Manufacturing method of high-efficiency inorganic membrane filtering plate for water treatment

A manufacturing method and technology of filter plates, which are used in osmotic/dialysis water/sewage treatment, chemical instruments and methods, membrane technology, etc., can solve the problem of low strength of ceramic membrane plates, uneven dispersion of membrane pores, and membrane peeling off. and other problems, to achieve the effects of excellent thermal cycle resistance and impact resistance, not easy to fall off and separate, and strong pollution interception ability.

Active Publication Date: 2018-09-04
萍乡市三盈科技有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to market research, the current inorganic ceramic membranes, especially inorganic ceramic membrane plates, have the following problems in the use of real hospitals: First, because the thickness of ceramic membrane plates is generally 8-15 mm and the area is 1-3 square meters, the The strength is not high and the brittleness is high. After working under harsh conditions for a period of time, the ceramic membrane plate is prone to cracking, which reduces the filtration efficiency. Affect the filtration effect; the third is that the membrane flux of the membrane layer is not high enough, and the size of the membrane pores is not very uniformly dispersed, which is easy to cause blockage of the membrane pores, increases the difficulty of backwashing, and increases the filtration cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1, the manufacture method step of the high-efficiency inorganic membrane filter plate of water treatment of the present invention is:

[0022] a. 60-80 mesh, 55wt% corundum sand, 21.5wt% Suzhou soil, 8wt% α-Al 2 o 3 , 4 wt% titanium aluminum carbide, 1 wt% feldspar, 7.5 wt% methylcellulose, 0.5 wt% dextrin, 0.5 wt% lepidolite, 0.5 wt% bentonite, 0.5 wt% talc and 1wt% oleic acid, first mix corundum sand, titanium aluminum carbide, α-Al 2 o 3 , Suzhou soil, feldspar, dextrin, lepidolite, bentonite, talc powder and oleic acid are put into the mixer and stirred for 15 minutes, then put into the prepared methyl cellulose and stirred to make a mixture;

[0023] b. Put the mixed material in a closed space to stale for 20 hours, put the aged mixed material into a hydraulic press to press into a plate-shaped green body, and then dry the plate-shaped green body naturally for 1 day;

[0024] c. Put the naturally dried plate-shaped body into a dryer to dry and shape ...

Embodiment 2

[0031] Embodiment 2, the manufacture method step of the water treatment high-efficiency inorganic membrane filter plate of the present invention is:

[0032] a. 60-80 mesh, 52wt% corundum sand, 26wt% Suzhou soil, 6wt% α-Al 2 o 3 , 3.5wt% titanium aluminum carbide, 0.8wt% feldspar, 8.4wt% methylcellulose, 1wt% dextrin, 0.7wt% lepidolite, 0.8wt% bentonite, 0.3wt% talc , 0.5wt% oleic acid raw material, corundum sand, titanium aluminum carbide, α-Al 2 o 3 , Suzhou soil, feldspar, dextrin, lepidolite, bentonite, talc powder and oleic acid are put into the mixer and stirred for 15 minutes, then put into the prepared methyl cellulose and stirred to make a mixture;

[0033] b. Put the mixed material in a closed space to stale for 20 hours, put the aged mixed material into a hydraulic press to press into a plate-shaped green body, and then dry the plate-shaped green body naturally for 1 day;

[0034] c. Put the naturally dried plate-shaped body into a dryer to dry and shape it. The...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
areaaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing method of a high-efficiency inorganic film filtering plate for water treatment. The manufacturing method comprises the following steps: firstly stirring emery,Suzhou soil, alpha-Al2O3, titanium aluminum carbide, feldspar, methyl cellulose, dextrin, lepidolite, bentonite, talcum powder and oleic acid according to the matching ratio, carrying out decaying andmechanical pressing for molding, drying and sizing, spraying a layer of zeolite slurry film on the platy surface, primarily sintering, coating film slurry consisting of the emery, the Suzhou soil, the feldspar, titanium oxide sol, fiber, the talcum powder, the bentonite, the dextrin, the lepidolite and sodium humate, secondarily sintering after natural drying, cooling, discharging from a furnace,assembling, inspecting, packaging and warehousing. The high-efficiency inorganic film filtering plate is widely used for treatment of industrial waste water in chemistry, foods, medicines, chemical fertilizer, metallurgy, paper making and printing and dyeing and the like, and has the advantages of high filtering efficiency, strong pollutant intercepting capability, good effluent quality, long service life and low operation cost.

Description

technical field [0001] The invention relates to solid-liquid separation of wastewater in the field of environmental protection, and aims to provide a high-efficiency, wide-adaptability, and low-cost manufacturing method of a high-efficiency inorganic membrane filter plate. Background technique [0002] In the process of removing SS and oil in wastewater, activated carbon adsorption, modified bentonite adsorption, and macroporous resin adsorption are the most representative traditional technologies. The principle is to use solid adsorbents with large specific surface area, high porosity, and polarity Strong, particles with charged polarity have good physical adsorption and surface chemical activity, have good adsorption capacity for various pollutants in wastewater, and achieve the purpose of purifying water. However, the traditional filtration technology has disadvantages such as high price, single function, high investment cost, and poor backwashing effect. [0003] Inorga...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01D71/02B01D69/10B01D67/00C02F1/44
CPCB01D67/0039B01D69/10B01D71/02C02F1/44
Inventor 邓建波
Owner 萍乡市三盈科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com