Metal zipper coloring agent, metal zipper and preparation method thereof

A metal zipper and coloring agent technology, applied in the field of zipper production, can solve problems such as delamination and paint falling, and achieve the effect of excellent coloring quality, not easy to fade, and excellent load resistance performance

Inactive Publication Date: 2018-12-14
ZHEJIANG WEIXING IND DEV
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the bonding force between the paint and the metal chain teeth has certain limitations. After repeated reciprocating pulls or repeated washings, delamination and paint will appear.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal zipper coloring agent, metal zipper and preparation method thereof
  • Metal zipper coloring agent, metal zipper and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0059] The present invention also provides a kind of preparation method of metal slide fastener, comprises the following steps:

[0060] A) degreasing the teeth of the metal zipper;

[0061] B) cleaning and coloring the degreased teeth to obtain colored teeth;

[0062] C) cleaning and dehydrating the colored teeth;

[0063] D) oiling the dehydrated teeth to obtain a metal zipper;

[0064] The coloring agent used in the coloring is the metal zipper coloring agent mentioned above.

[0065] In some embodiments of the present invention, the metal zipper is a brass zipper.

[0066] The present invention first degreases the teeth of the metal zipper to remove the oil stains on the teeth of the metal zipper. The degreasing agent used for the degreasing is preferably an alkaline degreasing agent. In some embodiments of the present invention, the degreaser is a commercially available alkaline degreaser HP-201A.

[0067]Before the degreasing, it is preferable to polish the teeth o...

Embodiment 1

[0093] Use a grinding machine to mechanically grind the teeth of the brass zipper;

[0094] Degreasing the zipper teeth: put in alkaline degreasing agent HP-201A to remove the oil on the zipper teeth;

[0095] Clean the zipper teeth with clean water;

[0096] Then, coloring is carried out in the coloring water, and the formula of the coloring agent is as follows:

[0097] Sodium chlorite: 80g / L;

[0098] Sodium hydroxide: 60g / L;

[0099] Sodium sulfate: 20g / L;

[0100] Water: balance.

[0101] Coloring temperature: 40°C; Coloring time: 3min;

[0102] After the coloring is completed, clean the zipper teeth with clean water;

[0103] dehydration;

[0104] The surface of the chain teeth is coated with epoxy resin paint commonly used in the zipper industry by using a box-type racking machine;

[0105] Drying; the drying temperature is 130°C; the drying time is 12 minutes.

Embodiment 2

[0108] Use a grinding machine to mechanically grind the teeth of the brass zipper;

[0109] Degreasing the zipper teeth: put in alkaline degreasing agent HP-201A to remove the oil on the zipper teeth;

[0110] Clean the zipper teeth with clean water;

[0111] Then, coloring is carried out in the coloring water, and the formula of the coloring agent is as follows:

[0112] Sodium chlorite: 50g / L;

[0113] Sodium hydroxide: 20g / L;

[0114] Sodium sulfate: 70g / L;

[0115] Water: balance.

[0116] Coloring temperature: 20°C; Coloring time: 5min;

[0117] After the coloring is completed, clean the zipper teeth with clean water;

[0118] dehydration;

[0119] The surface of the chain teeth is coated with epoxy resin paint commonly used in the zipper industry by using a box-type racking machine;

[0120] Drying; the drying temperature is 140°C; the drying time is 10min.

[0121] The color of the brass zipper observed by the naked eye is olive, such as figure 1 shown, from ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a metal zipper coloring agent. The metal zipper coloring agent comprises a material a of 20 to 100 g / L, a material b of 10 to 120 g / L, sodium sulfate solid of 0 to 100 g / L and the balance of water, wherein the material a is selected from one of sodium chlorite solid, sodium persulfate solid and potassium persulfate solid; and the material b is selected from sodium hydroxidesolid or potassium hydroxide solid. The metal zipper coloring agent is prepared from the components with specific proportion; by the metal zipper coloring agent, the metal zipper takes on olive color,the color is the color that the existing metal zipper does not take on, the coloring quality is excellent, and the color is not liable to lose; meanwhile, the durability of the zipper is excellent.

Description

technical field [0001] The invention belongs to the technical field of zipper production, and in particular relates to a metal zipper colorant, a metal zipper and a preparation method thereof. Background technique [0002] Metal zippers are one of the three major zipper product categories. Because of its high strength and strong metal texture, it has been favored by the market, and it is the main choice for jackets and luggage zippers. However, due to the limitations of the processing technology of metal zippers, the material currently used is mainly copper zippers. However, the surface coloring process of copper has many limitations due to the particularity of the zipper itself. Therefore, there are not many types of processes that can really be used for the surface coloring of metal zippers. As a result, metal zippers have been black, white, gold, and ancient for many years. Mainly silver, bronze and rose. Compared with resin and nylon zippers and metal zippers, the col...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/63
CPCC23C22/63
Inventor 马国杰
Owner ZHEJIANG WEIXING IND DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com