Waterproof heat-insulation exterior wall coating and preparation method thereof

An exterior wall paint, pigment and filler technology, applied in the field of paint, can solve the problems of poor waterproof and moisture-proof performance, poor flame retardant performance, etc., and achieve the effects of high waterproofness, easy industrial production, and simple preparation process

Inactive Publication Date: 2018-07-27
HEFEI DAZHUO ELECTRIC POWER CO LTD
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although the existing technology has improved the cohesiveness of putty powder to a certain extent, it often has defects such as poor waterproof and moisture-proof performance and poor flame retardant performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof heat-insulation exterior wall coating and preparation method thereof
  • Waterproof heat-insulation exterior wall coating and preparation method thereof
  • Waterproof heat-insulation exterior wall coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The waterproof and heat-insulating exterior wall paint of the present embodiment, in parts by weight, said material mainly includes the following components:

[0033]

[0034]

[0035] The nano-SiO2 airgel porosity of present embodiment is 85%-95%, and average aperture is 20nm, and specific surface area is 800-1100m 2 / g, the aluminum silicate fiber has a length of 0.25-2.2 μm and a diameter of 3-6 μm.

[0036] The pigments and fillers in this embodiment are selected from one or more of titanium dioxide, barium sulfate, and mica powder.

[0037] The dispersant in this embodiment is selected from any one of BYK-190, BYK-155, BYK-187 and BYK-184.

[0038] The leveling agent in this embodiment is selected from polyurethane leveling agents.

[0039] The film-forming aid of this embodiment is selected from Alcohol Twelve.

[0040] The present invention also provides a preparation method of waterproof and heat-insulating exterior wall coating, comprising the followin...

Embodiment 2

[0047] The waterproof and heat-insulating exterior wall paint of the present embodiment, in parts by weight, said material mainly includes the following components:

[0048]

[0049] The nano-SiO2 airgel porosity of present embodiment is 85%-95%, and average aperture is 20nm, and specific surface area is 800-1100m 2 / g, the aluminum silicate fiber has a length of 0.25-2.2 μm and a diameter of 3-6 μm.

[0050] The pigments and fillers in this embodiment are selected from one or more of titanium dioxide, barium sulfate, and mica powder.

[0051] The dispersant in this embodiment is selected from any one of BYK-190, BYK-155, BYK-187 and BYK-184.

[0052] The leveling agent in this embodiment is selected from polyurethane leveling agents.

[0053] The film-forming aid of this embodiment is selected from Alcohol Twelve.

[0054] The present invention also provides a preparation method of waterproof and heat-insulating exterior wall coating, comprising the following steps:

...

Embodiment 3

[0061] The waterproof and heat-insulating exterior wall paint of the present embodiment, in parts by weight, said material mainly includes the following components:

[0062]

[0063]The nano-SiO2 airgel porosity of present embodiment is 85%-95%, and average aperture is 20nm, and specific surface area is 800-1100m 2 / g, the aluminum silicate fiber has a length of 0.25-2.2 μm and a diameter of 3-6 μm.

[0064] The pigments and fillers in this embodiment are selected from one or more of titanium dioxide, barium sulfate, and mica powder.

[0065] The dispersant in this embodiment is selected from any one of BYK-190, BYK-155, BYK-187 and BYK-184.

[0066] The leveling agent in this embodiment is selected from polyurethane leveling agents.

[0067] The film-forming aid in this embodiment is selected from Alcohol Twelve.

[0068] The present invention also provides a preparation method of waterproof and heat-insulating exterior wall coating, comprising the following steps:

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Average pore sizeaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a waterproof heat-insulation exterior wall coating and a preparation method thereof. The waterproof heat-insulation exterior wall coating comprises the following components inparts by weight: 22-42 parts of a silicone-acrylic emulsion, 5-12 parts of alumina silicate fiber, 8-15 parts of hollow glass bead, 4-9 parts of pigments and fillers, 3-7 parts of expanded vermiculite, 1.3-2.8 parts of a dispersant, 0.6-1.4 parts of a levelling agent, 1.6-3.8 parts of a film-forming auxiliary agent, and 13-18 parts of deionized water. The waterproof heat-insulation exterior wall coating has excellent waterproof heat-insulation performance, the silicone-acrylic emulsion is used as a film-forming object, and fillers such as a nano SiO2 aerogel, hollow glass bead and expanded vermiculite are cooperated, and under cooperation of a plurality of auxiliary agents, the prepared coating has good heat insulation and water resisting performance.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a waterproof and heat-insulating exterior wall coating and a preparation method thereof. Background technique [0002] Paint is coated on the surface of the object to be protected or decorated, and can form a continuous film firmly attached to the object to be coated, usually based on resin, or oil, or emulsion, with or without adding pigments, fillers, and adding corresponding Additives, viscous liquids prepared with organic solvents or water. A layer of paint is often required on the outside of the wall to play a certain protective role. The exterior wall has high requirements for the paint. The existing paint often has defects such as poor waterproof and moisture-proof performance and poor flame retardancy. [0003] In China's published patent application CN102875086A, for the preparation of putty powder with strong water resistance and cohesiveness, sepiolite powder, kaolin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/04C09D7/61C09D7/63C09D7/47
CPCC09D143/04C08K2201/011C09D7/47C09D7/61C09D7/63C09D7/70C08L75/04C08K13/04C08K7/26C08K7/10C08K7/28
Inventor 杨自芬
Owner HEFEI DAZHUO ELECTRIC POWER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com