Synthetic method of special environment-friendly zinc-based SY-310 stabilizer for PVC calendered sheet
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of SY-310 and stabilizer, which is applied in the field of stabilizer for PVC processing, can solve the problems of poor transparency, easy fogging, affecting transparency, etc., and achieve the effect of ensuring whiteness, cost reduction and good compatibility
Inactive Publication Date: 2018-11-09
杭州三叶新材料股份有限公司
View PDF7 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] The technical problem to be solved by the present invention is to provide a synthesis method of environmentally friendly zinc-based SY-310 stabilizer for PVC calendered sheets, to solve the problem of calcium-zinc stabilizers in this industry decomposing during 200-degree processing, and to solve the transparency of calcium-zinc in sheets Not good, easy to fog, and affect transparency, effectively reduce production costs and improve environmental protection indicators
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0015] The specific embodiment of the present invention is provided, and the following formula is adopted to prepare a special environment-friendly SY-310 stabilizer for PVC calendered sheet:
[0016] 1. 105kg of 3-dimethyl-6 aminouracil compound, 100kg of cyanuric acid, 160kg of heterosexual acid, 140kg of oleic acid, 60kg of benzoic acid, 80kg of lauric acid, 300kg of zinc oxide, 70kg of calcium oxide, 12kg of DBM oxide, SBM antioxidant 12kg, antioxidant 1010 10kg, solvent oil 140kg, epoxy soybean oil 80kg, linoleic acid ester antioxidant 396kg, DBM oxide 10kg, SBM oxide 10kg, catalyst 0.5kg.
[0017]The specific operation steps are as follows:
[0018] 1), in a 3 cubic stainless steel reaction kettle equipped with agitator, thermometer and heating jacket, add 1.3-dimethyl-6 aminouracil compound 105kg, cyanuric acid 100kg, heterosexual acid 160kg, oleic acid 140kg, benzoic acid 60kg, 80kg of lauric acid, 300kg of zinc oxide, 70kg of calcium oxide, 140kg of solvent oil, and ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a synthetic method of a special environment-friendly zinc-based SY-310 stabilizer for a PVC calendered sheet. The special environment-friendly zinc-based SY-310 stabilizer is prepared from the following components: 1.3-dimethyl-6amino-uracil compound, cyanuric acid, isocaprylic acid, oleic acid, benzoic acid, lauric acid, zinc oxide, calcium oxide, DBM oxide, an SBM antioxidant, an antioxidant 1010, solvent oil, epoxy soybean oil, phosphite ester antioxidants, DBM oxide, SBM oxide, and a catalyst. The synthetic method comprises the following steps: measuring all components: the 1.3-dimethyl-6amino-uracil compound, cyanuric acid, isocaprylic acid, oleic acid, benzoic acid, lauric acid, zinc oxide, calcium oxide, DBM oxide, SBM antioxidant, antioxidant 1010, solvent oil, epoxy soybean oil, phosphite ester antioxidant, DBM oxide, SBM oxide, and a catalyst, and placing the components in to an enamel reaction kettle to react. The synthetic method is excellent in stable effect, simple in processing formula and technology, bright in sheet color, capable of meeting various requirements of the national standard for the mechanical performance, and higher in environmental protection performance compared with the existing stabilizer.
Description
technical field [0001] The invention relates to a stabilizer for PVC processing, in particular to a special environment-friendly zinc-based stabilizer SY-310 stabilizer for producing PVC hard sheets by a calendering process. Background technique [0002] PVC, scientific name polyvinyl chloride, is currently the most widely used plastic in the field of plastic processing, especially in the packaging industry, it is cheap and good, and easy to shape. This industry mainly uses PVC sheets, and in the sheet industry Among them, PVC materials have low manufacturing cost, excellent mechanical properties, good processing performance, corrosion resistance, insulation and other good characteristics, so PVC sheets have been widely used in the construction and decoration industry, pharmaceutical packaging, and food packaging industries. [0003] The stability of PVC material directly affects the quality of PVC products. Therefore, during the processing and preparation of PVC sheets, it ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.