Modified asphalt with high viscosity and high elasticity

A technology of modified asphalt and high elasticity, which is applied in building components, building insulation materials, buildings, etc. It can solve the problems of reduced road durability, low structural strength, and easy cracking, so as to improve service life and high structural stability , the effect of not easy to crack

Inactive Publication Date: 2019-01-11
SHENZHEN YUETONG CONSTR ENG CO LTD
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the main feature of drainage asphalt pavement is the large void ratio (18-25%), which makes it more likely to be eroded by water, air, and sunlight. It is relatively low, so it is prone to cracking, causing the internal structure to suffer from rainwater erosion for a long time, resulting in a decrease in the durability of the road surface, so there is still room for improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified asphalt with high viscosity and high elasticity

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A modified asphalt with high viscosity and high elasticity, comprising the following components in parts by mass:

[0043] 100 parts of asphalt; 10 parts of styrene-butadiene rubber; 20 parts of volcanic fiber; 0.5 parts of crosslinking agent; 5 parts of oil.

[0044] In this embodiment, the cross-linking agent can be a common cross-linking agent in the field, specifically a peroxide cross-linking agent.

[0045] In this embodiment, the length of the volcanic fiber is cut to 5mm-10mm.

[0046] In this embodiment, the asphalt that is commonly used in the field can be used as the asphalt, specifically No. 70 base asphalt.

[0047] In this embodiment, the oil used in the art is generally used, specifically rubber oil.

[0048] In this embodiment, the styrene-butadiene rubber can be styrene-butadiene rubber commonly used in the field, specifically SBR1502.

[0049] The preparation method of modified asphalt is as follows:

[0050] (1) Put styrene-butadiene rubber into t...

Embodiment 2

[0054] The difference with embodiment 1 is:

[0055] A modified asphalt with high viscosity and high elasticity, comprising the following components in parts by mass:

[0056] 100 parts of asphalt; 12 parts of styrene-butadiene rubber; 25 parts of volcanic fiber; 0.8 parts of crosslinking agent; 7 parts of oil.

Embodiment 3

[0058] The difference with embodiment 1 is:

[0059] A modified asphalt with high viscosity and high elasticity, comprising the following components in parts by mass:

[0060] 100 parts of asphalt; 15 parts of styrene-butadiene rubber; 30 parts of volcanic fiber; 1.5 parts of crosslinking agent; 10 parts of oil.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a modified asphalt and provides the modified asphalt with high viscosity and high elasticity, in order to solve the problem of reduction of durability of pavement. According to the technical scheme, the modified asphalt with high viscosity and high elasticity contains the following components in parts by weight: 100 parts of asphalt, 10-15 parts of butadiene styrene rubber, 20-40 parts of volcano fiber, 0.5-1.5 parts of cross-linking agent and 5-10 parts of oil. 'Structural asphalt' is formed by adding the volcano fiber; the volcano fiber has excellent heat-insulatingeffect and physical properties, so that viscosity and heat insulation of the modified asphalt are promoted; the modified asphalt is reinforced, so that the asphalt layer is difficult to crack and deform and the service life of the modified asphalt is prolonged.

Description

technical field [0001] The invention relates to a modified asphalt, more specifically, it relates to a modified asphalt with high viscosity and high elasticity. Background technique [0002] Asphalt is a dark brown complex mixture composed of hydrocarbons of different molecular weights and their non-metallic derivatives. It is a kind of high-viscosity organic liquid. It is liquid with a black surface and is soluble in carbon disulfide. Asphalt is a waterproof, moisture-proof and anti-corrosion organic gelling material. Pitch can be mainly divided into three types: coal tar pitch, petroleum pitch and natural pitch. Among them, coal tar pitch is a by-product of coking. Petroleum asphalt is the residue after distillation of crude oil. Natural bitumen is stored underground, and some form ore layers or accumulate on the surface of the earth's crust. Asphalt is mainly used in coatings, plastics, rubber and other industries as well as paving roads. [0003] Orthotropic steel br...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L9/06C08L11/00C08L71/02C08K7/04C08K3/34C08K3/00
CPCC08L95/00C08L2205/03C08L2205/035C08L9/06C08K7/04C08L11/00C08K3/346C08K3/00C08L71/02
Inventor 黄智郭新星赖鸿生胡瑞祥唐晨龙
Owner SHENZHEN YUETONG CONSTR ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com