PE-ABS (polyethylene-acrylonitrile-butadiene-styrene) alloy and preparation method thereof

A technology of PE-ABS and ABS resin, applied in the field of PE-ABS alloy and its preparation, can solve the problems of low strength and poor wear resistance, and achieve the effects of low processing cost, excellent comprehensive performance and prolonged service time

Inactive Publication Date: 2018-05-18
四川锦泰佳环保建材有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to overcome the deficiencies of the prior art, provide a PE-ABS alloy and its preparation method, and solve the problems of low strength and poor wear resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PE-ABS (polyethylene-acrylonitrile-butadiene-styrene) alloy and preparation method thereof
  • PE-ABS (polyethylene-acrylonitrile-butadiene-styrene) alloy and preparation method thereof
  • PE-ABS (polyethylene-acrylonitrile-butadiene-styrene) alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0038] The technical solution of the present invention will be further described in detail below in conjunction with specific examples, but the protection scope of the present invention is not limited to the following description.

[0039] A PE-ABS alloy consisting of the following components:

[0040]

[0041] Specifically, it consists of the following components:

[0042]

[0043] Specifically, the compatibilizer is styrene-acrylonitrile-glycidyl methacrylate, ethylene-glycidyl ester, ethylene-propylene n-butyl ester-glycidyl ester and / or maleic anhydride grafted acrylonitrile- at least one of butadiene-styrene copolymers.

[0044] Specifically, the toughening agent is polyolefin.

[0045] Specifically, the lubricant is at least one of magnesium stearate, calcium stearate and / or polysiloxane.

[0046] Specifically, the antioxidant is at least one of 2-hydroxy-4-n-octyloxybenzophenone, sodium ethylparaben, sodium D-isoascorbate and / or ascorbyl palmitate.

[0047] Sp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a PE-ABS (polyethylene-acrylonitrile-butadiene-styrene) alloy and a preparation method thereof. The alloy comprises, by weight, 35-40 parts of resin, 55-60 parts of ABS resin,3-5 parts of compatilizers, 4-6 parts of flexibilizers, 2-3 parts of lubricants, 2-3 parts of antioxidants, 5-8 parts of fillers, 2-3 parts of quick-drying agents and 3-4 parts of plasticizers. The alloy has the advantages of low cost, high strength and good wear resistance.

Description

technical field [0001] The invention relates to the technical field of organic polymers, in particular to a PE-ABS alloy and a preparation method thereof. Background technique [0002] A polymer is a compound that is repeatedly linked by one or several structural units (103-105). They are composed of few elements, mainly carbon, hydrogen, oxygen, nitrogen, etc., but the relative molecular mass is very large, generally above 10,000, and can be as high as several million. That's why it's called a polymer compound. [0003] The basic structural characteristics of high molecular compounds make them have many valuable properties different from low molecular compounds. For example, high mechanical strength, high elasticity, strong plasticity, high hardness, wear resistance, heat resistance, corrosion resistance, solvent resistance, strong electrical insulation, good air tightness, etc., make polymer materials have a very wide range of uses. Commonly used polymer materials are o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L23/06C08L23/08C08L25/14C08L23/20C08K13/02C08K5/098C08K5/132C08K3/34C08K3/22C08K5/09
CPCC08L55/02C08K2003/222C08L2201/02C08L2201/08C08L2205/025C08L2205/035C08L2205/08C08L23/06C08L23/0869C08L23/20C08K13/02C08K5/098C08K5/132C08K3/34C08K3/346C08K3/22C08K5/09
Inventor 邓利民
Owner 四川锦泰佳环保建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com