Preparation method of graphene-reinforced aluminum matrix composite

A technology of composite materials and enhanced aluminum base, which is used in the preparation and application of non-ferrous metal composite materials. It can solve the problems of poor wettability, weak interfacial bonding force, and difficulty in uniform distribution, and achieve pure slurry and good metallographic structure. , No shrinkage effect

Active Publication Date: 2018-05-22
ZHONGBEI UNIV
View PDF6 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Graphene has excellent mechanical properties, thermal properties and electrical properties, and is one of the most ideal reinforcements for the preparation of metal matrix nanocomposites. The addition of graphene to prepare graphene-reinforced aluminum matrix composites can improve the aluminum matrix composites. Comprehensive performance, thereby expanding the application range of aluminum alloy; it can not only expand the application range of graphene, but also create favorable conditions for the industrial production of aluminum matrix composite materials; but the wettability of graphene and aluminum and its alloys is poor, and the interface binding force is weak , it is difficult to distribute uniformly in the aluminum matrix, which is a difficult problem in the preparation technology of graphene-reinforced aluminum matrix composites
[0003] How to uniformly disperse graphene into the aluminum alloy metal matrix, and at the same time form a good contact interface between graphene and metal without destroying the microstructure of graphene has become a technical problem. Currently, graphene is used as a reinforcing phase to prepare aluminum substrates Composite materials are still in the research stage, and their technology needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of graphene-reinforced aluminum matrix composite
  • Preparation method of graphene-reinforced aluminum matrix composite
  • Preparation method of graphene-reinforced aluminum matrix composite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0055] The present invention will be further described below in conjunction with accompanying drawing:

[0056] figure 1 As shown, it is the smelting state diagram of the graphene aluminum alloy semi-solid slurry, the position and connection relationship of each part must be correct, the ratio should be proportioned, and the operations should be performed in sequence.

[0057] Quantities of chemicals used to prepare smelts are determined in pre-set ranges in grams, milliliters, centimeters3 is the unit of measurement.

[0058] The smelting of graphene aluminum alloy semi-solid slurry is carried out in a smelting and stirring atmosphere furnace, which is completed in the process of heating, smelting, heat preservation and standing, cooling solid liquid, adding graphene aluminum alloy mixed fine powder, and electromagnetic stirring;

[0059] The smelting stirred atmosphere furnace 1 is vertical, the inside of the smelting stirred atmosphere furnace 1 is a furnace chamber 2, and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a graphene-reinforced aluminum matrix composite. Aiming at the conditions that graphene is nonuniformly dispersed in an aluminum alloy matrix and is difficult to combine with the matrix, the preparation method adopts a semi-solid squeeze casting method, and comprises the steps of smelting in a smelting and stirring atmosphere oven, electromagnetically stirring, pouring, and conducting squeeze casting to obtain the graphene-reinforced aluminum matrix composite. The preparation method is advanced in process, accurate and detailed in data, and precise in process; a slurry is pure; a metallographic structure is good in compactness without the phenomenon of shrinkage porosity; the prepared graphene-reinforced aluminum matrix composite has the hardness reaching to 87 HB, the tensile strength reaching to 255 MPa, the elongation reaching to 8%, and the compactness reaching to 99.6%; and the preparation method is the advanced preparation method of the graphene-reinforced aluminum matrix composite.

Description

technical field [0001] The invention relates to a method for preparing a graphene-reinforced aluminum-based composite material, which belongs to the technical field of preparation and application of non-ferrous metal composite materials. Background technique [0002] Graphene has excellent mechanical properties, thermal properties and electrical properties, and is one of the most ideal reinforcements for the preparation of metal matrix nanocomposites. The addition of graphene to prepare graphene-reinforced aluminum matrix composites can improve the aluminum matrix composites. Comprehensive performance, thereby expanding the application range of aluminum alloy; it can not only expand the application range of graphene, but also create favorable conditions for the industrial production of aluminum matrix composite materials; but the wettability of graphene and aluminum and its alloys is poor, and the interface binding force is weak , it is difficult to distribute uniformly in t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/10C22C21/00C22C1/02B22D17/00
CPCC22C1/1036C22C21/00C22C32/0084B22D17/007C22C1/1073
Inventor 赵宇宏张婷梁建权陈利文侯华李沐奚
Owner ZHONGBEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com