Synthetic wax candle and preparation method thereof

A technology of synthetic wax and Fischer-Tropsch synthetic wax, which is applied in the field of candles, can solve the problems of not being able to know the properties of candles such as combustibility and stability, and not studying F-T Fischer-Tropsch synthetic wax candles, etc.

Inactive Publication Date: 2018-06-01
QINGDAO KINGKING APPL CHEM CO LTD
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present there is only research on the preparation of pure F-T Fischer-Tropsch synthetic wax, but it has not been studied whether F-T Fischer-Tropsch synthetic wax can replace paraffin to prepare candles, so it is impossible to know the flammability of candles prepared by replacing paraffin with F-T Fischer-Tropsch synthetic wax , stability and other performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Synthetic wax candle and preparation method thereof
  • Synthetic wax candle and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The preparation raw material of the synthetic wax candle that the embodiment of the present invention provides comprises according to parts by weight: F-T Fischer-Tropsch synthetic wax 45%, hydrogenated palm oil 45%, soft wax 3%, essence 5%, oil-locking agent 1% and anti-ultraviolet Additive 1%. Wherein, the melting point of F-T Fischer-Tropsch synthetic wax is 50° C., and the penetration is 18.

[0026] The synthetic wax candle that the embodiment of the present invention provides is cup wax, and the preparation method of this cup wax comprises:

[0027] S101: preheat the membrane with the wick glued to 30°C, and reserve the membrane for later use;

[0028] S102: Mixing and melting the weighed F-T Fischer-Tropsch synthetic wax, hydrogenated palm oil, soft wax, oil locking agent and anti-ultraviolet additive to form mixed wax a;

[0029] S103: add essence to mixed wax a at a temperature of 50°C, and stir evenly to form mixed wax b;

[0030] S104: Inject the mixed wax...

Embodiment 2

[0032] The preparation raw material of the synthetic wax candle that the embodiment of the present invention provides comprises according to parts by weight: F-T Fischer-Tropsch synthetic wax 60%, half-hydrogenated palm oil 30%, soft wax 3%, essence 5%, oil-locking agent 1% and β - Cyclodextrin 1%. Wherein, the melting point of F-T Fischer-Tropsch synthetic wax is 54° C., and the penetration is 15.

[0033] The synthetic wax candle that the embodiment of the present invention provides is cup wax, and the preparation method of this cup wax comprises:

[0034] S201: Preheat the membrane with the wick attached to 60°C, and reserve the membrane for later use;

[0035] S202: Mix and melt the weighed F-T Fischer-Tropsch synthetic wax, semi-hydrogenated palm oil, soft wax, oil-locking agent and β-cyclodextrin to form mixed wax a;

[0036] S203: add dye to mixed wax a at a temperature of 120°C, add essence at 80°C, and stir evenly to form mixed wax b;

[0037] S204: Inject the mixe...

Embodiment 3

[0039] The raw materials for the preparation of the synthetic wax candle provided by the embodiments of the present invention include: F-T Fischer-Tropsch synthetic wax 45%, hydrogenated soybean oil 45%, soft wax 3%, essence 5%, oil-locking agent 1% and anti-ultraviolet additive according to parts by weight 1%. Wherein, the melting point of F-T Fischer-Tropsch synthetic wax is 54° C., and the penetration is 15.

[0040] The synthetic wax candle that the embodiment of the present invention provides is cup wax, and the preparation method of this cup wax comprises:

[0041] S301: preheat the membrane with the wick attached to 35°C, and reserve the membrane for later use;

[0042] S302: Mixing and melting the weighed F-T Fischer-Tropsch synthetic wax, hydrogenated soybean oil, soft wax, oil-locking agent and anti-ultraviolet additive to form mixed wax a;

[0043] S303: add essence to mixed wax a at a temperature of 60°C, and stir evenly to form mixed wax b;

[0044] S304: Injec...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a synthetic wax candle and a preparation method thereof, wherein the synthetic wax candle includes, by weight, 5-80% of Fischer-Tropsch synthesis wax, 11-75% of plant wax, and 4-20% of a candle making additive including an additive, and at least one of soft wax, a dye and an essence. During preparation of the synthetic wax candle, original paraffin is replaced by the Fischer-Tropsch synthesis wax, which is then mixed with the plant wax and the candle making additive in order to produce the candle. The synthetic wax candle has stable performances of appearance, combustionand fragrance, is produced from environment-friendly and pollution-free raw materials, and is free of raw material exhaustion.

Description

technical field [0001] The invention relates to the technical field of candles, in particular to a synthetic wax candle and a preparation method. Background technique [0002] Candle is a kind of common commodity in daily life. According to the purpose of use, candles are divided into two categories: daily lighting candles and handicraft candles. Therefore, candles can be widely used in birthday parties, religious festivals, weddings and funerals, and activities to adjust the atmosphere. [0003] The main raw material for candle preparation is paraffin wax. Among them, paraffin is prepared from the waxy fraction of petroleum by cold pressing or solvent dewaxing, and is a mixture of several higher alkanes. With the continuous extraction of oil, the oil reserves continue to decline, so the output of paraffin wax extracted from the waxy fraction of oil continues to decline, and the paraffin wax is facing depletion. The decline in the production of paraffin wax, especially th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C11C5/00
CPCC11C5/002C11C5/004
Inventor 陈索斌刘小青莫欣欣侯婷婷韩朔
Owner QINGDAO KINGKING APPL CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com