Method and device for life estimation of high-temperature thick-walled pipeline

A technology for life estimation and pipelines, which is used in measuring devices, using one-time impact force to test the strength of materials, instruments, etc., can solve problems such as long time consumption, and achieve the effect of solving the problem of long time consumption and fast estimation time

Active Publication Date: 2021-02-02
国能锅炉压力容器检验有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of this, this application provides a method and device for estimating the life of high-temperature thick-walled pipelines, which are used to quickly estimate the life of high-temperature thick-walled pipelines in power stations, so as to solve the problem that traditional estimation methods take too long

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method and device for life estimation of high-temperature thick-walled pipeline
  • Method and device for life estimation of high-temperature thick-walled pipeline
  • Method and device for life estimation of high-temperature thick-walled pipeline

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] figure 1 It is a flowchart of a method for estimating the life of a high-temperature thick-walled pipeline provided in an embodiment of the present application.

[0050] Such as figure 1As shown, the life estimation method provided in this embodiment is used to estimate the remaining life of the high-temperature thick-walled pipeline in the power station, and the life estimation method specifically includes the following steps:

[0051] S1. Sampling the high-temperature thick-walled pipeline in the initial state.

[0052] The sampling of the high-temperature thick-walled pipeline can be carried out before the pipeline is put into operation, or the current state can be taken as the initial state. A small sample is obtained by sampling as a pipe sample, which is used to make the initial test piece and the failure test piece. Due to less sampling, it will not have any impact on the structure, strength and life of high-temperature thick-walled pipelines.

[0053] S2. Ma...

Embodiment 2

[0088] image 3 A block diagram of a life estimation device for a high-temperature thick-walled pipeline provided in an embodiment of the present application.

[0089] Such as image 3 As shown, the life estimating device provided in this embodiment is used to estimate the remaining life of the high-temperature thick-walled pipeline in a power station. The life estimating device specifically includes a first sampling module 10, a sample processing module 20, a sample aging module 30, The second sampling module 40 and the life calculation module 50 .

[0090] The first sampling module is used for sampling the high-temperature thick-walled pipeline in an initial state.

[0091] The sampling of the high-temperature thick-walled pipeline can be carried out before the pipeline is put into operation, or the current state can be taken as the initial state. A small sample is obtained by sampling as a pipe sample, which is used to make the initial test piece and the failure test pie...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This application provides a life estimation method and device for high-temperature thick-walled pipelines. The life estimation method and device obtain pipeline samples by sampling high-temperature thick-wall pipelines, and use the pipeline samples to make multiple initial samples and failure samples. Then conduct small punch tests on multiple initial samples and failure samples, and obtain the failure thickness through the obtained deflection-time curves, and then take samples of in-service high-temperature thick-walled pipes and conduct small punch tests to obtain the corresponding equivalent thickness , and finally calculate the remaining life of the high-temperature thick-walled pipe according to the failure thickness, the thickness to be inspected and the service time. Because the whole estimation time of this method is very fast, no enduring strength test is necessary, so the remaining life can be estimated quickly, thus solving the problem of the traditional estimation method taking too long.

Description

technical field [0001] The present application relates to the technical field of power generation, and more specifically, to a method and device for estimating the life of a high-temperature thick-walled pipeline. Background technique [0002] High-temperature thick-walled pipelines in power stations operate under high temperature and high pressure. With the prolongation of service time, the microstructure and mechanical properties of pipeline materials will change slowly. resulting in further component failure. The operating parameters of ultra (super) critical units are higher, and the parameters of power plant units are further improved. In order to ensure the safe operation of high-temperature thick-walled pipelines in power plants, it is necessary to estimate their life. [0003] The current life estimation of high-temperature thick-walled pipelines is based on the durability strength, that is, a section of the pipeline is cut off for the durability strength test, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N3/30
CPCG01N3/30G01N2203/001
Inventor 代小号郝晓军王强张广兴郑相锋王志永杨新军陶业成
Owner 国能锅炉压力容器检验有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com