Hydrogenated epoxy vinyl resin-modified nitrile butadiene rubber material and preparation method thereof

A technology of epoxy vinyl resin and nitrile rubber, which is applied in the field of rubber modification, can solve the problems of poor loss, poor insulation performance, and low elasticity, and achieve improved elasticity, guaranteed oil resistance and sealing, and simple preparation process Effect

Inactive Publication Date: 2018-08-17
常州市五洲化工有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing nitrile rubber also has fatal shortcomings, such as poor low temperature resistance, poor ozone resistance, poor insulation performance, and low elasticity, so its wearability is poor, and its scope of use is severely limited. When it belongs to cold environment, Nitrile rubber is prone to cracking and can easily cause serious hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] A kind of preparation method of hydrogenated epoxy vinyl resin modified nitrile rubber, the specific preparation steps of a kind of hydrogenated epoxy vinyl resin modified nitrile rubber described in claim 1-7 are as follows:

[0048] Step (1): Mix and masticate the epichloride rubber latex and styrene-butadiene rubber latex, then add silicon micropowder and mix evenly, and then carry out compound treatment in an electric field to obtain a mixed masterbatch of epichloride rubber and styrene-butadiene rubber;

[0049] Step (2): Dispersing the mixed masterbatch in step (1) in an organic solvent to form epichlorohydrin-styrene-butadiene rubber latex;

[0050] Step (3): mixing and modifying nitrile rubber and hydrogenated epoxy vinyl resin to obtain modified nitrile rubber mixing;

[0051] Step (4): dispersing the modified nitrile rubber compound obtained in step (3) in an organic solvent to form a modified nitrile rubber latex;

[0052] Step (5): Blend the chloroether rub...

Embodiment 1

[0055] Raw material and each material component are as follows in the present embodiment:

[0056] Nitrile rubber (1200) 40 parts

[0057] Styrene Butadiene Rubber (400) 10 parts

[0058] Chlorine ether rubber (400) 25 parts

[0059] Vulcanizing agent (zinc oxide) 0.1 parts

[0060] Silica powder 4 parts

[0061] Hydrogenated epoxy vinyl resin 4 parts

[0062] Anti-aging agent (N,N-nickel dibutyldithiocarbamate) 2 parts

[0063] Plasticizer (polyether plasticizer) 2 parts

[0064] Organic solvent (dioctyl sebacate) 15 parts

[0065] The preparation steps are as follows:

[0066] Step (1): Mix and masticate chloroether rubber latex and styrene-butadiene rubber latex for 10 minutes, then add silicon micropowder and mix evenly, and then perform compound treatment in an electric field of 0.6kv / m to obtain a mixed masterbatch of chloroether rubber-styrene-butadiene rubber glue;

[0067]Step (2): Dispersing the mixed masterbatch in step (1) in an organic solvent to form epi...

Embodiment 2

[0072] Raw material and each material component are as follows in the present embodiment:

[0073] Nitrile rubber (1200) 70 parts

[0074] Styrene Butadiene Rubber (400) 25 parts

[0075] Chlorine ether rubber (400) 10 parts

[0076] Vulcanizing agent (magnesia) 3 parts

[0077] Silica powder 12 parts

[0078] Hydrogenated epoxy vinyl resin 10 parts

[0079] Anti-aging agent (N,N-nickel dibutyldithiocarbamate) 5 parts

[0080] Plasticizer (polyether plasticizer) 5 parts

[0081] Organic solvent (dioctyl sebacate) 45 parts

[0082] The preparation steps are as follows:

[0083] Step (1): Mix and masticate chloroether rubber latex and styrene-butadiene rubber latex for 20 minutes, then add silicon micropowder and mix evenly, and then perform compound treatment in an electric field of 1.2kv / m to obtain a mixed masterbatch of chloroether rubber-styrene-butadiene rubber glue;

[0084] Step (2): Dispersing the mixed masterbatch in step (1) in an organic solvent to form epic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a hydrogenated epoxy vinyl resin-modified nitrile butadiene rubber material and a preparation method thereof. The hydrogenated epoxy vinyl resin-modified nitrile butadiene rubber material is prepared from the following raw materials in parts by weight: 40 to 70 parts of nitrile butadiene rubber; 10 to 25 parts of styrene butadiene rubber; 10 to 25 parts of epichlorohydrin rubber; 0.1 to 3 parts of vulcanizing agent; 4 to 12 parts of silicon powder; 4 to 10 parts of hydrogenated epoxy vinyl resin; 2 to 5 parts of anti-aging agent; 2 to 5 parts of plasticizer; and 15 to 45 parts of organic solvent. According to the hydrogenated epoxy vinyl resin-modified nitrile butadiene rubber material and the preparation method thereof provided by the invention, the preparation process is simple, not only are the oil resistance and leak tightness of the nitrile butadiene rubber ensured, but also the elasticity, tensile strength and low temperature resistance of the nitrile butadiene rubber are increased, and application to multiple aspects is met.

Description

technical field [0001] The invention relates to a hydrogenated epoxy vinyl resin modified nitrile rubber material and a preparation method thereof, belonging to the field of rubber modification. Background technique [0002] Nitrile rubber is produced by butadiene and acrylonitrile by low-temperature emulsion polymerization. It has excellent oil resistance, high wear resistance, good heat resistance, strong adhesion, good water resistance, and air tightness. sex and excellent. Nitrile rubber is widely used in the production of various oil-resistant rubber products, various oil-resistant gaskets, gaskets, sleeves, flexible packaging, soft hoses, printing and dyeing rubber rollers, cable rubber materials, etc. Essential elastic material. However, the existing nitrile rubber also has fatal shortcomings, such as poor low temperature resistance, poor ozone resistance, poor insulation performance, and low elasticity, so its wearability is poor, and its scope of use is severely l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L9/06C08L71/03C08L63/00C08K3/36C08K3/22
CPCC08K2003/222C08K2003/2296C08L9/02C08L2205/035C08L9/06C08L71/03C08L63/00C08K3/36C08K3/22
Inventor 张莉娜方春平
Owner 常州市五洲化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com