A kind of 2007 aluminum alloy bar production process

A production process and technology of aluminum alloy, applied in the field of aluminum alloy manufacturing, can solve the problems of difficulty in online quenching of φ200-210mm aluminum alloy bars, and achieve the effect of solving difficulty in online quenching, not easy to scratch, and uniform in chemical composition

Active Publication Date: 2020-06-02
CHINA ZHONGWANG
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, in order to solve the problem of difficult online quenching of φ200-210mm aluminum alloy rods, the present invention provides a production process for 2007 aluminum alloy rods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of 2007 aluminum alloy bar production process
  • A kind of 2007 aluminum alloy bar production process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Such as figure 2 A kind of 2007 aluminum alloy bar production process shown, comprises the following steps:

[0031] A. Melting and casting: Prepare 2007 aluminum alloy raw materials according to the following weight ratio: Si: 0.50%, Mg: 0.60%, Fe: 0.80%, Cu: 4.2%, Mn: 0.45%, Cr: 0.03%, Ni: 0.02 %; Zn: 0.02%, Pb: 0.80%, single impurity ≤ 0.05%, total impurity ≤ 0.15%, the balance Al, put the prepared aluminum alloy raw materials into the smelting furnace and mix them evenly to melt into liquid aluminum alloy, and the liquid The aluminum alloy is melted and cast into an aluminum alloy ingot, and the melting temperature of the liquid aluminum alloy is 720°C;

[0032] B. Homogenization: heat the aluminum alloy ingot obtained by melting and casting to 480°C and keep it for 8 hours, then heat it to 510°C and keep it for 3 hours, and cool it to 420°C to obtain a homogeneous aluminum alloy ingot;

[0033] C. Extrusion: Send the homogenized aluminum alloy ingot into the ext...

Embodiment 2

[0040] Such as figure 2 A kind of 2007 aluminum alloy bar production process shown, comprises the following steps:

[0041] A. Melting and casting: prepare 2007 aluminum alloy raw materials according to the following weight ratio: Si: 0.60%, Mg: 0.40%, Fe: 0.60%, Cu: 4.0%, Mn: 0.55%, Cr: 0.03%, Ni: 0.02% ; Zn: 0.02%, Pb: 0.90%, single impurity ≤ 0.05%, total impurity ≤ 0.15%, the balance Al, put the prepared aluminum alloy raw materials into the smelting furnace and mix them evenly to melt into liquid aluminum alloy, and the liquid aluminum The alloy is melted and cast into an aluminum alloy ingot, and the melting temperature of the liquid aluminum alloy is 750°C;

[0042] B. Homogenization: heat the aluminum alloy ingot obtained by melting and casting to 480°C and keep it for 8 hours, then heat it to 510°C and keep it for 3 hours, and cool it to 360°C to obtain a homogeneous aluminum alloy ingot;

[0043] C. Extrusion: Send the homogenized aluminum alloy ingot into the extru...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of aluminum alloy manufacturing and relates to a 2007 aluminum alloy rod manufacturing process. The 2007 aluminum alloy rod manufacturing process comprisesthe following steps of casting, homogenizing, extruding, online quenching, stretching, sawing and framing, aging heat treatment and packaging, wherein the homogenizing process comprises the steps ofheating an aluminum alloy cast ingot obtained by casting to a temperature of 480 degrees centigrade, preserving the heat of the aluminum alloy cast ingot for 8 h, heating the aluminum alloy cast ingotto 510 degrees centigrade, preserving the heat of the aluminum alloy cast ingot for 3 h, and cooling the aluminum alloy cast ingot 360-420 degrees centigrade to obtain the homogenized aluminum alloycast ingot; and therefore, the breakthrough pressure of an extruder in the extruding process is reduced to 260 Bar, stable extrusion is made easier in the whole extruding process, a situation of pressure building of equipment is uneasy to cause, the equipment and a mold are uneasily damaged, and a problem that the online quenching of a 2007 aluminum alloy rod is difficult is solved.

Description

technical field [0001] The invention belongs to the technical field of aluminum alloy manufacturing, and relates to a production process of 2007 aluminum alloy rods. Background technique [0002] The 2007 aluminum alloy belongs to the Al-Cu-Mg series of heat-treatable and strengthened aluminum alloys. As a structural high-strength aluminum alloy, it has a wide range of applications and is important for many load-bearing structures such as aircraft fuselages, wings, connectors, and rail trains. Material. 2007 Aluminum alloys are mainly used in aviation and aerospace fields. The leading idea of ​​new aircraft design is to reduce fuel consumption, increase flight speed, and increase load capacity in order to improve tactical performance and economic benefits. Therefore, in terms of structural design, it is required to reduce the weight of the machine body as much as possible, and in terms of material selection, the material that can represent the highest specific strength of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/02C22C21/14C22C21/16C22C21/18C22F1/057
CPCC22C1/026C22C21/14C22C21/16C22C21/18C22F1/002C22F1/057
Inventor 周广宇胡忠岐陈兴伟牟彭禄王红阳
Owner CHINA ZHONGWANG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com