Aqueous acrylic flame retardant coating, preparation method thereof and construction process

A technology of water-based acrylic and flame-retardant coatings, applied in anti-corrosion coatings, fire-resistant coatings, coatings, etc., can solve the problems of coatings that cannot be isolated from heat sources and are not heat-resistant, and achieve color retention, improved adhesion, and improved color brightness Effect

Inactive Publication Date: 2019-01-22
CHONGQING QICAIHONG CHEM
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the deficiencies of the above-mentioned prior art, the present invention provides a water-based acrylic flame-retardant coating, a preparation method and a construction process to solve the technical problems that the existing coating cannot isolate heat sources, is flammable, and is not heat-resistant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] In parts by mass, the coating includes the following components: 50 parts of water-based acrylic acid, 10 parts of ammonium polyphosphate, 20 parts of asbestos powder, 10 parts of melamine, 15 parts of coated mica powder, 8 parts of heat-resistant pigment and deionized water 40 servings. Wherein, the particle size of the coated mica powder is 2000 mesh.

Embodiment 2

[0024] In parts by mass, the coating includes the following components: 30 parts of water-based acrylic acid, 5 parts of ammonium polyphosphate, 10 parts of asbestos powder, 5 parts of melamine, 8 parts of coated mica powder, 5 parts of heat-resistant pigment and deionized water 30 servings. Wherein, the particle size of the coated mica powder is 1500 mesh.

Embodiment 3

[0026] In parts by mass, the coating includes the following components: 40 parts of water-based acrylic acid, 8 parts of ammonium polyphosphate, 15 parts of asbestos powder, 8 parts of melamine, 10 parts of coated mica powder, 6 parts of heat-resistant pigment and deionized water 35 servings. Wherein, the particle size of the coated mica powder is 3000 mesh.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses an aqueous acrylic flame retardant coating. The coating comprises the following components in parts by mass: 30-50 parts of aqueous acrylic acid, 5-10 parts of ammonium polyphosphate, 10-20 parts of asbestos powder, 5-10 parts of melamine, 8-15 parts of coated mica powder, 5 to 8 parts of temperature resistant pigment, and 30 to 40 parts of deionized water. The preparationmethod comprises the following steps: S1: weighing aqueous acrylic acid, ammonium polyphosphate, asbestos powder, melamine, coated mica powder and temperature-resistant pigment to obtain a preliminarymixture; S2: grinding the preliminary mixture, adding deionized water to mix and stir the materials, and finally filtering the material with a 200-mesh screen; and S3: packaging. The construction process comprises the following steps: A1: pretreatment of a part to-be-painted; A2: preparation of the aqueous acrylic flame retardant coating, and applying the primary coating to the part to-be-painted; and A3: performing the secondary coating, wherein a coating thickness in the primary coating and the secondary coating is 80 to 120 microns.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based acrylic flame-retardant coating, a preparation method and a construction process. Background technique [0002] Judging from the structural system and characteristics of the relatively complete ancient buildings preserved in my country, the frame structure system of the wooden frame structure is an important feature of the formation of ancient Chinese architectural structures. Its main structural features are wooden columns and beams as the main supporting components, which bear the load from the roof structure and transmit it to the columns through the beam frame, while the walls only bear their own loads, playing the role of enclosure and separation, quite Infill walls in existing frame structures. At present, the surface of ancient wooden structures in my country is mostly decorated with paint, which cannot be well protected and fireproof. Once a fire occurs, i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D5/08C09D5/18C09D5/25C09D7/61B05D7/24
CPCB05D7/24C08K2003/323C08L2201/02C08L2201/08C09D5/00C09D5/08C09D5/18C09D7/61C09D7/70C09D133/04C08K13/06C08K3/32C08K7/12C08K5/34922C08K3/34
Inventor 宋小阳
Owner CHONGQING QICAIHONG CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products