Preparation method of modified polysaccharide hydrogel and prepared modified polysaccharide hydrogel

A hydrogel and modification technology, applied in the field of hydrogel preparation, can solve the problems of harsh synthesis conditions and poor biocompatibility, and achieve the effects of simple reaction conditions, high equilibrium water content and improved biocompatibility

Active Publication Date: 2021-02-09
济南蓝锐新材料科技有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the shortcomings of many synthetic materials in the prior art, such as poor biocompatibility and harsh synthesis conditions, the present invention provides a method for preparing a modified polysaccharide hydrogel and the prepared modified polysaccharide hydrogel. The prepared hydrogel The glue has good biocompatibility, anti-protein adsorption performance, self-healing performance and high equilibrium moisture content, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of modified polysaccharide hydrogel and prepared modified polysaccharide hydrogel
  • Preparation method of modified polysaccharide hydrogel and prepared modified polysaccharide hydrogel
  • Preparation method of modified polysaccharide hydrogel and prepared modified polysaccharide hydrogel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The invention provides a kind of preparation method of modified polysaccharide hydrogel, comprising the following steps:

[0038] (1) Preparation of double bond modified polysaccharide:

[0039] Mix 0.5g of hyaluronic acid and water evenly in proportion to a concentration of 3wt%, under magnetic stirring, add 100μL of triethylamine, 0.47g of tetrabutylammonium bromide, 3.2mL of glycidyl methacrylate, and react for 24 hours , followed by dialysis in 0.1M sodium chloride and deionized water for 12 hours, and lyophilized to obtain double bond modified hyaluronic acid (HAGMA);

[0040] (2) Preparation of zwitterionic thiol polymer (CB-SH):

[0041] Dissolve 0.5 g of carboxybetaine methyl methacrylate (CBMA) and 40 mg of N,N'-bis(acryloyl) cystamine (BAC) in a mixed solvent of 4 ml of water and ethanol, then add 16 mg of ammonium persulfate, 20 μL N,N,N',N'-tetramethylethylenediamine, reacted for 24h, dialyzed the reaction product in deionized water for three days to remov...

Embodiment 2

[0047] The invention provides a kind of preparation method of modified polysaccharide hydrogel, comprising the following steps:

[0048] (1) The preparation of the double bond modified polysaccharide is the same as in Example 1 step (1);

[0049] (2) The preparation of the zwitterionic mercapto polymer (CB-SH) is the same as in Example 1 step (2);

[0050] (3) Preparation of "click" chemical hydrogel:

[0051] Dissolve 50mg HAGMA in 1ml PBS (PH=7.2) buffer solution, stir well, and set aside; Dissolve 0.1g CB-SH in 1ml PBS (PH=7.2) buffer solution, stir well, set aside; Take a certain amount of two kinds of Mix the mother liquor evenly according to the ratio of double bond-mercapto group of 2:1, put it in a constant temperature water bath at 37°C, and gel can be formed spontaneously within 1 hour.

Embodiment 3

[0053] The invention provides a kind of preparation method of modified polysaccharide hydrogel, comprising the following steps:

[0054] (1) The preparation of the double bond modified polysaccharide is the same as in Example 1 step (1);

[0055] (2) The preparation of the zwitterionic mercapto polymer (CB-SH) is the same as in Example 1 step (2);

[0056] (3) Preparation of "click" chemical hydrogel:

[0057] Dissolve 50mg HAGMA in 1ml PBS (PH=7.2) buffer solution, stir well, and set aside; Dissolve 0.1g CB-SH in 1ml PBS (PH=7.2) buffer solution, stir well, set aside. Take a certain amount of two kinds of mother liquors, mix them evenly according to the ratio of double bond-mercapto group of 1:2, put them in a constant temperature water bath at 37°C, and gel can be formed spontaneously within 1 hour.

[0058] In order to further illustrate the performance of the hydrogel prepared by the present invention, due to limited space, only Example 1 is used as an example to constru...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a modified polysaccharide hydrogel and the prepared modified polysaccharide hydrogel, belonging to the technical field of gel preparation. The preparation method of the above-mentioned modified polysaccharide hydrogel comprises the following steps: (1) preparation of double bond modified polysaccharide; (2) preparation of zwitterionic thiol polymer (CB-SH); (3) "click" chemical hydrogel preparation. The hydrogel of the present invention can be formed under physiological conditions, and the reaction conditions are simple and mild; the hyaluronic acid and the zwitterionic polymer work together to improve the biocompatibility of the material, so that the hydrogel material has a higher equilibrium content water, has anti-protein properties and self-healing properties, etc.

Description

technical field [0001] The invention relates to the technical field of hydrogel preparation, in particular to a preparation method of a modified polysaccharide hydrogel and the prepared modified polysaccharide hydrogel. Background technique [0002] Hydrogel is a three-dimensional cross-linked polymer network, which is soft in nature, absorbs a large amount of water and is insoluble in water while maintaining its integrity. Due to their excellent swelling-deswelling properties and stimuli-response behavior, hydrogels have been widely used in soft contact lenses, chemical sensors, drug-controlled release materials, tissue engineering, wound dressings, and diagnostic technologies. [0003] All water-soluble or hydrophilic polymers can form hydrogels through certain chemical cross-linking or physical cross-linking. These polymers can be divided into two categories according to their sources: natural and synthetic. Natural hydrophilic polymers include polysaccharides (starch, c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08J3/075C08B37/08C08F220/36C08F222/38C08L5/08C08L33/14
CPCC08B37/0072C08F220/36C08J3/075C08J2305/08C08J2433/14C08F220/365C08F222/385
Inventor 张亚彬刘淑艳张书香宗传永张炉青马佳晨翟丛丛曹影
Owner 济南蓝锐新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap