Fluorine-free abrasion-resistant polymer composite and preparation method thereof

A composite material and polymer technology, applied in the field of fluorine-free wear-resistant polymer composite materials and their preparation, can solve the problems of unenvironmental protection, scaling, and high specific gravity

Inactive Publication Date: 2018-12-14
安特普工程塑料(苏州)有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The main technical problem to be solved by the invention is that the wear-resistant modified polymer material contains fluorine, which is not environmentally friendly, has poor mechanical properties, fouling, and high specific gravity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fluorine-free abrasion-resistant polymer composite and preparation method thereof
  • Fluorine-free abrasion-resistant polymer composite and preparation method thereof
  • Fluorine-free abrasion-resistant polymer composite and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] figure 1 It is a flowchart of the preparation method of the fluorine-free wear-resistant polymer composite material of the present invention, as figure 1 As shown, a preparation method of a fluorine-free wear-resistant polymer composite material comprises the following steps:

[0032] Step 1, pour thermoplastic engineering plastics, wear-resistant fluorine-free graft copolymer, lubricant and stabilizer into the high-speed mixer from the feed port;

[0033] Step 2, stirring and mixing uniformly by a high-speed mixer;

[0034] Step 3: Put the mixture obtained in Step 2 into the twin-screw extruder through the main feeding port, add reinforcing fibers through the side feeding port of the twin-screw extruder, and the extruder starts to extrude after the feeding is completed Pelletizing, and then granulating through the strands through water to obtain fluorine-free wear-resistant polymer composite materials.

[0035] Further, the specific steps are:

[0036] Stir 90% by ...

Embodiment 1

[0038] Embodiment 1: polycarbonate PC: SAN grafts high molecular weight high-density polyethylene APWA=(30-95): (5-70);

Embodiment 2

[0039] Embodiment 2: polycarbonate PC: SAN grafts high molecular weight high-density polyethylene APWA: reinforcing fiber: (lubricant+stabilizer+antioxidant)=(30-88): (5-30): (5- 60): 2;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Impact strengthaaaaaaaaaa
Molecular weightaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of manufacturing of polymer materials, and discloses a fluorine-free abrasion-resistant polymer composite and a preparation method thereof. The fluorine-free abrasion-resistant polymer composite comprises the following raw materials in parts by mass: engineering thermoplastic and abrasion-resistant fluorine-free graft copolymer based on the ratio of (30-95): (5-70). The fluorine-free abrasion-resistant polymer composite further comprises reinforced fibers, wherein the ratio of engineering thermoplastic to abrasion-resistant fluorine-free graft copolymer to reinforced fibers is (30-90): (5-30): (5-60). The fluorine-free abrasion-resistant polymer composite further comprises a lubricating agent, a stabilizing agent and an antioxidant, wherein theratio of engineering thermoplastic to abrasion-resistant fluorine-free graft copolymer to reinforced fibers to (lubricating agent, stabilizing agent and antioxidant) is (30-89.9): (5-30): (5-60): (0.1-2). According to the fluorine-free abrasion-resistant polymer composite, PC, POM, PA and SAN grafted high molecular weight high density polyethylene is used as a material; polytetrafluoroethylene isnot added, so that the composite does not contain fluorine; an abrasion resisting additive is high in compatibility to substrate resin; the lubricating performance and the abrasion resistance are outstanding, the mass is light, and the appearance uniformity is improved under the same adding ratio; and moreover, the mechanical performance of the substrate resin is improved.

Description

technical field [0001] The invention relates to the technical field of polymer material manufacturing, in particular to a fluorine-free wear-resistant polymer composite material and a preparation method thereof. Background technique [0002] Among the existing wear-resistant modified polymer materials, polytetrafluoroethylene PTFE micropowder is commonly used as a wear-resistant modifier, but it will cause the material to contain fluorine, the specific gravity is high, and the mechanical properties are low. related scaling problems. In addition, on October 27, 2017, the list of carcinogens released by the International Agency for Research on Cancer of the World Health Organization was initially compiled for reference, and polytetrafluoroethylene was listed in the list of three types of carcinogens. All of these make the use of such wear-resistant modified polymer materials subject to certain restrictions. [0003] At present, more and more wear-resistant modified polymer m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L69/00C08L51/06C08L77/06C08L59/00
CPCC08L51/06C08L59/00C08L69/00C08L77/06
Inventor 贾永鹏
Owner 安特普工程塑料(苏州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com