A kind of preparation method of liquid band-aid
A band-aid and liquid technology, applied in medical science, bandages, etc., can solve the problem of low water vapor transmission rate, achieve the effect of promoting wound healing, good water resistance, and high water resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0038] (1) Take by weighing 10g of styrene-maleic anhydride copolymer (SMA-EF-80 of U.S. Cray Valley Company) at 20°C and disperse in 60% methylcyclohexane and 40% isopropanol by volume percentage In the mixed solvent of composition, make the polymer solution of mass percentage 8%;
[0039](2) Weigh 2g rosin resin (Shanghai Songxinlin Products Co., Ltd., X grade gum rosin) and disperse it in a mixed solvent composed of 60% methylcyclohexane and 40% isopropanol by volume percentage to make mass percentage 3% thickener solution;
[0040] (3) Add the thickener solution prepared in step (2) into the polymer solution prepared in step (1) at a volume ratio of 1:1, and then add 0.1 ppm of graphene / silver composite (Nanjing Xianfeng Nano Material Technology Co., Ltd. Co., Ltd., XF071), uniformly mixed to make a liquid band-aid, that is, the concentration of the graphene / silver compound in the liquid band-aid is 0.1mg / L.
Embodiment 2
[0042] (1) Under nitrogen protection, add 20 parts of styrene-ethylene-butadiene copolymer (Baling Petrochemical, SEBS YH-503) to 80 parts of 1,2-dichloroethane in a reaction kettle at 10°C in, stirred until dissolved, then added 1 part of chlorosulfonic acid, stirred and reacted for 18 hours, added 200 parts of ethanol for precipitation washing, and dried to obtain a copolymer composed of styrene-ethylene-butadiene and 4-vinylbenzenesulfonic acid. thing.
[0043] (2) Weigh 10 g of a copolymer composed of styrene-ethylene-butadiene and 4-vinylbenzenesulfonic acid at 20°C and disperse it in a mixture composed of 70% cyclohexane and 30% isopropanol by volume percentage In the solvent, make the polymer solution of 8% by mass percent;
[0044] (3) Weigh 2g of polyethylene glycol (Liaoning Aoke Chemical Co., Ltd., PEG600) and disperse it in a mixed solvent consisting of 70% cyclohexane and 30% isopropanol by volume percentage to make 3% by mass thickener solution;
[0045] (4) A...
Embodiment 3
[0047] (1) Under nitrogen protection, 16 parts of liquid polybutadiene (Polyvest 110 from Evonik, Germany) was added to 85 parts of 1,2-dichloroethane in a reaction kettle at 60° C., and stirred until dissolved. Then add 4 parts of fumaric acid and 0.1 part of azobisisobutyronitrile, stir and react for 24 hours, add 300 parts of ethanol for precipitation washing, and dry to obtain a block polymer composed of butadiene and fumaric acid;
[0048] (2) Take by weighing 10g of block polymers composed of butadiene and fumaric acid at 20°C and disperse them in a mixed solvent consisting of 70% n-hexane and 30% isopropanol by volume percentage to make 8% by mass % polymer solution;
[0049] (3) Weigh 2g of tributyl citrate (Shandong Kexing Chemical Co., Ltd.) and disperse it in a mixed solvent consisting of 70% by volume of n-hexane and 30% of isopropanol to make 1% by mass of thickened agent solution;
[0050] (4) Add the thickener solution prepared in step (3) into the polymer sol...
PUM
Property | Measurement | Unit |
---|---|---|
concentration | aaaaa | aaaaa |
molecular weight | aaaaa | aaaaa |
molecular weight | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com