One-component polyurethane adhesive for furniture and preparation method of one-component polyurethane adhesive

A polyurethane adhesive, one-component technology, applied in the direction of polyurea/polyurethane adhesives, adhesives, adhesive additives, etc., can solve the problems of difficult pollutant treatment and discharge, human harm, and high content, and achieve flame retardant performance. Good effect of improving antibacterial properties and excellent toughness

Inactive Publication Date: 2018-06-29
昆山市冠宝化学有限公司
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polyurethane adhesives were first industrialized in Germany in the 1940s, mainly including polyisocyanate solvent adhesives, thermoplastic polyurethane solvent adhesives, reactive single- and two-component solvent adhesives, solvent-free, water-dispersed, hot-melt polyurethane adhesives, etc. ; There are many types of synthetic raw materials and additives. Starting from molecular design, a series of adhesives with a wide range of performance can be synthesized and formulated, which can meet the requirements of different substrate bonding and use conditions. In the prior art, the traditional flame retardant Most of the agents are organophosphorus or halogen-containing flame retardants, but the content of free formaldehyde in the finished furniture or the content of halogen elements in the flame retardant is high, which is harmful to the human body, not environmentally friendly, and it is difficult to treat and discharge pollutants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A preparation method of one-component polyurethane adhesive for furniture, comprising the following steps:

[0021] (1) Add graphene oxide and tetraglycidyl ether tetraphenylethane into acetone, stir at reflux for 20 minutes, add glyceryl monostearate and diphenylsilanediol, continue stirring for 10 minutes, and then add paraffin , ammonium hexachloroiridate, stirred for 30 minutes to obtain a functional system;

[0022] (2) Mixing mass concentration of 10% polyvinyl alcohol (the average molecular weight of polyvinyl alcohol is 4800) aqueous solution, tetraphenyl porphyrin iron, hydrogen peroxide, stirred at 80°C for 3 hours, then rotary evaporated to remove water, then added hexaethylene oxide Methyl diisocyanate, 1,3,5-triglycidyl-S-triazinetrione, reflux and stir for 5 minutes, then add glycerol, stir to obtain a modified system;

[0023] (3) After mixing diethylene glycol, o-hydroxybenzoic acid, and N-methylpyrrolidone, stir at 60°C for 1 hour, then add 2-mercaptop...

Embodiment 2

[0027] A preparation method of one-component polyurethane adhesive for furniture, comprising the following steps:

[0028] (1) Add graphene oxide and tetraglycidyl ether tetraphenylethane into acetone, stir at reflux for 20 minutes, add glyceryl monostearate and diphenylsilanediol, continue stirring for 10 minutes, and then add paraffin , ammonium hexachloroiridate, stirred for 30 minutes to obtain a functional system;

[0029] (2) Mixing mass concentration of 10% polyvinyl alcohol (the average molecular weight of polyvinyl alcohol is 4200) aqueous solution, tetraphenyl porphyrin iron, hydrogen peroxide, stirred at 80°C for 3 hours, then rotary evaporated to remove water, then added hexaethylene oxide Methyl diisocyanate, 1,3,5-triglycidyl-S-triazinetrione, reflux and stir for 5 minutes, then add glycerol, stir to obtain a modified system;

[0030](3) After mixing diethylene glycol, o-hydroxybenzoic acid, and N-methylpyrrolidone, stir at 60°C for 1 hour, then add 2-mercaptopy...

Embodiment 3

[0034] A preparation method of one-component polyurethane adhesive for furniture, comprising the following steps:

[0035] (1) Add graphene oxide and tetraglycidyl ether tetraphenylethane into acetone, stir at reflux for 20 minutes, add glyceryl monostearate and diphenylsilanediol, continue stirring for 10 minutes, and then add paraffin , ammonium hexachloroiridate, stirred for 30 minutes to obtain a functional system;

[0036] (2) Mixing mass concentration of 10% polyvinyl alcohol (the average molecular weight of polyvinyl alcohol is 4800) aqueous solution, tetraphenyl porphyrin iron, hydrogen peroxide, stirred at 80°C for 3 hours, then rotary evaporated to remove water, then added hexaethylene oxide Methyl diisocyanate, 1,3,5-triglycidyl-S-triazinetrione, reflux and stir for 5 minutes, then add glycerol, stir to obtain a modified system;

[0037] (3) After mixing diethylene glycol, o-hydroxybenzoic acid, and N-methylpyrrolidone, stir at 60°C for 1 hour, then add 2-mercaptop...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a one-component polyurethane adhesive for furniture and a preparation method of the one-component polyurethane adhesive. The preparation method comprises the following steps ofadding a function system in a modification system, adding 4,4-diphenylmethane and maleic anhydride under stirring at 60 DEG C, performing stirring for 35mins, then adding a foundational system, performing stirring for 85mins at the temperature of 110 DEG C, adding ethanol while performing natural cooling to obtain a system with the solid content being 65-70 percent, i.e., the one-component polyurethane adhesive for the furniture. The obtain product can be used in the furniture industry, has excellent peeling strength, fairly excellent flame retardancy and toughness and particularly good antibacterial property.

Description

technical field [0001] The invention belongs to the field of adhesives, and in particular relates to a one-component polyurethane adhesive for furniture and a preparation method thereof. Background technique [0002] With the gradual enhancement of people's awareness of environmental protection and the improvement of national environmental protection laws and regulations, the development of non-toxic, non-polluting, green and environmentally friendly wood adhesives has become an inevitable trend in the development of the industry. Polyurethane adhesives were first industrialized in Germany in the 1940s, mainly including polyisocyanate solvent adhesives, thermoplastic polyurethane solvent adhesives, reactive single- and two-component solvent adhesives, solvent-free, water-dispersed, hot-melt polyurethane adhesives, etc. ; There are many types of synthetic raw materials and additives. Starting from molecular design, a series of adhesives with a wide range of performance can be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/04C09J11/04C09J11/08
CPCC09J11/04C09J11/08C09J175/04C08L91/06C08K3/04
Inventor 朱桂荣肖华明
Owner 昆山市冠宝化学有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com