A kind of preparation method of iron-nickel battery negative electrode material

An iron-nickel battery and negative electrode material technology, applied in nickel batteries, battery electrodes, alkaline battery electrodes, etc., can solve the problems of self-discharge, poor negative rate performance, low gram capacity, etc., and achieve lower electrode impedance and high gram capacity. , the effect of increasing the surface area

Active Publication Date: 2021-02-05
YANGZHOU UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, iron-nickel batteries on the market generally have problems such as low gram capacity, poor negative electrode rate performance, and self-discharge.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of iron-nickel battery negative electrode material
  • A kind of preparation method of iron-nickel battery negative electrode material
  • A kind of preparation method of iron-nickel battery negative electrode material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0025] Add 0.5 g of carbon nanotubes, 1.0 g of graphene, 3.6 g of calcium hydroxide, and 93 g of nano-ferric oxide powder into 100.0 g of water, stir to form a uniform suspension, and then pass in carbon dioxide to carry out the reaction at 60°C. Gas-solid reaction, until the pH value of the suspension drops to 7, stop the ventilation, filter with suction, and wash to obtain 135 g of composite nanomaterial filter cake of calcium carbonate-loaded carbon nanotubes, graphene and ferroferric oxide.

[0026] Dissolve 0.3 g of hydroxyethyl cellulose in 15 g of water to make a 2 wt% aqueous solution of hydroxyethyl cellulose.

[0027] The above hydroxyethyl cellulose aqueous solution was added to 135 g of composite material filter cake, and then 13 g of water was added to obtain a slurry with a certain viscosity, and its solid content was determined to be 60 wt %.

[0028] Apply the above slurry evenly on the copper grid, and then put it in a vacuum drying oven. The temperature condi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A method for preparing an iron-nickel battery negative electrode material, belonging to the technical field of battery negative electrode material production, performing a gas-solid reaction with a suspension obtained by mixing carbon nanotubes, graphene, nanometer iron tetroxide, calcium hydroxide and water , when the pH value of the suspension drops to 7, the filter cake is obtained by filtration, and then the filter cake is mixed with an aqueous solution of hydroxyethyl cellulose to obtain a composite nanomaterial slurry, which is coated on a copper grid and dried in vacuum and then rolled and slicing to prepare the negative plate of the iron-nickel battery. In the present invention, through the gas-solid reaction of carbon dioxide and calcium hydroxide, the submicron calcium carbonate supports graphene, carbon nanotubes, and ferric oxide nanocomposites, thereby preparing a high gram capacity, low resistance and good cycle stability. Iron-nickel battery anode material.

Description

technical field [0001] The invention belongs to the technical field of battery negative electrode material production, and in particular relates to the preparation technology of iron-nickel battery negative electrode material. Background technique [0002] The iron-nickel battery was researched and developed almost simultaneously by Edison of the United States and Junger of Sweden in 1901. It is one of many rechargeable batteries, and its development process has gone through twists and turns. At the beginning of the 20th century, it was widely used in the field of locomotive traction. But after 1960, people's interest in its research began to weaken, until after 1975, with the upsurge of electric vehicle research, it once again attracted the attention of countries all over the world. In 2012, a research report on iron-nickel batteries by scientists from Stanford University once again focused people's attention on iron-nickel batteries. It is believed that this will inevitab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/26H01M4/52H01M4/62H01M10/30B82Y30/00
CPCB82Y30/00H01M4/26H01M4/521H01M4/625H01M4/628H01M10/30H01M2004/021H01M2004/027Y02E60/10
Inventor 朱爱萍顾思凌姜云龙芮敏
Owner YANGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com