weight, thixotropic enhancer (AFCONA-7530): 0.3 parts by weight.

[0092] Gel coat component B: curing agent A (JH-5400): 15 parts by weight, curing agent B (JH-5472): 15 parts by weight.

[0093] Stir the liquid bisphenol A epoxy resin, defoamer, leveling agent and wetting and dispersing agent in component A of the gel coat evenly; slowly add the filler and disperse evenly; then add the thixotropic agent and thixotropic enhancer and Stir evenly; then add to a three-roll mill for grinding to obtain component A of the gel coat.

[0094] Stir curing agent...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of epoxy resin composite material, and discloses an epoxy resin rubber clothes composition, an epoxy resin composite board, and a preparation method thereof. The composition comprises, by weight, 100 parts of a base epoxy resin, 20 to 30 parts of a curing agent, 0.3 to 2.2 parts of an antifoaming agent, 0.3 to 1.1 parts of a leveling agent, 0.6 to 2.2 parts of awetting dispersing agent, 60 to 110 parts of a filler, 1.8 to 2.2 parts of a thixotropic agent, 0.3 to 1.4 parts of a thixotropic enhancer, and 0 to 3 parts of an optional pigment; the base epoxy resin is a liquid bisphenol A epoxy resin with an epoxy equivalent of 184 to 194 g / eq, and viscosity of 10,000 to 15,000cps at 25 DEG C, the curing agent including a curing agent A and a curing agent B, the curing agent A is a fatty amine with an active hydrogen equivalent of 50 to 60 g / eq; the curing agent B is an alicyclic amine with an active hydrogen equivalent of 40 to 95 g / eq; and the weight ratio of the curing agent A to the curing agent B is 1: (1-4). Excellent adhesion performance with glass fiber reinforced epoxy resin composite materials is provided, and the composite board is providedwith better surface processing performance.

Description

technical field [0001] The invention relates to the field of epoxy resin composite materials, in particular to an epoxy resin gel coat composition, an epoxy resin composite board formed by combining the epoxy resin gel coat composition with glass fiber reinforced epoxy resin composite materials, and The preparation method of the composite board. Background technique [0002] Glass fiber reinforced epoxy resin is a good composite material, but the surface hardness is high and it is difficult to process the surface of the product. [0003] CN104149361A discloses a manufacturing method of a carbon fiber composite material propeller by overmolding. In this method, the carbon fiber is coated on the metal propeller hub, and then the composite molding of the propeller is further carried out. During the molding process, the gel coat resin is sprayed on the mold. Gel coat resin used to insulate the mold from the composite material, composition not disclosed. [0004] CN103895290A ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L63/00C08J5/12C08K7/00C08K7/14
CPCC08J5/12C08J2363/00C08J2463/00C08L63/00C08L2205/025C08L2205/03C08L2205/035C08L83/04C08K7/00C08K7/14
Inventor 周维段平平张晓宇
Owner BYD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com