Foam ceramic high-temperature release agent and its application method

A technology of foamed ceramics and mold release agent, which is applied in the direction of lubricating composition and petroleum industry, etc. It can solve the problems of insufficient paper area and length, irregular corners of products, difficulty in sticking and fixing, etc., so as to improve the neatness of products , labor saving, and stable performance

Active Publication Date: 2021-04-20
中科国发(广州)智能环保科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The first is that a lot of manual pasting is required, because the area and length of the paper are not large enough, and splicing and pasting are required;
[0005] The second is that there are corners and corners in the mold, and these corners or four corners are difficult to lay flat release paper, and it is also difficult to paste and fix, so it still takes a lot of labor, and the products prepared by this method There are also cases where the corners are not neat

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Foam ceramic high-temperature release agent and its application method
  • Foam ceramic high-temperature release agent and its application method
  • Foam ceramic high-temperature release agent and its application method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A high-temperature release agent for foamed ceramics, consisting of the following raw materials in mass fraction:

[0028]

[0029] The dispersant is a silane dispersant.

[0030] The particle size of each material is greater than 325 mesh.

[0031] Said materials are mixed evenly and then mixed with water, the mass ratio of mixing is material:water=3:7.

[0032] The foam ceramic high-temperature release agent is mixed with water, and after mixing, the mold is sprayed by spraying equipment, and the spraying thickness is 0.7mm.

[0033] The high-temperature release agent for foamed ceramics is mixed with water, and the mold is sprayed by spraying equipment after mixing. The sintering temperature of the sprayed coating is 910 degrees, while that of the foamed ceramics is 1100 degrees. The sprayed coating is sintered earlier than the foamed ceramics.

Embodiment 2

[0035] A high-temperature release agent for foamed ceramics, consisting of the following raw materials in mass fraction:

[0036]

[0037] The dispersant is a silane dispersant.

[0038] The particle size of each material is greater than 325 mesh.

[0039] Said materials are mixed evenly and then mixed with water, the mass ratio of mixing is material:water=3:5.

[0040] The foam ceramic high-temperature release agent is mixed with water, and after mixing, the mold is sprayed by spraying equipment, and the spraying thickness is 1mm.

[0041] The high-temperature release agent for foamed ceramics is mixed with water, and the mold is sprayed by spraying equipment after mixing. The sintering temperature of the sprayed coating is 930 degrees, while that of the foamed ceramics is 1150 degrees. The sprayed coating is sintered earlier than the foamed ceramics.

Embodiment 3

[0043] A high-temperature release agent for foamed ceramics, consisting of the following raw materials in mass fraction:

[0044]

[0045] The dispersant is a silane dispersant.

[0046] The particle size of each material is greater than 325 mesh.

[0047] Said materials are mixed evenly and then mixed with water, the mixing mass ratio is material:water=4:6.

[0048] The foam ceramic high-temperature release agent is mixed with water, and after mixing, the mold is sprayed by spraying equipment, and the spraying thickness is 0.9mm.

[0049] The high-temperature release agent for foamed ceramics is mixed with water, and the mold is sprayed by spraying equipment after mixing. The sintering temperature of the sprayed coating is 890 degrees, while that of the foamed ceramics is 1090 degrees. The sprayed coating is sintered earlier than the foamed ceramics.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-temperature release agent for foamed ceramics and a use method thereof, belonging to the field of preparation of foamed ceramics; it consists of the following raw materials in mass fractions: 5-15% of montmorillonite; 3-10% of dolomite; 3-3% of talc powder ‑10%; alumina powder 65‑70%; dispersant 0.1‑0.5%; calcite 1‑3%; magnesia clay 5‑10%; lithium china stone 1‑3%. Use foam ceramic high-temperature release agent and water to mix and then spray. This technology can reduce a lot of manual labor. Normal spraying equipment can be used for spraying, which can greatly improve work efficiency. At the same time, the spraying is even and there is no cutting seam. All corners of the mold can also be sprayed evenly, which is not possible with pasting.

Description

technical field [0001] The invention relates to a high-temperature release agent for foamed ceramics and a use method thereof, belonging to the field of preparation of foamed ceramics. Background technique [0002] With the development of science and technology, the application rate of foamed ceramics is getting higher and higher, and foamed ceramics are also more and more accepted by people. Zhou Suozhou and the current foamed ceramics are all foamed by molds. It is a well-known problem that the mold and the foamed sheet stick together during the foaming process. If no measures are taken, the mold and the foamed sheet will easily stick together during the sintering process, and it will be difficult to separate the mold and the sheet. If Forcible separation can easily damage the mold and the plate, or the mold cannot be used, or the plate is defective and becomes a defective product; [0003] At present, the effective means in this field is to use release paper to separate ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C10M169/00C10M173/02C10N40/36
CPCC10M169/00C10M173/02C10M2201/062C10M2201/102C10M2201/103C10M2227/00C10M2229/02C10N2040/36
Inventor 王民董景宏孙亚欣
Owner 中科国发(广州)智能环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap