Processing method of baking-free colorful tiles

A processing method and technology for bricks and tiles are applied in the processing field of non-burning colorful bricks and tiles, which can solve the problems of high cost, various types of materials, heavy weight, etc., and achieve the effects of low cost, good development prospect and light weight.

Inactive Publication Date: 2018-07-27
武威霖沐科技发展有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of this, the present invention provides a processing method of non-fired colorful tiles. The present invention overcomes the shortcomings of existing similar products such as many types of materials, heavy weight, and high cost, and provides a low-cost, light-weight, high-strength The non-burning and non-steaming building block bricks and their manufacturing process utilize and improve the activity of industrial waste residues to make them have gelling properties, thereby reducing the amount of cement and reducing costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of processing method of fire-free colorful brick and tile, it is the following steps:

[0023] 1) Clean up the operation table, after it is leveled, put the asbestos tile mould, polyester mould, and flat steel frame, then spread the surface material on the polyester mould, then spread 400 grams of glass fiber filaments, and use a wipe Press it evenly, then spread one-third of the back layer material, compact it, then spread 300 grams of glass fiber filaments, and finally spread two thirds of the back layer material, use a trowel to flatten and spread the polyester film. ;

[0024] 2) The molded tiles should be removed from the mold after eight hours. Do not wipe the surface of the tiles after removing the molds. Stack the tiles face-to-face or back-to-back or well stacked. The stacking height should not exceed 1.5m. Stop and harden for 15 days.

[0025] The surface material is made by mixing magnesium oxide, fly ash or talcum powder, 191 resin, pigment and magn...

Embodiment 2

[0029] A kind of processing method of fire-free colorful brick and tile, it is the following steps:

[0030] 1) Clean up the operation table, after it is leveled, put the asbestos tile mould, polyester mould, and flat steel frame, then spread the surface material on the polyester mould, then spread 400 grams of glass fiber filaments, and use a wipe Press it evenly, then spread one-third of the back layer material, compact it, then spread 300 grams of glass fiber filaments, and finally spread two thirds of the back layer material, use a trowel to flatten and spread the polyester film. ;

[0031] 2) The molded tiles should be removed from the mold after eight hours. Do not wipe the surface of the tiles after removing the molds. Stack the tiles face-to-face or back-to-back or well stacked. The stacking height should not exceed 1.5m. Stop and harden for 15 days.

[0032] The surface material is made by mixing magnesium oxide, fly ash or talcum powder, 191 resin, pigment and magn...

Embodiment 3

[0036] A kind of processing method of fire-free colorful brick and tile, it is the following steps:

[0037] 1) Clean up the operation table, after it is leveled, put the asbestos tile mould, polyester mould, and flat steel frame, then spread the surface material on the polyester mould, then spread 400 grams of glass fiber filaments, and use a wipe Press it evenly, then spread one-third of the back layer material, compact it, then spread 300 grams of glass fiber filaments, and finally spread two thirds of the back layer material, use a trowel to flatten and spread the polyester film. ;

[0038] 2) The molded tiles should be removed from the mold after eight hours. Do not wipe the surface of the tiles after removing the molds. Stack the tiles face-to-face or back-to-back or well stacked. The stacking height should not exceed 1.5m. Stop and harden for 15 days.

[0039] The surface material is made by mixing magnesium oxide, fly ash or talcum powder, 191 resin, pigment and magn...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a processing method of baking-free colorful tiles. The method comprises the steps that 1) after an operation table is cleaned and leveled, an asbestos tile mold, a polyester mold and a flat steel frame are placed on the operation table, and then a thin surface-layer material is laid uniformly on the polyester mold, 400 grams of glass fiber filaments are laid, a trowel is used to press the glass fiber filaments uniformly, then one third of a back-layer materials are laid and compacted, then 300 grams of the glass fiber filaments are laid, the two thirds of the back-layermaterials are laid and flattened and compacted by the trowel, and finally a polyester film is laid on the two thirds of the back-layer materials; and 2), demolding is carried out on the formed tilesafter eight hours, wiping the tile surfaces is not allowed after the mold is stripped, then the tiles are stacked in a face-to-face and back-to-back mode or are stacked into the shape like a Chinese character "jing", the stacking height is not more than 1.5 m, and then after airing is carried out on the stacked tiles for 10 days, the stacked tiles are left to stand to be hardened for 15 days. According to the processing method of the baking-free colorful tiles, the tiles belong to building blocks which are low in cost, light in weight, high in strength and free of baking and steaming, the activity of industrial waste residues is utilized and improved, so that the industrial waste residues are enabled to have gel property, then the use amount of cement is reduced, and the cost is reduced.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a method for processing non-fired colorful bricks and tiles. Background technique [0002] Wall materials are indispensable and important building materials in the construction industry. The construction industry is also a pillar industry of the national economy and plays an irreplaceable role in promoting the process of modernization in my country. Its huge construction market capacity also provides a very broad prospect for the production of wall materials. Contents of the invention [0003] In view of this, the present invention provides a processing method of non-fired colorful tiles. The present invention overcomes the shortcomings of existing similar products such as many types of materials, heavy weight, and high cost, and provides a low-cost, light-weight, high-strength The non-burning and non-steaming building block brick and its manufacturing process utili...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B28B1/29B28B1/52B28B19/00C04B28/32
CPCB28B1/29B28B1/522B28B19/0015C04B28/32C04B22/066C04B18/08C04B24/24C04B2103/54C04B22/124C04B14/042C04B18/26
Inventor 梁兴旺吴文才
Owner 武威霖沐科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com