Insulated layer and sheath material of charging pile connecting cable and preparation method for insulated layer and sheath material

A sheath material, a technology for connecting cables, applied in the directions of insulators, insulated conductors, insulated cables, etc., can solve problems such as poor low temperature resistance and flexibility

Inactive Publication Date: 2018-08-03
金龙电缆科技有限公司
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The cable insulation layer and sheath material of the invention have better flexibility, but its low temperature resistance and flexibility under low temperature environment are poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Insulated layer and sheath material of charging pile connecting cable and preparation method for insulated layer and sheath material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025]The preparation method of the insulating layer and the sheath material of the charging pile connecting cable comprises the following steps:

[0026] S1: Add polyvinyl chloride resin, ethylene vinyl acetate copolymer, hydrogenated nitrile rubber, acrylate rubber, and cross-linking agent into the mixer and stir evenly, then add accelerator, anti-aging agent, and plasticizer, and heat up to 70- Mix at 80°C for 6-10 minutes to obtain mixed material A; the stirring speed of the mixer is 200-500r / min;

[0027] S2: Add anti-scorch agent, stabilizer, polymer compatibilizer, coupling agent, naphthenic oil, polychlorotrifluoroethylene, polyethylene wax to the mixed material A in step S1, then heat up to 90-110°C, mix 6-8min, to obtain the mixed material B;

[0028] S3: Put the mixed material B in step S2 into a twin-screw extruder to granulate at a processing temperature of 150-180° C. to obtain insulation layer and sheath material for cables.

Embodiment 1

[0030] An insulation layer and sheath material for a charging pile connection cable, in parts by weight, including the following raw materials: 40 parts of polyvinyl chloride resin, 45 parts of ethylene vinyl acetate copolymer, 13 parts of hydrogenated nitrile rubber, and 12 parts of acrylic rubber part, 0.1 part of crosslinking agent, 0.3 part of flame retardant, 0.2 part of anti-scorch agent, 0.3 part of accelerator, 0.2 part of antioxidant, 0.2 part of anti-aging agent, 0.5 part of plasticizer, 0.2 part of stabilizer, polymer phase 0.4 parts of solvent, 0.3 parts of coupling agent, 0.3 parts of naphthenic oil, 0.5 parts of polychlorotrifluoroethylene, and 0.2 parts of polyethylene wax.

[0031] The cross-linking agent is triallyl cyanurate; the flame retardant is a mixture of red phosphorus and aluminum hydroxide; the anti-scorch agent is N-cyclohexylthiophthalimide; The accelerator is dipentamethylenethiuram tetrasulfide; the antioxidant is propylene pentaerythritol ester;...

Embodiment 2

[0037] An insulation layer and sheath material for a charging pile connection cable, in parts by weight, including the following raw materials: 30 parts of polyvinyl chloride resin, 40 parts of ethylene vinyl acetate copolymer, 15 parts of hydrogenated nitrile rubber, and 11 parts of acrylic rubber part, 0.3 part of crosslinking agent, 0.2 part of flame retardant, 0.4 part of anti-scorch agent, 0.2 part of accelerator, 0.2 part of antioxidant, 0.5 part of anti-aging agent, 0.4 part of plasticizer, 0.1 part of stabilizer, polymer phase 0.6 parts of solvent, 0.2 parts of coupling agent, 0.2 parts of naphthenic oil, 0.3 parts of polychlorotrifluoroethylene, and 0.1 parts of polyethylene wax.

[0038] The cross-linking agent is triallyl cyanurate; the flame retardant is a mixture of red phosphorus and aluminum hydroxide; the anti-scorch agent is N-cyclohexylthiophthalimide; The accelerator is dipentamethylene thiuram tetrasulfide; the antioxidant is stearyl propionate; the antioxi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an insulated layer and sheath material of a charging pile connecting cable, and belongs to the technical field of preparation. The insulated layer and sheath material of the charging pile connecting cable is prepared from the following raw materials: polyvinyl chloride resin, ethylene vinyl acetate copolymer, hydrogenated butadiene-acrylonitrile rubber, acrylate rubber, a cross-linking agent, a flame retardant, a scorch retarder, an accelerant, an anti-oxidant, an anti-ageing agent, a plasticizer, a stabilizer, a high molecular weight compatibilizer, a coupling agent, naphthenic oil, polytrifluorochloroethylene, and polyethylene wax. Tensile strength, elongation at break and electrical resistivity of the cable insulated layer and sheath material are improved througha reinforcing system which is prepared from naphthenic oil, polytrifluorochloroethylene and polyethylene wax, and reduces thermal deformation.

Description

technical field [0001] The invention belongs to the technical field of cable preparation, and in particular relates to an insulating layer and a sheath material of a charging pile connection cable and a preparation method thereof. Background technique [0002] At present, the existing electric vehicle charging pile connecting cable adopts a circular structure. During the charging process of the electric vehicle, the connecting cable needs to move back and forth between the vehicle and the charging pile. Since the connecting cable is exposed to the atmosphere for a long time, such a long time In use, it is inevitable that the cables will be squeezed and worn by external forces, which will affect the service life of the cables. The material is not soft enough. After the electric vehicle is charged, the cable can only be slowly retracted into the charging pile under the action of external force. When charging is required, the charging gun and the cable must be pulled out slowly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L27/06C08L15/00C08L33/08C08L23/06C08L27/12C08L51/06C08L91/00C08K13/02C08K3/02C08K3/22C08K5/3492H01B3/44H01B7/17
CPCC08K2003/026C08K2003/2227C08L23/0853C08L27/06C08L2203/202C08L2205/035C08L2205/08H01B3/441H01B3/443H01B7/18C08L15/005C08L33/08C08L23/06C08L27/12C08L51/06C08L91/00C08K13/02C08K3/02C08K3/22C08K5/34924
Inventor 毛冰花圣纪生章俊
Owner 金龙电缆科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com