Water-based coating

A water-based paint and raw material technology, applied in the direction of coating, can solve the problems of poor storage stability and performance to be improved, and achieve the effects of high stability, good viscosity and good scratch resistance

Inactive Publication Date: 2018-06-19
黄建如
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Water-based coatings widely used in the prior art usually use polyurethane dispersions and acrylate emulsions as raw materials, but their performance needs to be improved and their storage stability is poor, which cannot meet people's needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Embodiment 1: A kind of water-based coating is made of the following raw materials in parts by weight: 12 parts of synthetic resin, 3 parts of polystyrene, 9 parts of linseed oil, 8 parts of acrylonitrile, 10 parts of acrylic emulsion, 18 parts of oil, nano-oxidized 7 parts of zinc antibacterial agent, 3 parts of calcium carbonate, 6 parts of curing agent, 2 parts of defoamer, 3 parts of retarder, 4 parts of magnesium chloride, 4 parts of toning pigment, and 1 part of antioxidant.

Embodiment 2

[0012] Embodiment 2: A kind of water-based coating is made of the following raw materials in parts by weight: 14 parts of synthetic resin, 5 parts of polystyrene, 11 parts of linseed oil, 10 parts of acrylonitrile, 13 parts of acrylic emulsion, 20 parts of oil, nano-oxidized 9 parts of zinc antibacterial agent, 5 parts of calcium carbonate, 8 parts of curing agent, 3 parts of defoamer, 5 parts of retarder, 6 parts of magnesium chloride, 5 parts of toning pigment, and 3 parts of antioxidant.

Embodiment 3

[0013] Embodiment 3: A kind of water-based coating is made of the following raw materials in parts by weight: 16 parts of synthetic resin, 7 parts of polystyrene, 13 parts of linseed oil, 12 parts of acrylonitrile, 16 parts of acrylic emulsion, 22 parts of oil, nano-oxidized 11 parts of zinc antibacterial agent, 7 parts of calcium carbonate, 10 parts of curing agent, 4 parts of defoamer, 7 parts of retarder, 8 parts of magnesium chloride, 6 parts of toning pigment, and 5 parts of antioxidant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a water-based coating. The water-based coating is prepared from the following raw materials in parts by weight: 12-16 parts of synthetic resin, 3-7 parts of polystyrene, 9-13 parts of linseed oil, 8-12 parts of acrylonitrile, 10-16 parts of an acrylic emulsion, 18-22 parts of an oil material, 7-11 parts of a nano-zinc oxide antibacterial agent, 3-7 parts of calcium carbonate, 6-10 parts of a curing agent, 2-4 parts of a defoaming agent, 3-7 parts of a retarder, 4-8 parts of magnesium chloride, 4-6 parts of color mixing pigments and 1-5 parts of an antioxidant. The water-based coating is high in stability and good in viscidity, has relatively good scraping resistance, water resistance and weather resistance and is unlikely to fall, uniform in luminosity, environmentally friendly and free from pollution.

Description

technical field [0001] The invention belongs to the field of coatings, in particular to a water-based coating. Background technique [0002] Coatings usually use organic solvents such as formaldehyde and benzene as solvents for film-forming substances, so they contain more volatile organic compounds, which not only cause environmental pollution, but also cause great harm to human health. Water-soluble coatings use water-soluble resins as film-forming materials, represented by polyvinyl alcohol and its various modified products, in addition to water-soluble alkyd resins, water-soluble epoxy resins, and inorganic polymer water-based resins. Water-based coatings widely used in the prior art usually use polyurethane dispersions and acrylate emulsions as raw materials, but their performance needs to be improved and their storage stability is poor, which cannot meet people's needs. Contents of the invention [0003] In order to solve the problems of the prior art, the present i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D7/61
CPCC09D4/06
Inventor 黄建如
Owner 黄建如
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com