Tempering method of mineral wool produced from silicon manganese slag

A silicon-manganese slag, quenching and tempering technology, applied in glass manufacturing equipment, manufacturing tools and other directions, can solve the problems of environmental protection pressure of silicon-manganese production, high slag viscosity, affecting mineral wool production and filament quality, etc. good use effect

Inactive Publication Date: 2018-06-05
NINGXIA JIYUAN JUNTAI NEW MATERIAL TECH CO LTD
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the high-temperature thermal slag conditioning process, it is difficult for the slag to mix with the conditioning agent and reduce the temperature, resulting in high viscosity of the slag, and it is difficult to form the silicate system required for silk, which seriously affects the production of mineral wool and the quality of silk, and restricts The utilization of silicomanganese slag has resulted in the environmental protection pressure of silicomanganese production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The hot molten slag produced by smelting silicon-manganese alloys is directly poured into the heating furnace for heating and heat preservation, and the heat preservation temperature is 1400°C; and the conditioning agent is added to mix evenly for conditioning; the conditioning agent is dolomite, silicon particles 1. One or more types of fly ash, the amount of the conditioning agent added accounts for 10% of the weight of the slag, the fused slag after conditioning meets the requirements of cotton, and the hot slag after conditioning is blown into slag wool According to the test, the diameter of the blown slag wool fiber is 5um, the content of slag balls is less than 8%, the thermal conductivity at room temperature is 0.04w / m k, and the density is 140kg / m³, reaching the requirements of "Rock Wool, Slag Wool and Their Products for Thermal Insulation" GB / T11835- 2007 performance requirements.

Embodiment 2

[0019] The hot molten slag produced by smelting silicon-manganese alloys is directly poured into the heating furnace for heating and heat preservation, and the heat preservation temperature is 1400°C; and the conditioning agent is added to mix evenly for conditioning; the conditioning agent is dolomite, silicon particles 1. One or more types of fly ash, the amount of the conditioning agent added accounts for 20% of the weight of the slag, the fused slag after quenching and tempering meets the requirement of forming cotton, and the hot slag after conditioning is blown into slag wool, According to the test, the diameter of the blown slag wool fiber is 5um, the content of slag balls is less than 8%, the thermal conductivity at room temperature is 0.04w / mk, and the density is 140kg / m³, which meets the requirements of GB / T11835-2007 of "Rock Wool, Slag Wool and Their Products for Thermal Insulation". performance requirements.

Embodiment 3

[0021] The hot molten slag produced by smelting silicon-manganese alloys is directly poured into the heating furnace for heating and heat preservation, and the heat preservation temperature is 1400°C; and the conditioning agent is added to mix evenly for conditioning; the conditioning agent is dolomite, silicon particles 1. One or more types of fly ash, the amount of conditioning agent added accounts for 30% of the weight of the slag, the fused slag after quenching and tempering meets the requirements of cotton, and the hot slag after conditioning is blown into slag wool According to the test, the diameter of the blown slag wool fiber is 5um, the content of slag balls is less than 8%, the thermal conductivity at room temperature is 0.04w / m k, and the density is 140kg / m³, reaching the requirements of "Rock Wool, Slag Wool and Their Products for Thermal Insulation" GB / T11835- 2007 performance requirements.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a tempering method of mineral wool produced from silicon manganese slag and relates to a tempering method of high-temperature hot-molten slag during the production of building mineral wool from metallurgy furnace slag. According to the tempering process, molten silicon manganese slag produced during the production of silicon-manganese alloy through mine heating method is directly poured into a heating furnace and is heated and subjected to heat preservation, and a tempering agent is added and is uniformly mixed with the molten silicon manganese slag for tempering. According to the tempering method, the molten slag is poured into an electrode of a heat preservation furnace so as to generate fluidity, so that adequate mixing with the added tempering agent is accelerated, and a silicate system is rapidly formed; and the molten slag with proper melt temperature and viscosity and with components meeting wool slag blowing requirements is obtained through the heating ofthe heat preservation furnace, so that the problem that molten slag is difficult to be mixed with the tempering agent so as to be cooled is solved, the performance standard of the mineral wool is satisfied, the mineral resources are saved, and the industrial waste slag is well utilized.

Description

technical field [0001] The invention relates to a tempering method for producing mineral wool from silicomanganese slag, which relates to a high-temperature thermal slag conditioning method in the process of producing mineral wool for construction by using metallurgical slag. Background technique [0002] Mineral wool and rock wool belong to the same type of thermal insulation materials. Compared with other inorganic fiber thermal insulation materials, rock wool has a wide range of applications and has developed into an important thermal insulation material for construction. [0003] Mineral wool is made of blast furnace, ferronickel, silicomanganese and other industrial waste slag as raw materials, and the molten slag is made of silky inorganic fibers by high-speed centrifugal blowing and other processes to make mineral wool. Compared with rock wool, which is widely used at present, mineral wool still has a big gap with rock wool in terms of acidity coefficient, water resis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03B37/00C03C13/06
CPCC03B37/00C03C13/06
Inventor 周占红莫军红杨浩曹国峰
Owner NINGXIA JIYUAN JUNTAI NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com