Environmentally-friendly superfine fiber non-woven facial mask cloth and making method thereof

A technology of ultra-fine fiber and manufacturing method, applied in the field of non-woven fabrics, can solve the problems of unstable raw materials, poor skin-friendly effect, expensive price, etc. Excellent performance

Inactive Publication Date: 2019-05-07
杭州海拓皮革有限公司
View PDF19 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Product 1, in the process of long-term use by users, the skin-friendly effect of this product is relatively poor in terms of user experience;
[0009] Product 2, the product is effective, but the raw material is unstable and the price is too expensive;
[0010] Product 3, this product has good strength, but the skin sticking effect is average, the reduction rate is high, and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmentally-friendly superfine fiber non-woven facial mask cloth and making method thereof
  • Environmentally-friendly superfine fiber non-woven facial mask cloth and making method thereof
  • Environmentally-friendly superfine fiber non-woven facial mask cloth and making method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A kind of environment-friendly microfiber non-woven facial mask base cloth is manufactured by the following method:

[0046] (1) The raw materials are mixed according to the following ratio:

[0047] A, brocade / polyester 70 / 30 island-in-the-sea superfine short fibers (nylon / polyester 70 / 30 represent nylon content 70%, polyester content 30%, the following representations are the same), 3D*51mm, weight ratio 10%;

[0048] B. Nylon / polyester 20 / 80 split ultrafine short fibers, 2D*51mm, 90% by weight;

[0049] (2) After opening, carding, web laying, spunlace process, drying, and winding, a spunlace composite nonwoven fabric with a gram weight of 60 g / m2 is obtained. The spunlace process uses full cross spunlace, The width of the door is 160cm, and the spunlace pressure of the spunlace unit is 40, 60, 90, 100, 120, 120 kg in sequence;

[0050] (3) Spunlace composite forming non-woven fabrics for weight reduction, process conditions: NaOH solution 40g / L, temperature 95°C, t...

Embodiment 2

[0054] A kind of environment-friendly microfiber non-woven facial mask base cloth is manufactured by the following method:

[0055] (1) The raw materials are mixed according to the following ratio:

[0056] A. Nylon / polyester 70 / 30 sea-island superfine short fiber, 3D*51mm, weight ratio 10%;

[0057] B. Nylon / polyester 30 / 70 split ultrafine short fiber, 2D*51mm, 90% by weight;

[0058] (2) After opening, carding, web laying, spunlace process, drying, and winding, a spunlace composite nonwoven fabric with a gram weight of 55 grams per square meter is obtained. In the spunlace process, full cross spunlace is used. The door width is 160cm, and the spunlace pressure of the spunlace unit is 40, 70, 90, 100, 110, and 130 kg in sequence;

[0059] (3) Spunlace composite forming non-woven fabrics for weight reduction, process conditions: NaOH solution 35g / L, temperature 95°C, time 50 minutes, weight reduction accelerator 3g / L,

[0060] (4) Combined use of pressure washing and ultras...

Embodiment 3

[0063] A kind of environment-friendly microfiber nonwoven fabric is manufactured by the following method:

[0064] (1) The raw materials are mixed according to the following ratio:

[0065] A. Nylon / polyester 70 / 30 sea-island superfine short fiber, 3D*51mm, weight ratio 50%;

[0066] B. Nylon / polyester 15 / 85 split ultrafine short fiber, 2D*51mm, weight ratio 50%;

[0067] (2) After opening, carding, web laying, spunlace process, drying, and winding, a spunlace composite nonwoven fabric with a gram weight of 60 g / m2 is obtained. The spunlace process uses full cross spunlace, The door width is 160cm, and the spunlace pressure of the spunlace unit is 40, 70, 90, 100, 110, and 130 kg in sequence;

[0068] (3) Spunlace composite forming non-woven fabrics for weight reduction, process conditions: NaOH solution 25g / L, temperature 95°C, time 45 minutes, weight reduction accelerator 2g / L;

[0069] (4) Pressure washing, after cleaning NaOH and decrementing accelerator, hot air penetr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of non-woven clothes, in particular to an environmentally-friendly superfine fiber non-woven facial mask cloth and a making method thereof. Sea-island typeand splitting type super-thin short fibers are mixed according to a proportion, carded and laid into a fiber net with a uniform gram weight, a matched non-woven spunlaced composite strengthening technology is used for forming a composite spunlaced non-woven cloth, and the non-woven cloth is used for making the environmentally-friendly superfine fiber non-woven facial mask cloth according to a tension-free fiber splitting technology. The environmentally-friendly superfine fiber non-woven facial mask cloth has the advantage of being well attached and being skin-friendly.

Description

technical field [0001] The invention relates to the technical field of nonwoven fabrics, in particular to an environment-friendly superfine fiber nonwoven facial mask cloth and a manufacturing method thereof. Background technique [0002] Mask is a common facial beauty care product. Generally, the base cloth is used to infiltrate the prepared essence. After laying on the face for a short time, it temporarily isolates the outside air and pollution, promotes the secretion and metabolism of sweat glands, and makes the skin oxygenated. The increase in the amount is beneficial for the skin to eliminate the products of epidermal cell metabolism and accumulated oily substances. At the same time, the moisture and maintenance ingredients in the mask penetrate into the stratum corneum of the epidermis, making the skin soft and naturally bright and elastic. [0003] Among the masks in the current market, except for coated masks such as kaolin and seaweed mud, most of the remaining mask...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04H1/4382D04H1/492D06M11/38
Inventor 胡明礼
Owner 杭州海拓皮革有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More