Method for preparing graphite-phase carbon nitride visible-light-induced photocatalyst through copolymerization of 2-aminoterephthalic acid and amine compound

An amino terephthalic acid, graphitic carbon nitride technology, applied in nitrogen and non-metallic compounds, physical/chemical process catalysts, chemical instruments and methods, etc. problems such as low catalytic activity, to achieve the effects of low cost, optimized chemical composition, and simple synthesis process

Active Publication Date: 2019-06-14
XI AN JIAOTONG UNIV
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But g-C 3 N 4 The internal layers are not arranged strictly according to the ideal graphite phase, but the layers are stacked, so the actual specific surface area is often low, and the electron-hole pairs generated by photoexcitation recombine too fast and cannot effectively reduce hydrogen ions.
The above reasons lead to g-C 3 N 4 The photocatalytic activity of the photocatalyst is low, and it is urgent to find effective modification methods to further improve the photocatalytic hydrogen production capacity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing graphite-phase carbon nitride visible-light-induced photocatalyst through copolymerization of 2-aminoterephthalic acid and amine compound
  • Method for preparing graphite-phase carbon nitride visible-light-induced photocatalyst through copolymerization of 2-aminoterephthalic acid and amine compound
  • Method for preparing graphite-phase carbon nitride visible-light-induced photocatalyst through copolymerization of 2-aminoterephthalic acid and amine compound

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] 10 g of urea and 0.5 mg of 2-aminoterephthalic acid were dissolved in 20 mL of deionized water to form a transparent mixed solution, which was stirred and evaporated to dryness in a water bath at 70°C. The resulting mixture was ground evenly in a mortar, added to a 50mL crucible with a cover, and then the crucible was placed in an ash furnace, and the temperature was raised from room temperature to 550 °C at a heating rate of 5 °C / min, kept for 4 hours, and naturally cooled to room temperature . That is, a new type of graphite-phase carbon nitride copolymerized is obtained, and the performance test is to be performed.

Embodiment 2

[0040] 10 g of urea and 1 mg of 2-aminoterephthalic acid were dissolved in 20 mL of deionized water to form a transparent mixed solution, which was stirred and evaporated to dryness in a water bath at 70°C. The resulting mixture was ground evenly in a mortar, added to a 50mL crucible with a cover, and then the crucible was placed in an ash furnace, and the temperature was raised from room temperature to 550 °C at a heating rate of 5 °C / min, kept for 4 hours, and naturally cooled to room temperature . That is, a new type of graphite-phase carbon nitride copolymerized is obtained, and the performance test is to be performed.

Embodiment 3

[0042]10 g of urea and 3 mg of 2-aminoterephthalic acid were dissolved in 20 mL of deionized water to form a transparent mixed solution, which was stirred and evaporated to dryness in a water bath at 70°C. The resulting mixture was ground evenly in a mortar, added to a 50mL crucible with a cover, and then the crucible was placed in an ash furnace, and the temperature was raised from room temperature to 550 °C at a heating rate of 5 °C / min, kept for 4 hours, and naturally cooled to room temperature . That is, a new type of graphite-phase carbon nitride copolymerized is obtained, and the performance test is to be performed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing a graphite-phase carbon nitride visible-light-induced photocatalyst by copolymerization of 2-aminoterephthalic acid and an amine compound. The method comprises the following steps: uniformly mixing the amine compound and the 2-aminoterephthalic acid to obtain mixed powder, and calcining the mixed powder at 520-600 DEG C to obtain the graphite-phase carbon nitride visible-light-induced photocatalyst. The preparation method is simple, and the obtained novel graphite-phase carbon nitride has better visible light catalytic hydrogen production performance compared with original carbon nitride.

Description

technical field [0001] The invention relates to a method for preparing a graphite-phase carbon nitride visible light catalyst by copolymerizing 2-aminoterephthalic acid and an amine compound, and belongs to the field of energy material preparation and photocatalysis. Background technique [0002] Today's human society is facing two major problems of energy and environment. Energy shortage and environmental pollution seriously restrict the development of human society. On the one hand, the rapid development of society has made human beings have an increasing demand for energy, and the energy we currently use is still dominated by traditional fossil fuels, but because of the non-renewability of fossil fuels, they will be exhausted one day. On the other hand, the combustion of fossil fuels has caused serious environmental pollution and harm to the environment, such as the greenhouse effect, acid rain, photochemical smog, etc., which pose a serious threat to human survival. The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/24B01J37/08C01B21/082C01B3/04
CPCY02E60/36
Inventor 师进文程诚毛柳浩郭烈锦
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com