Polishing agent for new energy automobile surface and preparation method thereof

A new energy vehicle and polishing agent technology, which is applied in the direction of polishing compositions, chemical instruments and methods, etc., can solve the problems that the polishing agent is not corrosion-resistant, the protective film is easily scratched by external objects, etc., and achieves high anti-corrosion effect and good sterilization Effect, uniform brightness effect

Inactive Publication Date: 2019-03-22
合肥天沃能源科技有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the polishing agent prepared by this invention is not corrosion-resistant, and the formed protective film is easily scratched by external objects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polishing agent for new energy automobile surface and preparation method thereof
  • Polishing agent for new energy automobile surface and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A polishing agent for the surface of a new energy vehicle, comprising the following raw materials in parts by weight: 15 parts of disodium aminotriacetate, 10 parts of vegetable oil, 16 parts of hypromellose, 5 parts of organic polytricarboxylic acid, and water-soluble polyamine 8 parts, 6 parts of polymer latex, 2 parts of hydrochloric acid, 1 part of cationic surfactant, 7 parts of sodium stearate, 15 parts of hydrogen peroxide, 5 parts of preservative, 1 part of stabilizer, 6 parts of coconut oil diethanolamide , 10 parts of deionized water.

[0034]The polymer latex includes the following raw materials in parts by weight: 5 parts of epoxy resin modified acrylic emulsion, 2 parts of polyurethane modified acrylic emulsion, and 3 parts of silicone modified acrylic emulsion; The amount of resin added accounts for 10% of the mass of epoxy resin-modified acrylic, the amount of polyurethane added in polyurethane-modified acrylic emulsion accounts for 6% of the mass of poly...

Embodiment 2

[0045] A polishing agent for the surface of a new energy vehicle, comprising the following raw materials in parts by weight: 20 parts of disodium aminotriacetate, 11 parts of vegetable oil, 17 parts of hypromellose, 8 parts of organic polytricarboxylic acid, water-soluble polyamine 9 parts, 7 parts of polymer latex, 2.5 parts of hydrochloric acid, 1.5 parts of cationic surfactant, 8 parts of sodium stearate, 16 parts of hydrogen peroxide, 6 parts of preservatives, 3 parts of stabilizer, 7 parts of coconut oil diethanolamide , 15 parts of deionized water.

[0046] The polymer latex includes the following raw materials in parts by weight: 7 parts of epoxy resin modified acrylic emulsion, 3 parts of polyurethane modified acrylic emulsion, 4 parts of silicone modified acrylic emulsion; wherein, the epoxy resin modified acrylic acid The amount of resin added accounts for 11% of the mass of epoxy resin-modified acrylic, the amount of polyurethane added in polyurethane-modified acryl...

Embodiment 3

[0057] A polishing agent for the surface of a new energy vehicle, comprising the following raw materials in parts by weight: 25 parts of disodium aminotriacetate, 12 parts of vegetable oil, 18 parts of hypromellose, 11 parts of organic polytricarboxylic acid, water-soluble polyamine 10 parts, 8 parts of polymer latex, 3 parts of hydrochloric acid, 2 parts of cationic surfactant, 9 parts of sodium stearate, 17 parts of hydrogen peroxide, 7 parts of preservative, 5 parts of stabilizer, 8 parts of coconut oil diethanolamide , 20 parts of deionized water.

[0058] The polymer latex includes the following raw materials in parts by weight: 9 parts of epoxy resin modified acrylic emulsion, 4 parts of polyurethane modified acrylic emulsion, 5 parts of silicone modified acrylic emulsion; wherein, the epoxy resin modified acrylic acid The amount of resin added accounts for 12% of the mass of epoxy resin-modified acrylic, the amount of polyurethane added in polyurethane-modified acrylic ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a polishing agent for a new energy automobile surface and a preparation method thereof. The polishing agent for the new energy automobile surface is prepared from the followingraw materials in parts by weight: 15 to 35 parts of aminotriacetic acid disodium salt, 10 to 14 parts of vegetable oil, 16 to 20 parts of hydroxypropyl methylcellulose, 5 to 17 parts of organic poly-tricarboxylic acid, 8 to 12 parts of water-soluble polyamine, 6 to 10 parts of high-molecular polymer latex, 2 to 4 parts of hydrochloric acid, 1 to 3 parts of cationic surface active agent, 7 to 11 parts of sodium stearate, 15 to 19 parts of hydrogen peroxide, 5 to 9 parts of preservative, 1 to 9 parts of stabilizer, 6 to 10 parts of coconut oil diethanolamide, and 10 to 30 parts of deionized water. After the polishing agent for the new energy automobile surface prepared by the invention is used for polishing, the glossiness is high, the brightness is uniform and consistent, the polishing effect is good, an automobile is not easy to fade in color after being polished for a long time, the inoxidizability is high, and the polishing agent prepared through the invention has high temperature resistance stability and relatively good hydrophobicity, so that the occurrence of the phenomenon that acid materials in rainwater or air corrode the polishing agent so as to damage an automobile surface paint is prevented.

Description

technical field [0001] The invention relates to the technical field of car beauty, in particular to a new energy car surface polish and a preparation method thereof. Background technique [0002] The coating on the surface of the car body endows the car with a beautiful appearance and excellent protection performance, which can improve the use value of the car and prolong its service life. The surface coating of the car is affected by many factors and needs to be protected scientifically. The paint surface polishing is the most important part in the maintenance of the car coating. When removing the stubborn hard film of the car coating, the removal of the stubborn hard film can be accelerated by friction At the same time, make the paint surface smooth and clean or polish it with a polishing agent according to the damage degree of the paint surface after thorough cleaning, so that scratches, surface damage, paint surface cracks and other defects can be repaired, and the appea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09G1/18
CPCC09G1/18
Inventor 魏芳芳
Owner 合肥天沃能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com