A kind of precursor and the method and application of preparing carbon nanomaterial

A carbon nanomaterial and precursor technology, applied in the field of nanomaterials, can solve the problems of large volume expansion rate of iron oxide, complex preparation method, poor cycle performance, etc., and achieve the effects of high versatility, simplified synthesis process, and mild reaction conditions.

Active Publication Date: 2021-04-20
BEIJING INSTITUTE OF TECHNOLOGYGY
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The preparation method is relatively complicated, and the reaction temperature is high
[0008] Chinese patent CN201810995604.2 discloses a biomass carbon / iron oxide composite material for lithium battery negative electrode and its preparation method, which solves the problems of large volume expansion rate and poor cycle performance of lithium battery negative electrode material iron oxide

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of precursor and the method and application of preparing carbon nanomaterial
  • A kind of precursor and the method and application of preparing carbon nanomaterial
  • A kind of precursor and the method and application of preparing carbon nanomaterial

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] 1. Preparation of carbon nanomaterials

[0050]Dissolve 5.0g of ethylene glycol citrate, 2.0g of carboxymethylcellulose ammonium, and 5.0g of ferric nitrate nonahydrate in 100mL of water, stir evenly, and concentrate the liquid to 8mL at 120°C. Then the mixed gel-like liquid was placed in a 300 mL cylindrical ceramic crucible with a cover, and the crucible was placed in a constant temperature furnace at 300° C., and taken out after 5 minutes to obtain carbon nanomaterials.

[0051] After testing by the applicant, the SEM photos of the obtained carbon nanomaterials are as follows: figure 1 Shown, N 2 The adsorption-desorption curve and pore size distribution are as follows: figure 2 As shown, the Raman spectrum is shown as image 3 shown. It can be seen from the figure that the obtained carbon nanomaterial is a porous material composed of carbon nanofibers and carbon nanosheets, and its Brunauer–Emmett–Teller (BET) specific surface area is 202.5m 2 / g, which is at ...

Embodiment 2

[0057] 1. Preparation of carbon nanomaterials

[0058] Dissolve 5.0g of ethylene glycol citrate, 1.0g of carboxymethylcellulose ammonium, and 5.0g of manganese nitrate tetrahydrate in 50mL of water, stir evenly, and concentrate the liquid to 10mL at 120°C. Then the mixed gel-like liquid was placed in a 300 mL cylindrical ceramic crucible with a cover, and the crucible was placed in a constant temperature furnace at 350° C., and was taken out after 3 minutes to obtain a carbon nanomaterial.

[0059] After testing by the applicant, the SEM photos of the obtained carbon nanomaterials are as follows: Figure 4 Shown, N 2 The adsorption-desorption curve and pore size distribution are as follows: Figure 5 As shown, the Raman spectrum is shown as Image 6 shown. It can be seen from the figure that the obtained carbon nanomaterial is a porous material composed of carbon nanofibers and carbon nanosheets, and its BET specific surface area is 282.9m 2 / g, which is at 1360cm -1 and...

Embodiment 3

[0065] 1. Preparation of carbon nanomaterials

[0066] Dissolve 5.0g of ethylene glycol citrate, 1.0g of carboxymethylcellulose lithium, and 8.0g of nickel nitrate hexahydrate in 50mL of water, stir well, and concentrate the liquid to 10mL at 120°C. Then the mixture was placed in a 300mL cylindrical ceramic crucible with a cover, and the crucible was placed in a constant temperature furnace at 400°C, and it was taken out after 2 minutes.

[0067] After testing by the applicant, the SEM photos of the obtained carbon nanomaterials are as follows: Figure 7 Shown, N 2 The adsorption-desorption curve and pore size distribution are as follows: Figure 8 As shown, the Raman spectrum is shown as Figure 9 shown. It can be seen from the figure that the obtained carbon nanomaterial is a porous material composed of carbon nanofibers and carbon nanosheets, and its BET specific surface area is 350.6m 2 / g, which is at 1360cm -1 and 1589cm -1 Two distinct Raman peaks are shown, belo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
current efficiencyaaaaaaaaaa
Login to View More

Abstract

A precursor comprises the following components in parts by weight: 5 parts of ethylene glycol citrate; 1-2 parts of water-soluble cellulose; and 1-10 parts of metal nitrate. The method for preparing carbon nanomaterials is as follows: 1) taking materials in proportion, dissolving them in water and mixing them evenly, and concentrating to obtain a mixed solution; 2) putting the mixed solution obtained in step 1) into a reaction vessel, and heating the mixture under the condition of 250-400° C. The reaction was carried out for 1-10min to obtain carbon nanomaterials. The obtained carbon nanometer material can be used as an energy storage active material of an electrode sheet, and can be used to prepare a high-performance capacitor or a lithium ion battery.

Description

technical field [0001] The invention relates to the field of nanomaterials, in particular to a precursor and a method and application for preparing carbon nanomaterials. Background technique [0002] Due to their excellent chemical stability, remarkable electrical conductivity, and unique micro / nanostructure, carbon nanomaterials are considered as potential alternative materials in the fields of polymer industry, environmental treatment, heterogeneous catalysis, and advanced electronic devices. When carbon nanomaterials have a porous structure, high specific surface area, hybrid structure, and proper heteroatom doping, their energy storage performance becomes particularly prominent and competitive. [0003] Currently, different methods, such as hydrothermal carbonization (HTC), template-assisted carbonization, electrochemical deposition, and powder carbonization, have been developed to synthesize different types of nanocarbon materials from various organic precursors. Howev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B32/15H01M4/587H01M10/0525
CPCY02E60/10
Inventor 邵自强李磊陈垦王飞俊王文俊王建全刘建新
Owner BEIJING INSTITUTE OF TECHNOLOGYGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com