Degradable trace lubricating oil and preparation method thereof
A technology of lubricating oil and lubricating oil composition, applied in the field of lubrication, can solve the problems of environmentally unfriendly sulfur and chlorine-containing additives, affecting the health of operators, processing sites and environmental pollution, etc., achieving excellent biodegradability, Good degradation performance and good biodegradability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0024] Weigh 500g of phosphoric acid with an effective concentration of 20%, and add 250g of chitosan into the reaction kettle together, stir and heat to 160°C, fully react for 4 hours, drain water every 1 hour during the reaction, drain the remaining water after the reaction, add and weigh 250g of lauric acid is heated up to 240°C, stirred and heated for 6 hours, and the moisture generated by the reaction is discharged, which is a lubricating oil composition.
[0025] Weigh 300g of the lubricating oil composition prepared above, 400g of propylene glycol dicaprate, 200g of epoxidized soybean oil, and 100g of organic molybdenum, mix and stir at 40°C until it becomes transparent, then it is a degradable trace lubricating oil.
[0026] The preparation method of the above-mentioned organic molybdenum: Weigh 100g oleamide, 20g molybdic acid, and 20g hydroxyethylethanolamine and mix them at 80°C for 2 hours, then raise the temperature to 120°C and reduce pressure (keep the pressure i...
Embodiment 2
[0028] Take by weighing 333g of phosphoric acid with an effective concentration of 30%, add by weighing 350g of chitosan into the reaction kettle together, stir and heat to 200°C, fully react for 3 hours, drain water every 1 hour in the middle of the reaction, and discharge the remaining water after the reaction, that is It is a lubricating oil composition.
[0029] Weigh 200g of the lubricating oil composition prepared above, 500g of propylene glycol dicaprate, 150g of epoxidized soybean oil, and 150g of organic molybdenum, mix and stir at 50°C until translucent, then it is a degradable trace lubricating oil.
[0030] The preparation method of the above organic molybdenum: Weigh 100g oleamide, 25g molybdic acid, and 15g hydroxyethylethanolamine and mix them at 100°C for 1 hour, then raise the temperature to 110°C and reduce pressure (keep the pressure in the container not greater than 100mmHg) and stir for 3 hours, The brown liquid obtained after filtering the precipitate is ...
Embodiment 3
[0032] Weigh 400g of phosphoric acid with an effective concentration of 25%, and add 300g of chitosan into the reaction kettle together, stir and heat to 180°C, fully react for 3.5 hours, drain water once every 1.5 hours during the reaction, drain the remaining water after the reaction, add the weighed 450g of myristic acid is heated up to 220°C, stirred and heated for 7 hours, and the moisture generated by the reaction is discharged, which is a lubricating oil composition.
[0033] Weigh 250g of the lubricating oil composition prepared above, 450g of propylene glycol dicaprate, 200g of epoxidized soybean oil, and 100g of organic molybdenum, mix and stir at 50°C until it becomes transparent, then it becomes a degradable trace lubricating oil.
[0034] The preparation method of the above-mentioned organic molybdenum: Weigh 100g oleamide, 22g molybdic acid, and 18g hydroxyethylethanolamine, mix them at 90°C for 1.5 hours, then raise the temperature to 112°C and reduce pressure (k...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
modulus | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap