Austenitic stainless steel resistant to high temperature and high-concentration sulfuric acid

A high-concentration austenitic stainless steel technology, applied in the field of austenitic corrosion-resistant steel, can solve the problems of high leakage rate, long manufacturing period, and cracking of steel shells in towers lined with acid-resistant ceramic tiles, and achieve the improvement of comprehensive machinery Improvement of performance and acid resistance, and improvement of yield

Inactive Publication Date: 2018-05-29
YONGXING SPECIAL STAINLESS STEEL
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Years of production practice have shown that this structure has many disadvantages: first, the tower body lined with acid-resistant ceramic tiles has a high leakage rate, and safety accidents such as steel shell expansion and cracking are prone to occur; second, the tower body lined with steel shell bricks is very heavy and the construction is complicated , long manufacturing period, high operation and maintenance costs
For example, foreign companies have successively developed brands such as Zecor (similar to ASTM S38815), Saramet35, and sandvik SX (similar to ASTM S32615), but due to reasons such as processing technology, performance, and cost, they have not been widely used in China.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Austenitic stainless steel resistant to high temperature and high-concentration sulfuric acid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] An austenitic stainless steel resistant to high temperature and high concentration of sulfuric acid, including the following components: Cr 13.3wt%, Ni 15.2wt%, Si 5.9wt%, Cu 0.98wt%, Mo 0.9wt%, C0.014wt%, Mn1.1wt% %, S 0.002wt%, P0.022wt%, Al 0.05wt%, N 0.015wt%, B 0.004wt%, rare earth 0.03wt%, Bi 0.001wt%, As0.002wt%, Pb 0.002wt%, Sn 0.005% , Sb 0.002 wt%, the balance is Fe; and the sum of the five elements of Bi, As, Pb, Sn, Sb <0.05wt%.

Embodiment 2

[0049] An austenitic stainless steel resistant to high temperature and high concentration of sulfuric acid, including the following components: Cr 13.6wt%, Ni 15.7wt%, Si 6.05wt%, Cu 0.95wt%, Mo 1.0wt%, C 0.012wt%, Mn 1.0wt% %, S 0.001wt%, P0.020wt%, Al 0.03wt%, N 0.018wt%, B 0.004wt%, rare earth 0.03wt%, Bi 0.001wt%, As0.002wt%, Pb 0.002wt%, Sn 0.004% , Sb 0.001 wt%, the balance is Fe; and the sum of Bi, As, Pb, Sn, Sb five elements <0.05wt%.

Embodiment 3

[0051] An austenitic stainless steel resistant to high temperature and high concentration of sulfuric acid, including the following components: Cr 17.8wt%, Ni 20.wt%, Si5.4wt%, Cu 0.92wt%, Mo 1.95wt%, C 0.015wt%, Mn 1.1 wt%, S 0.002wt%, P0.022wt%, Al 0.04wt%, N≤0.016wt%, B 0.003wt%, rare earth 0.02wt%, Bi 0.001wt%, As0.002wt%, Pb 0.002wt%, Sn 0.005%, Sb 0.002 wt%, the balance is Fe; and the sum of Bi, As, Pb, Sn, Sb five elements <0.05wt%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an austenitic stainless steel resistant to high temperature and high-concentration sulfuric acid and belongs to the technical field of austenitic stainless steel. The austenitic stainless steel resistant to high temperature and high-concentration sulfuric acid comprises, by weight, 13-19.5% of Cr, 13-22% of Ni, 4.5-6.5% of Si, 0.30-1.5% of Cu, 0.75-2.5% of Mo, 0.07% or less of C, 2% or less of Mn, 0.015% or less of S, 0.03% or less of P, 0.3% or less of Al, inevitable impurities, and the balance Fe. Among steel varieties in the prior art, Zecor, Saramet35 and sandvik SX developed by foreign companies are similar to the austenitic stainless steel on the aspects of material design and overall performance, and compared with the steel of foreign countries, the austenitic stainless steel has more obvious advantages on the aspects of material manufacturing process, yield improvement, corrosion resistance and the like.

Description

technical field [0001] The invention relates to an austenitic corrosion-resistant steel, in particular to an austenitic stainless steel resistant to high temperature and high concentration of sulfuric acid, belonging to the technical field of austenitic stainless steel. Background technique [0002] Sulfuric acid, as an important industrial raw material, is also known as the mother of industry. It can be used to manufacture fertilizers, medicines, explosives, pigments, detergents, batteries, etc. It is also widely used in industries such as purification of petroleum, metal smelting, and dyes. It can be used as a chemical reagent, and can be used as a dehydrating agent and sulfonating agent in organic synthesis. [0003] Drying towers and absorption towers in the sulfuric acid production process are generally made of steel shells lined with acid-resistant tiles. Years of production practice have shown that this structure has many disadvantages: first, the tower body lined wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/42C22C38/44C22C38/58C22C38/04C22C38/06C22C38/54C22C30/02
CPCC22C38/34C21D2211/001C22C30/02C22C38/005C22C38/04C22C38/06C22C38/42C22C38/44C22C38/54C22C38/58
Inventor 王建勇顾晓暾杜雯雯陈根保吴明华慎琪琦张跃良邹伟民
Owner YONGXING SPECIAL STAINLESS STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com