Processing technology of fibrilia for seedling base cloth

A processing technology, hemp fiber technology, applied in the field of hemp fiber processing technology, can solve the problems of uneven distribution of fiber thickness, poor degumming effect of hemp fiber, poor mechanical properties, etc., to achieve uniform distribution of fiber pores, satisfactory mechanical properties, reduce The effect of intensity

Inactive Publication Date: 2018-11-06
JIANGXI JINGZHU IND
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the above-mentioned problems in the prior art, the present invention provides a processing technology of hemp fiber for seedling raising base cloth, so as to overcome the disadvantages of poor degumming effect of hemp fiber, uneven distribution of fiber thickness and poor mechanical properties in the prior art.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The present embodiment provides a kind of processing technology of hemp fiber for seedling raising base cloth, and its technical process is as follows:

[0025] (1) Mechanical pretreatment: The raw hemp is repeatedly rolled 120 times by rollers to obtain rough hemp, and then washed with water to initially remove part of the hemicellulose and lignin attached to the fiber surface;

[0026] (2) Pre-soaking treatment: Soak the hemp obtained in step (1) in a peracetic acid pre-soaking treatment solution, wherein the concentration of peracetic acid is 4%, the temperature is 65° C., the pH value is 6, and the time is 65 minutes; Washing with water again after completing the presoaking process to obtain hemp fibers;

[0027] (3) Scouring: the hemp fiber obtained in step (2) is further scoured, and after scouring, first use 80°C hot water to rinse, and then use 20°C cold water to wash; wherein, the bath ratio of scouring is 1: 9. The scouring temperature is 60°C, the scouring t...

Embodiment 2

[0033] The present embodiment provides a kind of processing technology of hemp fiber for seedling raising base cloth, and its technical process is as follows:

[0034] (1) Mechanical pretreatment: The raw hemp is repeatedly rolled by rollers for 150 times to obtain rough hemp, and then washed with water to initially remove part of the hemicellulose and lignin attached to the fiber surface;

[0035] (2) Pre-soaking treatment: soak the hemp obtained in step (1) in a peracetic acid pre-soaking treatment solution, wherein the concentration of peracetic acid is 4%, the temperature is 70° C., the pH value is 7, and the time is 80 minutes; Washing with water again after completing the presoaking process to obtain hemp fibers;

[0036] (3) Scouring: the hemp fiber obtained in step (2) is further scoured, and after scouring, first use 90°C hot water to rinse, and then use 30°C cold water to wash; wherein, the bath ratio of scouring is 1: 12. The scouring temperature is 70°C, the scour...

Embodiment 3

[0043] The present embodiment provides a kind of processing technology of hemp fiber for seedling raising base cloth, and its technical process is as follows:

[0044] (1) Mechanical pretreatment: the raw hemp is repeatedly rolled by rollers for 180 times to obtain rough hemp, and then washed with water to initially remove part of the hemicellulose and lignin attached to the fiber surface;

[0045] (2) Pre-soaking treatment: soak the hemp obtained in step (1) in a peracetic acid pre-soaking treatment solution, wherein the concentration of peracetic acid is 5%, the temperature is 75° C., the pH value is 8, and the time is 90 minutes; Washing with water again after completing the presoaking process to obtain hemp fiber;

[0046] (3) Scouring: the hemp fiber obtained in step (2) is further scoured, and after scouring, first use 80-100°C hot water to wash, and then use 35°C cold water to wash; wherein, the bath ratio of scouring is 1:14, the scouring temperature is 80°C, the scou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
elongationaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a processing technology of fibrilia for seedling base cloth, andthe processing technology flow is as follows: after mechanically and repeatedly rolling of the raw hemp, the fine fibrilia is obtained by facilitating pre-soaking, boiling, softening, dewatering and drying and mechanical post-treatment. The processing method realizes good degumming effect by using three flow steps of mechanical pretreatment, pre-leaching and boiling off, in particular to the degumming treatment of the fibrilia by using an acid-base coordination compound enzyme, the residual gum rate is low,the process flow is simple, and the fine fibers are favorably obtained. By using the softening and mechanical post-processing, the fine fibrilia is further obtained through slow carding, the strengthof the fibrilia is reduced, and the fiber is uniformly distributed, so that the prepared seedling base cloth has stable quality, and the mechanical property can well meet the requirement of seedlingraising and seedling cultivation.

Description

technical field [0001] The invention relates to a processing technology of hemp fiber, in particular to a processing technology of hemp fiber for seedling raising base cloth. Background technique [0002] Hemp fiber is a fiber obtained from various hemp plants, including the bast fiber of the cortex of annual or perennial herbaceous dicotyledonous plants and the leaf fiber of monocotyledonous plants. Because of its high strength, high rigidity, and good functions of moisture absorption, moisture dissipation and ventilation, it is widely used in various textiles, daily necessities and agricultural production. In particular, with the continuous development of agricultural production and the improvement of the quality of agricultural products, the technical requirements for hemp fibers used in agricultural production such as seedling raising, lawn sowing modeling, and agricultural product coverage are getting higher and higher. [0003] The main component of hemp fiber is cell...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01B1/22D01C1/02D01G15/00
CPCD01B1/22D01C1/02D01G15/00
Inventor 徐丽
Owner JIANGXI JINGZHU IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products