A kind of PVC wood grain film adhesive preparation method

A bonding adhesive and film technology, applied in the direction of adhesive type, ester copolymer adhesive, polymer adhesive additive, etc., can solve the problem of easy peeling and poor bonding strength between plastic wood flooring and wood grain PVC film , strong adhesive force and other issues, to achieve the effect of stable and controllable reaction process, not easy to delaminate, and strong adhesive force

Active Publication Date: 2019-12-13
DUALSHINE TECH SHENZHEN
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims to solve the problem that the acrylic adhesives in the prior art generally have low initial adhesion and poor bonding strength, which makes it easy to peel off between the plastic wood floor and the wood grain PVC film, and provides a simple process step , the preparation method of PVC wood grain film adhesive glue with stable and controllable reaction process, the prepared product can be cross-linked and solidified at room temperature, has good stability, is not easy to delaminate, and has strong adhesive force. It is not easy to peel off and has high promotion value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of PVC wood grain film adhesive preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022](1) Ingredients: Weigh each component according to the following weight ratio: 550g deionized water, 40g N-methylolacrylamide, 300g butyl acrylate, 300g vinyl acetate, 40g composite emulsifier and anionic surfactant twelve Alkyl sodium sulfate mixed in a mass ratio of 1:2), 2g composite initiator (mixed with potassium persulfate and sodium metabisulfite in a mass ratio of 1:1), 100g emulsified rosin tackifier, butyl acrylate and Vinyl acetate is mixed to obtain mixed monomers; the emulsified rosin tackifier is prepared by the following method: first add rosin to a flask, add an appropriate amount of toluene and dibutyl phthalate, heat until the rosin is completely melted, and then add the emulsifier Dissolve the co-emulsifier in an appropriate amount of deionized water and add it to the above-mentioned molten rosin. At the same time, add the deionized water dropwise under stirring at a temperature of 80°C. After the addition of the deionized water is completed, continue s...

Embodiment 2

[0030] (1) Ingredients: Weigh each component according to the following weight ratio: 580g deionized water, 45g N-methylolacrylamide, 350g butyl acrylate, 350g vinyl acetate, 45g compound emulsifier and anionic surfactant twelve Alkyl sodium sulfate mixed according to the mass ratio of 1:2.5), 2.5g composite initiator (mixed by potassium persulfate and sodium metasulfite according to the mass ratio of 1:1.1), 150g emulsified rosin tackifier, butyl acrylate Mixed with vinyl acetate to obtain a mixed monomer; the emulsified rosin tackifier is prepared by the following method: first add rosin to a flask, add an appropriate amount of toluene and dibutyl phthalate, heat until the rosin is completely melted, and then emulsify Dissolve the agent and co-emulsifier in deionized water and add it to the above-mentioned molten rosin. At the same time, add the deionized water dropwise under stirring at a temperature of 82°C. After the addition of the deionized water is completed, continue t...

Embodiment 3

[0038] (1) Ingredients: Weigh each component according to the following weight ratio: 600g deionized water, 50g N-methylolacrylamide, 400g butyl acrylate, 400g vinyl acetate, 50g composite emulsifier and anionic surfactant twelve Sodium alkyl sulfate mixed according to the mass ratio of 1:3), 3g composite initiator (mixed by potassium persulfate and sodium metasulfite according to the mass ratio of 1:1.2), 200g emulsified rosin tackifier, butyl acrylate and Vinyl acetate is mixed to obtain mixed monomers; the emulsified rosin tackifier is prepared by the following method: first add rosin to a flask, add an appropriate amount of toluene and dibutyl phthalate, heat until the rosin is completely melted, and then add the emulsifier Dissolve the co-emulsifier in an appropriate amount of deionized water and add it to the above-mentioned molten rosin. At the same time, add the deionized water dropwise under stirring at a temperature of 85°C. After the addition of the deionized water i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention relates to a bonding agent, and discloses a preparation method of PVC (polyvinyl chloride) wood grain thin film bonding glue by aiming at solving the problems that in the prior art, thegeneral initial adhesion of an acrylate bonding agent is low, and the bonding intensity is poorer, so that a Plastic wood floor and a PVC wood grain thin film can easily peel. The preparation method comprises the following steps of (1) material preparation; (2) pre-emulsification; (3) pre-polymerization; (4) copolymerization; (5) blending. The types and the composition of comonomers are optimized;an emulsified rosin thickening agent is added; the process steps are simple; the reaction process is stable and controllable; the prepared product can be crosslinked and cured at normal temperature;the stability is good; the layering cannot easily occur; the bonding force is strong; the plastic wood floor and the PVC wood grain thin film cannot easily peel; higher popularization values are realized.

Description

technical field [0001] The invention relates to an adhesive, in particular to a method for preparing PVC wood grain film adhesive. Background technique [0002] Wood-plastic composite floor is a kind of wood (wood cellulose, plant cellulose) as the basic material, thermoplastic polymer materials (PE, PVC plastic) and processing aids, etc., mixed evenly and then heated and extruded by mold equipment The high-tech green environmental protection material has the properties and characteristics of wood and plastic, and can replace wood. [0003] One of the plastic-wood composite floor surfaces is compounded with a PVC film with printed wood grains, which needs to be coated with a layer of adhesive on the surface of the plastic-wood composite floor during production. The adhesive currently used is a commercially available two-component adhesive, which needs to be mixed with component A (main agent) and component B (curing agent) during use, which is very inconvenient to use. In ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J133/08C09J11/08C08F220/18C08F218/08C08F220/58C08F2/26C08F2/30
CPCC08F2/26C08F2/30C08F218/08C08F220/18C08F220/1804C09J11/08C09J133/24C08L93/04C08F220/58
Inventor 程嘉义
Owner DUALSHINE TECH SHENZHEN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap