Waterproof acrylic coating for zipper and preparation method thereof

A technology of prepolymerization of acrylic acid and acrylic acid, applied in the direction of coating, etc., can solve the problems of coating stretchability, poor toughness, zipper not washable, affecting clothing texture, etc., to improve crosslinking stability, mechanical strength, etc. Improved performance and good stretchability

Active Publication Date: 2019-01-04
东莞市瑞翔新型材料科技有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing waterproof coatings have the following problems: 1. The formed coating has poor stretchability and toughness. In the process of repeated bending of the zipper tape, the coating is easy to crack, which affects the texture of the clothing; 2. Most of the existing waterproof coatings are solvent-based coatings, and there are very few water-based coatings, and generally water-based coatings do not perform well in water resistance, so the zipper will not be washable.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof acrylic coating for zipper and preparation method thereof
  • Waterproof acrylic coating for zipper and preparation method thereof
  • Waterproof acrylic coating for zipper and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A waterproof acrylic paint for slide fasteners, comprising the following raw materials in parts by weight:

[0034]

[0035] Wherein, the composite fiber is composed of nanocellulose filaments and a polyacrylamide layer covering nanocellulose filaments;

[0036] Wherein, each part by weight of the acrylic acid prepolymer emulsion is made from the following raw materials in percentage by weight:

[0037]

[0038] Wherein, the emulsifier is composed of sodium dodecylbenzenesulfonate, sodium lauryl sulfate and sorbitan oleate in a weight ratio of 2:2:1.

[0039]Wherein, the inorganic peroxide initiator is composed of ammonium persulfate and potassium persulfate in a ratio of 1:1 by weight.

[0040] Wherein, the preparation method of the acrylic acid prepolymer emulsion comprises the following steps: weighing methyl methacrylate, methacrylic acid, butyl acrylate, vinyltrimethoxysilane, emulsifier, inorganic peroxide Initiator and deionized water, add methyl methacry...

Embodiment 2

[0048] A waterproof acrylic paint for slide fasteners, comprising the following raw materials in parts by weight:

[0049]

[0050]

[0051] Wherein, the composite fiber is composed of nanocellulose filaments and a polyacrylamide layer covering nanocellulose filaments;

[0052] Wherein, each part by weight of the acrylic acid prepolymer emulsion is made from the following raw materials in percentage by weight:

[0053]

[0054] Wherein, the emulsifier is composed of sodium dodecylbenzenesulfonate, sodium lauryl sulfate and sorbitan oleate in a weight ratio of 1:1:1.

[0055] Wherein, the inorganic peroxide initiator is composed of ammonium persulfate and potassium persulfate in a ratio of 1:2 by weight.

[0056] Wherein, the preparation method of the acrylic acid prepolymer emulsion comprises the following steps: weighing methyl methacrylate, methacrylic acid, butyl acrylate, vinyltrimethoxysilane, emulsifier, inorganic peroxide Initiator and deionized water, add me...

Embodiment 3

[0064] A waterproof acrylic paint for slide fasteners, comprising the following raw materials in parts by weight:

[0065]

[0066] Wherein, the composite fiber is composed of nanocellulose filaments and a polyacrylamide layer covering nanocellulose filaments;

[0067] Wherein, each part by weight of the acrylic acid prepolymer emulsion is made from the following raw materials in percentage by weight:

[0068]

[0069]

[0070] Wherein, the emulsifier is composed of sodium dodecylbenzenesulfonate, sodium lauryl sulfate and sorbitan oleate in a weight ratio of 3:3:1.

[0071] Wherein, the inorganic peroxide initiator is composed of ammonium persulfate and potassium persulfate in a weight ratio of 2:1.

[0072] Wherein, the preparation method of the acrylic acid prepolymer emulsion comprises the following steps: weighing methyl methacrylate, methacrylic acid, butyl acrylate, vinyltrimethoxysilane, emulsifier, inorganic peroxide Initiator and deionized water, add methy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of waterproof coatings of zippers, in particular to a waterproof acrylic coating for a zipper and a preparation method thereof. The waterproof acrylic coating comprises acrylic prepolymer emulsion, complex fiber, active diluent monomer, photoinitiator, flatting agent and deionized water, wherein the complex fiber is composed of a nanocellulose filamentand a polyacrylamide layer coated with the nanocellulose filament. The waterproof acrylic coating for the zipper and the preparation method thereof have the advantages that coating modification is carried out on the nanocellulose filament through the polyacrylamide layer, so that the nanocellulose filament can have a stable suspension property in the coating, thereby being conductive to the dispersion of the nanocellulose filament in the coating, carbon-carbon double bonds of the polyacrylamide layer can also be subjected to polymerization reaction with the active diluent monomer and an acrylic prepolymer under the action of a photoinitiator, the dispersion stability of the complex fiber is further improved, and the coating can have good stretchability, tenacity and waterproofness.

Description

technical field [0001] The invention relates to the technical field of zipper waterproof paint, in particular to a waterproof acrylic paint used for zippers and a preparation method thereof. Background technique [0002] A zipper is a connecting piece that relies on continuously arranged chain elements to merge or separate items. It is now widely used in clothing, bags, tents, etc. Nowadays, there are many kinds of zippers, and some functional clothing, such as jackets, need to have a waterproof effect. In the existing zipper clothing, due to the water absorption of the fiber, water can easily penetrate from the zipper tape, thereby limiting the application of the zipper on waterproof clothing. [0003] Coating waterproof paint on the zipper tape to form a waterproof layer is one of the methods that can improve the water resistance of the zipper tape. However, the existing waterproof coatings have the following problems: 1. The formed coating has poor stretchability and to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D7/65C08F220/06C08F220/14C08F220/18C08F230/08
CPCC08F220/06C09D4/06C09D7/65C09D7/70C08F220/14C08F220/1804C08F230/08
Inventor 吴小锐
Owner 东莞市瑞翔新型材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com