A kind of preparation method and product thereof of water-based polyurethane textile finishing agent doped in situ with nano-silver

A water-based polyurethane and textile finishing technology, applied in textiles and papermaking, fiber treatment, abrasion-resistant fibers, etc., can solve the problems of poor film formation, poor hydrophilicity of chitosan, hard hand feeling, etc., and improve the antibacterial effect. Effect

Active Publication Date: 2021-03-23
河北多维康助剂有限公司 +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, chitosan has poor hydrophilicity, poor film-forming properties, and hard hand feeling, so it is not suitable for multifunctional finishing of textile products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method and product thereof of water-based polyurethane textile finishing agent doped in situ with nano-silver
  • A kind of preparation method and product thereof of water-based polyurethane textile finishing agent doped in situ with nano-silver

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] Embodiment 1 The preparation method of the water-based polyurethane textile finishing agent doped in situ with nano-silver of the present invention

[0055] The concrete steps of this preparation method:

[0056] (1) The step of polyurethane dispersion preparation, this step reacts polyester diol, polyether diol and diisocyanate, nonionic chain extender, cationic chain extender, quaternizing agent, stannous octoate, and then Glycol is dispersion medium, makes polyurethane dispersion liquid; Specifically:

[0057] (1.1) drop into polyester diol, the polyether diol of total amount 70%, the nonionic chain extender of total amount 60% in reactor;

[0058] (1.2) Heat up to 75°C, add diisocyanate and react under stirring for 30min;

[0059] (1.3) Add stannous octoate, heat up to 85-90°C and react for 120min under stirring;

[0060] (1.4) Cool down to 45°C, add the cationic chain extender dropwise evenly within 15 minutes, control the temperature at 50-55°C after the droppi...

Embodiment 2

[0070] Embodiment 2 The preparation method of the water-based polyurethane textile finishing agent doped with nano-silver in situ of the present invention

[0071] The concrete steps of this preparation method:

[0072] (1) The step of polyurethane dispersion preparation, this step reacts polyester diol, polyether diol and diisocyanate, nonionic chain extender, cationic chain extender, quaternizing agent, stannous octoate, and then Glycol is dispersion medium, makes polyurethane dispersion liquid; Specifically:

[0073] (1.1) drop into polyester diol, the polyether diol of total amount 75%, the nonionic chain extender of total amount 60% in reactor;

[0074] (1.2) Heat up to 70°C, add diisocyanate and react for 40min under stirring;

[0075] (1.3) Add stannous octoate, heat up to 80-85°C and react for 100min under stirring;

[0076] (1.4) Cool down to 45°C, add cationic chain extender evenly dropwise within 10 minutes, control the temperature at 55±5°C and react under stirr...

Embodiment 3

[0086] Embodiment 3 The preparation method of the water-based polyurethane textile finishing agent doped in situ with nano-silver of the present invention

[0087] The concrete steps of this preparation method:

[0088] (1) The step of polyurethane dispersion preparation, this step reacts polyester diol, polyether diol and diisocyanate, nonionic chain extender, cationic chain extender, quaternizing agent, stannous octoate, and then Glycol is dispersion medium, makes polyurethane dispersion liquid; Specifically:

[0089](1.1) drop into polyester diol, the polyether diol of total amount 65%, the nonionic chain extender of total amount 50% in reactor;

[0090] (1.2) Heat up to 70°C, add diisocyanate and react for 40min under stirring;

[0091] (1.3) Add stannous octoate, heat up to 80-85°C and react for 150min under stirring;

[0092] (1.4) Cool down to 50°C, add cationic chain extender evenly dropwise within 15 minutes, control the temperature at 55±5°C after dropping, and re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
antibacterial rateaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a nano-silver in situ doped waterborne polyurethane textile finishing agent and a product thereof. The preparation method comprises the following steps: preparing raw materials: a polymeric monomer, silver nitrate and ethylene glycol, wherein the polymeric monomer is prepared from diisocyanate, polyester glycol, polyether diol, a non-ionic chain extender, a cationic chain extender and a quaternization reagent; preparing polyurethane dispersion; performing nano-silver in situ doping and compounding; obtaining the nano-silver in situ doped waterborne polyurethane textile finishing agent. The finishing agent selects quaternization cationic hydrophilic polyurethane as a dispersion medium of nano-silver and is used for textile products such as synthetic fibers, recycled fibers, protein fibers and cellulose fibers; the finishing agent has the advantages of having a certain anti-pilling function on needle textiles while endowing the textile with hydrophilic, anti-static and antibacterial effects; a product is safe and environmentally friendly and is convenient to use.

Description

technical field [0001] The present invention relates to the hydrophilic, antibacterial and antistatic finishing of various synthetic fibers, regenerated fibers, protein fibers, cellulose fibers and other textile products, in particular to a preparation method of a water-based polyurethane textile finishing agent doped with nano-silver in situ and its products. Background technique [0002] As an antibacterial agent, nano silver will not produce drug resistance, and the antibacterial effect is stable. The study found that the antibacterial and bactericidal properties of nano-silver are not only related to its own physical and chemical properties, but also affected by its dispersion medium. At present, the liquid-phase chemical reduction method is the most widely used nano-silver preparation method, which generally requires the dispersion of polyethylene glycol or polyvinylpyrrolidone to prevent the agglomeration of nano-silver particles. Specifically, ethylene glycol, hydra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D06M11/83D06M15/564D06M15/568D06M15/572C08G18/66C08G18/48C08G18/42C08G18/32C08G18/83
CPCC08G18/4018C08G18/4238C08G18/425C08G18/4833C08G18/6622C08G18/83D06M11/83D06M15/564D06M15/568D06M15/572D06M16/00D06M2200/35
Inventor 权衡殷映婷孔祥锋倪丽杰毕曙光李时伟孙庆诚
Owner 河北多维康助剂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap