Impregnating resin for filter paper of engine oil filter element device

A technology of impregnating resin and engine oil filter, which is applied in the field of impregnating resin for filter paper of engine oil filter, which can solve the problems of large amount of solvent and difficulty in solvent recovery, etc., and achieve the improvement of tensile strength and oil resistance retention rate, excellent filtration performance, and fracture work retention rate Improved effect

Inactive Publication Date: 2018-06-01
安徽新立滤清器有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has been more than half a century since the first batch of oil filter paper was produced in the United States. Since the first batch of products, alcohol-soluble phenolic resin has been used as the impregnated resin for reinforcing filter paper. Alcohol-soluble phenolic resin has a large amount of solvent and potential danger during use. , Solvent recovery difficulties and other problems, based on these reasons, domestic and foreign are constantly committed to research and development of new impregnating resin systems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] An impregnated resin for filter paper of an oil filter element, made of the following components in parts by weight: 95% water-soluble phenolic resin, 5.2% dimethylol propionic acid, 0.2% modified nano-silica, 3% epoxy resin, and fumaric acid Dimethyl ester 1, dimethyl itaconate 0.3, modified sodium lignosulfonate 1.5, plasticizer 0.3;

[0019] The preparation method of the modified nano-silica is as follows: uniformly disperse the nano-silica in deionized water, prepare a nano-silica suspension with a mass fraction of 12%, and add its mass fraction to the nano-silica suspension. 0.5% dimethylolpropionic acid, stirred at 500r / min for 40min, then added sodium hydroxide, adjusted the pH of the nano-silica suspension to 8.5, kept it at 90°C for 2 hours, and then filtered it. Wash with deionized water until neutral, and dry to constant weight.

[0020] Further, the preparation method of the modified sodium lignosulfonate is:

[0021] (1) Mix sodium lignosulfonate and deio...

Embodiment 2

[0030] An impregnated resin for oil filter paper, made of the following components in parts by weight: water-soluble phenolic resin 100, dimethylol propionic acid 5.5, modified nano silicon dioxide 0.6, epoxy resin 5, fumaric acid Dimethyl ester 3, dimethyl itaconate 0.6, modified sodium lignosulfonate 2.0, plasticizer 0.8;

[0031] The preparation method of the modified nano-silica is as follows: uniformly disperse the nano-silica in deionized water, prepare a nano-silica suspension with a mass fraction of 12%, and add its mass fraction to the nano-silica suspension. 0.5% dimethylolpropionic acid, stirred at 500r / min for 40min, then added sodium hydroxide, adjusted the pH of the nano-silica suspension to 8.5, kept it at 90°C for 2 hours, and then filtered it. Wash with deionized water until neutral, and dry to constant weight.

[0032] Further, the preparation method of the modified sodium lignosulfonate is:

[0033] (1) Mix sodium lignosulfonate and deionized water uniform...

Embodiment 3

[0042] An impregnated resin for oil filter filter paper, made of the following components in parts by weight: water-soluble phenolic resin 98, dimethylol propionic acid 5.3, modified nano silicon dioxide 0.4, epoxy resin 4, fumaric acid Dimethyl ester 2, dimethyl itaconate 0.5, modified sodium lignosulfonate 1.8, plasticizer 0.5;

[0043] The preparation method of the modified nano-silica is as follows: uniformly disperse the nano-silica in deionized water, prepare a nano-silica suspension with a mass fraction of 12%, and add its mass fraction to the nano-silica suspension. 0.5% dimethylolpropionic acid, stirred at 500r / min for 40min, then added sodium hydroxide, adjusted the pH of the nano-silica suspension to 8.5, kept it at 90°C for 2 hours, and then filtered it. Wash with deionized water until neutral, and dry to constant weight.

[0044] Further, the preparation method of the modified sodium lignosulfonate is:

[0045] (1) Mix sodium lignosulfonate and deionized water u...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses impregnating resin for filter paper of an engine oil filter element device and relates to the technical field of filter element devices. The impregnating resin is prepared fromthe following components: water-soluble phenolic resin, dihydromethyl propionic acid, modified nano silicon dioxide, epoxy resin, dimethyl fumarate, dimethyl itaconate, modified sodium lignosulphonate and a plasticizer. The filter paper impregnated with the resin can keep good filtering performance; the impregnating resin does not cause a pore-blocking phenomenon on pores of the filter paper.

Description

technical field [0001] The invention belongs to the technical field of filter elements, and in particular relates to an impregnating resin for filter paper of an oil filter element. Background technique [0002] Oil filter paper, also known as lubricating oil filter paper, is used to remove impurities such as dust, metal particles, carbon deposits, and bituminous coal particles in the oil to keep the engine clean and prevent machine wear. In recent years, due to the rapid development of my country's automobile industry, the amount of oil filter paper has gradually expanded. It has been more than half a century since the first batch of oil filter paper was produced in the United States. Since the first batch of products, alcohol-soluble phenolic resin has been used as the impregnated resin for reinforcing filter paper. Alcohol-soluble phenolic resin has a large amount of solvent and potential danger during use. , Solvent recovery difficulties and other issues, based on these...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/08D21H17/20D21H17/14D21H17/68D21H17/05D21H21/14
CPCD21H17/05D21H17/14D21H17/20D21H17/68D21H21/14D21H27/08
Inventor 徐晓玲
Owner 安徽新立滤清器有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products