A kind of graft copolymer containing epoxy group and its application

A graft copolymer and epoxy group technology, which is applied in the synthesis and application of graft copolymers, can solve problems such as poor compatibility and limited application, achieve good compatibilization effect, and enhance the combination between two phases. strength, the effect of improving compatibility

Active Publication Date: 2019-11-19
KINGFA SCI & TECH CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nevertheless, the polymer segment of the side chain of the compatibilizer in this patent is mainly a homopolymer of methacrylate or acrylate monomers, and in practical applications, the side chain and another phase state are often not very good. compatible
At the same time, a single homopolymer on the side chain of the compatibilizer has specific polarity and solubility parameters, which also limits its application to a certain extent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of graft copolymer containing epoxy group and its application
  • A kind of graft copolymer containing epoxy group and its application
  • A kind of graft copolymer containing epoxy group and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Under the protection of nitrogen, mix and stir 80g methyl methacrylate, 20g ethyl acrylate, 1.5g chain transfer agent mercaptopropanol, 4.5g initiator azobisisobutyronitrile and 200g solvent toluene, and then move to a stirring In a four-necked flask with a paddle, a condenser and a thermometer, heat to 65°C, and react for 6 hours to obtain a toluene solution containing polymer D; lower the reaction system to room temperature, add 0.01g of polymerization inhibitor hydroquinone, 0.04g Catalyst N,N-dimethylbenzylamine and 2.1g of monomer E methacryloyl chloride containing carbon-carbon double bonds (the molar ratio of polymer D to monomer E is 1:1.2), after stirring at room temperature for 8 hours, the product After rotary evaporation and drying, a polymer C containing a carbon-carbon double bond was obtained, and the number average molecular weight of the obtained polymer C was about 4200 through GPC testing.

[0051] Under nitrogen protection, 80g methyl methacrylate, 4...

Embodiment 2

[0053] Under nitrogen protection, after mixing and stirring 60g methyl methacrylate, 50g butyl acrylate, 1.5g chain transfer agent mercaptopropanol, 3.5g initiator azobisisobutyronitrile and 250g solvent xylene, move to a In a four-neck flask with a stirring blade, a condenser and a thermometer, heat to 65°C and react for 6 hours to obtain a xylene solution containing polymer D; lower the reaction system to room temperature, add 0.01g of polymerization inhibitor hydroquinone, 0.02g catalyst triethylamine and 2.1g carbon-carbon double bond-containing monomer E methacryloyl chloride (the molar ratio of polymer D to monomer E is 1:1.2), stirred at room temperature for 5 hours, and the product was dried by rotary evaporation , to obtain a carbon-carbon double bond-containing polymer C. According to the GPC test, it can be seen that the number average molecular weight of the obtained polymer C is about 5100.

[0054] Under nitrogen protection, 110g of styrene, 20g of ethyl acrylat...

Embodiment 3

[0056] Under the protection of nitrogen, mix and stir 80g ethyl methacrylate, 40g butyl acrylate, 2g chain transfer agent mercaptoethanol, 1.2g initiator azobisisoheptanonitrile and 150g solvent ethyl acetate, and then move to a stirring Paddle, condenser and a four-necked flask with a thermometer, heated to 70°C, and reacted for 5 hours to obtain an ethyl acetate solution containing polymer D; the reaction system was lowered to room temperature, and 0.01g of polymerization inhibitor hydroquinone, 0.02g catalyst triethylamine and 5.0g carbon-carbon double bond-containing monomer E isocyanoethyl methacrylate (the molar ratio of polymer D to monomer E is 1:1.25), after stirring at room temperature for 10 hours, the product After rotary evaporation and drying, a high molecular polymer C containing carbon-carbon double bonds is obtained. According to the GPC test, it can be seen that the number average molecular weight of the obtained polymer C is about 11900.

[0057] Under nitr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
degree of graftingaaaaaaaaaa
Login to View More

Abstract

The invention discloses a graft copolymer containing epoxy groups and its application. The graft copolymer is a type of polymer containing epoxy groups and polymer copolymer side chains, mainly composed of 40wt%~90wt% monomer A containing carbon-carbon double bonds, 5wt%~30wt% containing epoxy The radical unsaturated monomer B and 5wt%~30wt% carbon-carbon double bond-containing polymer C are copolymerized by free radical polymerization. The preparation process is as follows: firstly, the high molecular polymer D is obtained by free radical copolymerization, and then the high molecular polymer C containing carbon-carbon double bonds is prepared by using the reaction between the groups; finally, the obtained high molecular polymer C and the monomer A 1. Carrying out free radical copolymerization of monomer B, and obtaining a graft copolymer containing epoxy groups after drying and devolatilization. The epoxy group-containing graft copolymer of the present invention can be used as a compatibilizer for blended polymers and a chain extender for polymers.

Description

technical field [0001] The invention relates to the synthesis and application fields of graft copolymers, in particular to an epoxy group-containing acrylate graft copolymer and its application. Background technique [0002] Compatibilizer refers to the use of physical or chemical means to promote the combination of incompatible blending systems, and then obtain a stable blending system additives. For polymer blends, phase separation due to differences in chemical structure, polarity, molecular weight (viscosity) and crystallinity between the components results in poor performance of the polymer blend. Therefore, compatibilizers are the cornerstone of high-level blend modification products. Especially in the current market of raw materials and modified materials, the production formula and process flow of enterprises are mostly open and transparent, and the addition of compatibilizers has become the key to the differentiation of material modified manufacturers and competito...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F265/06C08F265/04C08F220/14C08F220/18C08F220/32C08F216/14C08F212/12C08F220/44C08F8/30C08F8/00
CPCC08F8/00C08F8/30C08F220/14C08F265/04C08F265/06C08F220/1804C08F220/325C08F8/44C08F220/1802C08F212/08C08F212/12C08F220/44C08F220/1808C08F216/1416C08F216/14C08F290/04C08L51/00
Inventor 李坤泉柴生勇刘振峰李积德孔蕾陈林刘勤李岩
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com