A preparation method and application of a carbon-wrapped porous cobaltous oxide nanomaterial with a shell-core structure

A technology of cobaltous oxide nanometer and cobalt trioxide nanometer, which is applied in the preparation and application field of carbon-wrapped porous cobaltous oxide nanomaterial with shell-core structure, to achieve the effect of improving the transmission path, simple preparation process and improving rate performance

Active Publication Date: 2021-06-04
ZHENGZHOU UNIV
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are few reports on carbon-wrapped porous cobaltous oxide nanocube three-dimensional materials with a shell-core structure, so it has practical significance and application value for the research and development of this material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method and application of a carbon-wrapped porous cobaltous oxide nanomaterial with a shell-core structure
  • A preparation method and application of a carbon-wrapped porous cobaltous oxide nanomaterial with a shell-core structure
  • A preparation method and application of a carbon-wrapped porous cobaltous oxide nanomaterial with a shell-core structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] In this embodiment, the preparation steps of carbon-wrapped porous cobaltous oxide nanomaterials with a shell-core structure are as follows:

[0032] The first step, preparation of cobalt trioxide nanocubes

[0033] The hydrothermal method (also known as the hydrothermal method) was used to prepare cobalt tetroxide, and 0.04 mol of cobalt nitrate hexahydrate was dispersed in 40 mL of deionized water, and stirred until transparent under magnetic stirring; then 0.01 mol of sodium hydroxide was added to the above solution to continue Stir until a clear solution is obtained; transfer the above solution to a 50 mL polytetrafluoroethylene reactor, and place it in an oven at 180 °C for 24 h; after the reaction, the reactor is naturally cooled to room temperature, and the obtained sample is centrifuged Separated, washed three times by centrifugation with water / ethanol mixed solution, and dried at 65°C for 12 h;

[0034] The second step, preparation of PDA (polydopamine)-wrappe...

Embodiment 2

[0040] Same as Example 1, the difference is,

[0041] The fourth step, preparation of porous carbon-coated cobaltous oxide etched by hydrochloric acid

[0042] The product prepared in the third step was dispersed in a hydrochloric acid solution with a concentration of 0.1 mol / L and etched for 3 minutes, then soaked in deionized water / ethanol to remove soluble impurities, and the obtained material was vacuum-dried at 65°C after centrifugation , and a carbon-wrapped porous cobaltous oxide nanocube three-dimensional material with a shell-core structure was prepared.

[0043] The transmission electron microscope image of the carbon-wrapped porous cobaltous oxide nanocube three-dimensional material etched by hydrochloric acid in this embodiment is as follows Figure 4 shown.

Embodiment 3

[0045] Same as Example 1, the difference is,

[0046] The fourth step, preparation of porous carbon-coated cobaltous oxide etched by hydrochloric acid

[0047] The product prepared in the third step was dispersed in a hydrochloric acid solution with a concentration of 0.1 mol / L and etched for 6 min, then soaked in deionized water / ethanol to remove soluble impurities, and the obtained material was vacuum-dried at 65°C after centrifugation , and a carbon-wrapped porous cobaltous oxide nanocube three-dimensional material with a shell-core structure was prepared.

[0048] The transmission electron microscope image of the carbon-wrapped porous cobaltous oxide nanocube three-dimensional material etched by hydrochloric acid in this embodiment is as follows Figure 5 shown.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a simple method for preparing a carbon-wrapped porous cobaltous oxide nanomaterial with a shell-core structure and its electrochemical performance as an anode of a lithium ion battery. The specific preparation steps include: preparing solid cobalt trioxide nano Cube: After the surface of the prepared nanocube is wrapped with PDA, the carbon-wrapped porous cobaltous oxide shell-core nanomaterial is obtained by medium-high temperature calcination, and finally the shell-core structure carbon-wrapped porous cobaltous oxide nanomaterial is formed by hydrochloric acid etching. The method of the present invention does not add any directing agent and surfactant to participate, the whole synthesis process has mild conditions, environmental protection, cheap raw materials, low requirements on equipment, and is convenient for industrial production. It has great advantages in the preparation of anode materials for lithium ion batteries. Great application prospects.

Description

technical field [0001] The invention relates to a synthesis method for preparing a carbon-wrapped porous cobaltous oxide nanomaterial with a shell-core structure and its application in a power lithium ion battery anode. Background technique [0002] With the continuous development of technology and the gradual change of people's lifestyle, lithium-ion batteries are becoming more and more prominent in life, and people's demand for electrode materials with high rate performance is becoming more and more urgent. As a negative electrode material for lithium-ion batteries, the theoretical specific capacity of cobaltous oxide is as high as 715mAh g -1 , is about 2 times that of graphitized carbon. However, the first coulombic efficiency and cycle performance of cobaltous oxide are poor. In order to overcome these shortcomings, the structural design of cobaltous oxide is particularly important. For example, Chinese patent document CN 103950994 B adopts organic metal cobalt salt a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/52H01M4/62H01M10/0525B82Y40/00
CPCB82Y40/00H01M4/362H01M4/523H01M4/62H01M4/628H01M10/0525Y02E60/10
Inventor 李丹苏行董玉涛马宇航张建民
Owner ZHENGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com