High-photocatalytic-activity single-phase ferroelectric nano-material and preparation method thereof

A nanomaterial, catalytically active technology, applied in the field of catalytic new energy materials, can solve the problems of limited practical application and low absorption efficiency

Active Publication Date: 2019-05-14
XINYANG NORMAL UNIVERSITY
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Obviously TiO 2 The absorption efficiency for the solar spectrum is too low, which greatly limits its practical application
In addition, TiO 2 The internal photogenerated electron-hole pair recombination rate is also high, which inhibits the further improvement of its photocatalytic activity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-photocatalytic-activity single-phase ferroelectric nano-material and preparation method thereof
  • High-photocatalytic-activity single-phase ferroelectric nano-material and preparation method thereof
  • High-photocatalytic-activity single-phase ferroelectric nano-material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] The application also provides chemical formula as [Bi 2 o 2 ][(Bi 0.9 SM 0.1 )(Fe 0.5 Nb 1.5 )O 7 ] The preparation method of the nanometer material, it may further comprise the steps:

[0032] Add the bismuth source, samarium source, iron source and niobium source into the diluted acid solution according to the stoichiometric ratio, and stir for half an hour to obtain a uniform mixed solution;

[0033] The homogeneous mixed solution was neutralized by adding alkali solution dropwise, and the final alkali concentration of the mixed solution was adjusted to 3mol / L, and the final volume was adjusted to 80mL, and then the obtained yellow suspension was transferred to a polytetrafluoroethylene with a volume of 100mL In the ethylene reactor, put the reactor into an oven at last, and conduct heat treatment under certain conditions to obtain the target powder;

[0034] The obtained target powder is repeatedly centrifuged, washed to neutrality, and then dried to obtain t...

Embodiment 1

[0043] (1) According to the molecular formula stoichiometric ratio weighing 1.8756g purity is 99% bismuth nitrate pentahydrate, 0.0448g purity is 99% samarium nitrate, 0.2693g purity is 98.5% iron nitrate nonahydrate and 0.3198g trihydrate pentoxide Diniobium was added successively to 20 mL of dilute nitric acid with a concentration of 4 mol / L, and the stirring was continued for half an hour to obtain a homogeneous mixture.

[0044] (2) The above-mentioned homogeneous mixed solution was neutralized by dropping sodium hydroxide solution, and the final alkali concentration of the mixed solution was guaranteed to be 3 mol / L by accurately controlling the added sodium hydroxide content (11.36 g), and the final volume was 80 mL. The resulting yellow suspension was then transferred to a polytetrafluoroethylene reactor with a capacity of 100 mL. Finally, put the reactor into an oven, set the heat treatment temperature at 200° C., and the heat treatment time at 72 hours.

[0045] (3) ...

Embodiment 2

[0054] (1) according to molecular formula stoichiometric ratio weighing 1.8756g purity is 99% bismuth nitrate pentahydrate, 0.0448g purity is 99% samarium nitrate, 0.2693g purity is 98.5% ferric nitrate nonahydrate and 0.5403g niobium pentachloride Then add 20 mL of dilute nitric acid with a concentration of 4 mol / L in sequence, and continue stirring for half an hour to obtain a uniform mixed solution.

[0055] (2) The above-mentioned homogeneous mixed solution was neutralized by dropping sodium hydroxide solution, and the final alkali concentration of the mixed solution was guaranteed to be 3 mol / L by accurately controlling the added sodium hydroxide content (11.36 g), and the final volume was 80 mL. The resulting yellow suspension was then transferred to a polytetrafluoroethylene reactor with a volume of 100 mL. Finally, put the reactor into an oven, set the heat treatment temperature at 200° C., and the heat treatment time at 72 hours.

[0056] (3) The powder obtained by hyd...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention provides a high-photocatalytic-activity single-phase ferroelectric nano-material and a preparation method thereof. Fluorite structural layers [Bi2O2]2+ and perovskite-like titanium ore layers [(Bi0.9Sm0.1)(Fe0.5Nb1.5)O7]2<-> are alternately stacked along a C direction to form the nano-material. The single-phase nano-material has structure characteristics, so that a built-in electricfield generated by ferroelectric spontaneous polarization induction is present in the single-phase nano-material, the nano-material has high light absorption in a visible region by a crack of a 3d rail of a Fe element in an iron oxide octahedron. By the aid of two characteristics, the single-phase nano-material has efficient photo-degradation activity for colored organic pollutant rhodamine B andcolorless organic pollutant salicylic acid in the visible region. The invention further provides a synthetic method of the nano-material.

Description

technical field [0001] The invention relates to the technical field of catalytic new energy materials, in particular to a ferroelectric nanometer material with high photocatalytic activity and a preparation method thereof. Background technique [0002] In recent years, environmental pollution has become increasingly serious, and water pollution, especially industrial printing and dyeing wastewater, has posed a great threat to the sustainable and healthy development of human society. According to statistics, 100-200 tons of water is consumed per ton of textile printing and dyeing, of which 80-90% become waste water. Textile printing and dyeing wastewater has the characteristics of large water volume, high content of organic pollutants, and high alkalinity, and is one of the most difficult industrial wastewater to treat. How to effectively remove a large number of organic pollutants in printing and dyeing wastewater is a key step in solving wastewater pollution. Photocatalyt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/843C02F1/30C02F103/30
Inventor 殷小丰孙书杰程念雷宝田永尚赵珂李渊
Owner XINYANG NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka