Preparation method of layered functional material calcium sulphoaluminate

A technology of calcium sulfoaluminate and functional materials, applied in chemical instruments and methods, aluminum compounds, aluminum sulfur compounds, etc., can solve problems such as long reaction time and troublesome operation, and achieve good batch stability, convenient operation, and distribution narrow effect

Active Publication Date: 2019-03-12
JIANGSU LONGCHANG CHEM
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] After retrieval, Feng Xiuji, Liao Guanglin, etc. according to the molar ratio of CaCO 3 :Al 2 o 3 : CaSO 4 . 2H 2 O=3:3:1 mixed raw materials, kept at 1350°C for 2 hours, cooled rapidly to obtain anhydrous calcium sulfoaluminate powder crystals; then according to the mass ratio C 4 A 3 S: PbCl 2 =5:100 mixed, put into a platinum crucible and heat up to 850°C for 24 hours, then heat up to 950°C for 48 hours to prepare anhydrous calcium sulfoaluminate single crystals with a size of 50-100µm; the reaction time of this preparation method is relatively short. Long, the raw materials are fed in batches, and the operation is more troublesome

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of layered functional material calcium sulphoaluminate
  • Preparation method of layered functional material calcium sulphoaluminate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0021] The preparation method of the layered functional material calcium sulfoaluminate in this example, the fully back-mixed explosive nucleation reactor used in the preparation method includes a reaction cylinder 1, a stirrer 2 and a mixer 3; a stirrer 2 and a mixer 3 are all arranged in the reaction cylinder 1, and the stirrer 2 is driven by a stirring motor.

[0022] The reaction cylinder 1 includes an inner cylinder 11 and an outer cylinder 12; a heat exchange cavity is formed between the inner cylinder 11 and the outer cylinder 12, and an outlet of the heat exchange cavity is provided on the upper side of the outer cylinder 12 13. A heat exchange cavity inlet 14 is provided on the lower side of the outer cylinder 12; the reaction cylinder 1 is divided into an upper reaction cylinder 15 and a lower reaction cylinder 16 by a mixer 3 in the reaction cylinder 1; The reaction cylinder 1 is provided with a cylinder cover 17 and the cylinder cover 17 is provided with a first fe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of layered functional material calcium sulphoaluminate. The preparation method comprises the following steps of: (1) mixing a certain proportion of calcium sulfate, aluminum hydroxide and calcium oxide in a full backmixing explosive nucleation reactor, and adding water more than the materials to mix; and (2) synthesizing calcium sulphoaluminate gel under the conditions that the revolving speed of a rotor is 4,000-6,000 rpm, the voltage is 220-330 V and the nucleating time is 8-16 min by adopting the full backmixing explosive nucleation reactor, then enabling the calcium sulphoaluminate gel to be crystallized for 12-16 h at 90-150 DEG C, cooling to 30-50 DEG C, stirring for 12-16 h, then heating to 90-150 DEG C, and circulating 3-5 times to prepare the layered functional material calcium sulphoaluminate. The preparation method of the layered functional material calcium sulphoaluminate has the advantages that the calcium sulfate, the aluminumhydroxide and the calcium oxide can nucleate and grow in the full backmixing explosive nucleation reactor through a 'one-pot method', the preparation process of the calcium sulphoaluminate is effectively simplified, the preparation time is shortened, the reaction operation is simplified, and the production efficiency is improved.

Description

technical field [0001] The invention belongs to the technical field of layered functional inorganic materials, in particular to a method for preparing layered functional material calcium sulfoaluminate. Background technique [0002] Calcium sulfoaluminate has a layered structure, and its structural formula can be written as [Ca 2 Al(OH) 6 ](SO 4 )0 3 , which is the main component of sulphoaluminate cement, sulphoaluminate expansion agent, etc. The properties of quick hardening, dry strength and micro expansion of minerals are closely related to the crystal sister of anhydrous calcium sulfoaluminate. [0003] After retrieval, Feng Xiuji, Liao Guanglin, etc. according to the molar ratio of CaCO 3 :Al 2 o 3 : CaSO 4 . 2H 2 O=3:3:1 mixed raw materials, kept at 1350°C for 2 hours, cooled rapidly to obtain anhydrous calcium sulfoaluminate powder crystals; then according to the mass ratio C 4 A 3 S: PbCl 2 =5:100 mixed, put into a platinum crucible and heat up to 850°C...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01F7/68B01J19/18B01J19/00
CPCB01J19/0013B01J19/0066B01J19/18C01F7/68B01J2219/00094C01F7/78
Inventor 张剑宇吴春江佘卫民
Owner JIANGSU LONGCHANG CHEM
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com