Preparation method of electrode supporting zeolite imidazole diaphragm of lithium ion battery

A technology for lithium-ion batteries and diaphragms, applied in secondary batteries, battery pack components, circuits, etc., can solve problems such as complex production methods, and achieve the effects of simple and easy-to-operate manufacturing processes, high porosity, and high chemical stability

Inactive Publication Date: 2018-08-28
QILU UNIV OF TECH
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, Ji-AeChoi et al. (Enhancement of thermal stability and cycling performance in lithium-ion cells through the use of ceramic-coated separators) in this article use ceramics to coat organic separators, the liquid absorption of inorganic particles and the polymer separators The combination of flexibility allows composite membranes to exhibit superior properties, but this method of production is complex

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of electrode supporting zeolite imidazole diaphragm of lithium ion battery
  • Preparation method of electrode supporting zeolite imidazole diaphragm of lithium ion battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] (1) ZIF-67 is a porous structure assembled by metal cobalt and organic ligands. Its typical synthesis method is to dissolve 1.455g cobalt nitrate hexahydrate and 1.642g 2-methylimidazole in methanol solution respectively. The 2-methylimidazole solution was then added to the cobalt nitrate hexahydrate solution under vigorous stirring and stirred for 1 min, and aged at room temperature for 10 h. The resulting purple precipitate was collected by centrifugation, washed three times with ethanol, and dried under vacuum at 80°C for 24h.

[0014] (2) LiNi 0.5 co 0.2 mn 0.3 o 2 (NCM) electrode material, acetylene black and polyvinylidene fluoride (PVDF) were dispersed in N-methyl-2-pyrrolidone (NMP) at a mass ratio of 8:1:1, and a uniform slurry was formed after vigorous stirring, and then The slurry was uniformly coated on an aluminum foil, and dried under vacuum at 120°C for 12 h.

[0015] (3) The prepared ZIF-67 was ground into powder, and then added to the mixed solut...

Embodiment 2

[0018] (1) ZIF-67 is a porous structure assembled by metal cobalt and organic ligands. Its typical synthesis method is to dissolve 1.455g cobalt nitrate hexahydrate and 1.642g 2-methylimidazole in methanol solution respectively. Then the 2-methylimidazole solution was added to the cobalt nitrate hexahydrate solution under vigorous stirring and stirred for 1 min, and aged at room temperature for 20 h. The resulting purple precipitate was collected by centrifugation, washed three times with ethanol, and dried under vacuum at 80°C for 24h.

[0019] (2) LiNi 0.5 co 0.2 mn 0.3 o 2 (NCM) electrode material, acetylene black and polyvinylidene fluoride (PVDF) were dispersed in N-methyl-2-pyrrolidone (NMP) at a mass ratio of 8:1:1, and a uniform slurry was formed after vigorous stirring, and then The slurry was uniformly coated on an aluminum foil, and dried under vacuum at 120°C for 12 h.

[0020] (3) The prepared ZIF-67 was ground into powder, and then added to the mixed solut...

Embodiment 3

[0023] (1) ZIF-67 is a porous structure assembled by metal cobalt and organic ligands. Its typical synthesis method is to dissolve 1.455g cobalt nitrate hexahydrate and 1.642g 2-methylimidazole in methanol solution respectively. The 2-methylimidazole solution was then added to the cobalt nitrate hexahydrate solution under vigorous stirring and stirring was continued for 5 h. The resulting purple precipitate was collected by centrifugation, washed three times with ethanol, and dried under vacuum at 80°C for 24h.

[0024] (2) LiNi 0.5 co 0.2 mn 0.3 o 2 (NCM) electrode material, acetylene black and polyvinylidene fluoride (PVDF) were dispersed in N-methyl-2-pyrrolidone (NMP) at a mass ratio of 8:1:1, and a uniform slurry was formed after vigorous stirring, and then The slurry was uniformly coated on an aluminum foil, and dried under vacuum at 120°C for 12 h.

[0025] (3) The prepared ZIF-67 was ground into powder, and then added to the mixed solution of PVDF and NMP. Stir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an electrode supporting zeolite imidazole diaphragm of a lithium ion battery. The porous diaphragm disclosed by the invention is prepared from Zeoliticimidazolate fraemwroks (ZIFs), wherein the Zeolitic imidazolate fraemwroks are Metal organic frameworks (MOFs) which are prepared from tetrahedral coordination configuration transition metal of cobalt, zinc, copper and the like, levomisole and derivative ligand coordination of the transition metal and the levomisole, and the ZIFs are a novel MOFs material. According to the preparation method disclosed by the invention, the prepared ZIF-67 is directly covered to the surface of an electrode material to form the electrode supporting diaphragm. Compared with a polyolefin diaphragm, the ZIF-67 diaphragm has good electrolyte wettability, high-temperature stability, higher discharge capacity and better cycling stability. The ZIF-67 is proved to have the potential of serving as a lithium ion battery diaphragm.

Description

technical field [0001] The invention specifically relates to a lithium-ion battery electrode-supported zeolite imidazole diaphragm and a preparation method thereof, belonging to the technical field of lithium-ion batteries. Background technique [0002] Among the various components that make up the battery, the separator plays an important role. Its structure and performance determine the interface structure and internal resistance of the battery, which greatly affects the performance of the battery, including the energy and power density of the battery, cycle life and safety performance etc. With the continuous development of lithium-ion batteries in the energy storage and electric vehicle markets, the demand for lithium battery separators continues to increase. At present, my country is already the world's largest lithium battery production and manufacturing base, the second largest lithium battery producer and exporter, and my country's demand for separators is increasin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M2/14H01M2/16H01M10/0525H01M50/403H01M50/446
CPCH01M10/0525H01M50/403H01M50/411Y02E60/10
Inventor 沈建兴陈攀代孟李敏王帅
Owner QILU UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com