Alloy cast iron cutting fluid and preparation method thereof

A technology of alloy cast iron and cutting fluid, which is applied in the field of alloy cast iron cutting fluid and its preparation, can solve the problems of abnormal use, easy precipitation and deterioration of emulsion, etc., and achieve the effect of not easy precipitation and deterioration, and good chemical stability

Inactive Publication Date: 2018-09-04
蒋超
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When used for fine boring (reaming) machining of cylinder liner inner holes or other alloy cast iron cutting, the traditional cutting fluid cannot be used normally in high-hard water after being diluted with water. In addition, the traditional cutting fluid emulsion is easy to precipitate and deteriorate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Example 1, the alloy cast iron cutting fluid of the present invention is composed of the following raw materials by mass: sodium petroleum sulfonate 5, glycerol 7, triethanolamine oleate soap 4, nonylphenol polyoxyethylene ether 4, and kerosene 80.

Embodiment 2

[0015] Example 2, the alloy cast iron cutting fluid of the present invention is composed of the following raw materials in parts by mass: petroleum sodium sulfonate 10, glycerol 8, oleic acid triethanolamine soap 5, nonylphenol polyoxyethylene ether 5, kerosene and diesel 70.

[0016] Kerosene is kerosene for lamps, and the model of diesel is 10# diesel.

[0017] The present invention also provides a production process of alloy cast iron cutting fluid, which includes the following steps:

[0018] First, add petroleum sodium sulfonate into the reactor, heat to 40-60℃, add glycerin, oleic acid triethanolamine soap, nonylphenol polyoxyethylene ether after 10-15min, stir for 10-15min, and finally add kerosene Or diesel oil or its mixture, stir for 20-25min to get the desired product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of metal cutting machining. The technical scheme of the invention is as follows: alloy cast iron cutting fluid is prepared from the following raw materialsin parts by mass: 5 to 12 parts of sodium alkane sulfoate, 5 to 10 parts of glycerol, 3 to 5 parts of triethanolamine oleate soap, 3 to 5 parts of nonylphenol polyoxyethylene ether and 70 to 80 partsof kerosene, diesel oil or a mixture thereof. The alloy cast iron cutting fluid has the beneficial effects that the alloy cast iron cutting fluid is an environment-friendly product, does not containtoxic components and is high in chemical stability, and emulsion of the alloy cast iron cutting fluid is difficult to settle and spoil.

Description

Technical field [0001] The invention belongs to the technical field of metal cutting processing, and particularly relates to an alloy cast iron cutting fluid and a preparation method thereof. Background technique [0002] When metal cutting, cutting fluid is usually used to cool and lubricate the tool. When used for fine boring (reaming) machining of cylinder liner inner holes or cutting of other alloy cast irons, traditional cutting fluids can not be used normally in high-hard water after being diluted by water. In addition, traditional cutting fluid emulsions are easy to precipitate and deteriorate. Summary of the invention [0003] The object of the present invention is to provide an alloy cast iron cutting fluid, which has the advantages of not being easy to precipitate and deteriorate. [0004] In order to achieve the above objectives, the present invention adopts the following technical solutions: [0005] The alloy cast iron cutting fluid of the present invention is composed ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/04C10N40/22
CPCC10M169/04C10M2203/10C10M2207/022C10M2209/104C10M2209/108C10M2215/04C10M2219/044C10N2010/02C10N2040/22C10N2040/244
Inventor 蒋超
Owner 蒋超
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com