High-temperature-resistance industrial canvas impregnation composition

An industrial, high-temperature-resistant technology, applied in wear-resistant fibers, textiles, papermaking, fiber processing, etc., to achieve good high-temperature aging performance, improved performance, and long service life

Inactive Publication Date: 2018-05-08
WUHU HUAYE NEW MATERIALS
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing dipping solution needs to be improved urgently in improving the heat resistance, corrosion resistance and pressure resistance of the weaving fibers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A high-temperature-resistant industrial canvas dipping formula, including a first bath formula and a second bath formula, the first bath formula includes blocked isocyanate, epoxy compound, and soft water, and the weight parts of blocked isocyanate, epoxy compound, and soft water are respectively 6-15 parts, 1.5-5.5 parts, 92.5-140.5 parts; the second bath formula includes sodium hydroxide solution, formaldehyde, resorcinol, latex, deionized water, the sodium hydroxide solution, formaldehyde, The parts by weight of resorcinol, latex and deionized water are respectively 0.3-4.5 parts, 16.2-26.8 parts, 11-22 parts, 50-150 parts and 180-280 parts.

[0016] The concentration of blocked isocyanate is 25%, the concentration of sodium hydroxide solution is 10%, and the concentration of formaldehyde solution is 37%.

Embodiment 2

[0018] A high-temperature-resistant industrial canvas dipping formula, including a first bath formula and a second bath formula, the first bath formula includes blocked isocyanate, epoxy compound, and soft water, and the weight parts of blocked isocyanate, epoxy compound, and soft water are respectively It is 15 parts, 5.5 parts, 140.5 parts; the second bath formula includes sodium hydroxide solution, formaldehyde, resorcinol, latex, deionized water, and the sodium hydroxide solution, formaldehyde, resorcinol, latex , The weight parts of deionized water are respectively 4.5 parts, 26.8 parts, 22 parts, 150 parts, 280 parts.

[0019] The concentration of blocked isocyanate is 25%, the concentration of sodium hydroxide solution is 10%, and the concentration of formaldehyde solution is 37%.

Embodiment 3

[0021] A high-temperature-resistant industrial canvas dipping formula, including a first bath formula and a second bath formula, the first bath formula includes blocked isocyanate, epoxy compound, and soft water, and the weight parts of blocked isocyanate, epoxy compound, and soft water are respectively It is 6 parts, 1.5 parts, 92.5 parts; the second bath formula includes sodium hydroxide solution, formaldehyde, resorcinol, latex, deionized water, and the sodium hydroxide solution, formaldehyde, resorcinol, latex , The parts by weight of deionized water are 0.3 parts, 16.2 parts, 11 parts, 50 parts, 180 parts respectively.

[0022] The concentration of blocked isocyanate is 25%, the concentration of sodium hydroxide solution is 10%, and the concentration of formaldehyde solution is 37%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high-temperature-resistance industrial canvas impregnation composition. The high-temperature-resistance industrial canvas impregnation composition id characterized by comprising a first bath composition and a second bath composition, and the first bath composition is prepared from, by weight, 6-15 parts of blocked isocyanate, 1.5-5.5 parts of an epoxy compound and 92.5-140.5 parts of soft water; the second bath composition is prepared from, by weight, 0.3-4.5 parts of a sodium hydroxide solution, 16.2-26.8 parts of formaldehyde, 11-22 parts of resorcinol, 50-150 partsof latex and 180-280 parts of deionized water. The high-temperature-resistance industrial canvas impregnation composition has the advantages of being resistant to high temperature, acid and alkali andhighly resistant to wear and improves the performance of impregnation liquid.

Description

technical field [0001] The invention relates to a dipping solution formula, in particular to a dipping formula for high-temperature-resistant industrial canvas, which belongs to the technical field of industrial cloth. Background technique [0002] Glue dipping means that the fabric passes through the glue dipping tank, so that the fabric fibers are soaked in the glue, so as to improve the bonding force between the fabric and the glue. Dipping can make the surface of rayon, synthetic fiber and glass fiber cord smooth. After dipping, it can significantly improve the adhesion of rubber and fiber. The commonly used immersion solution is an aqueous emulsion of natural latex and resorcinol formaldehyde resin. The glue service equipment includes a stain tank, a drying room, a hot sheet and a coiling device, which can also be connected with a calender to form a joint production line of dipping, glue application and glue wiping. The dipping solution can improve the private adhesio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/693D06M13/127D06M13/152D06M13/395
CPCD06M13/127D06M13/152D06M13/395D06M15/693D06M2200/35
Inventor 童志海
Owner WUHU HUAYE NEW MATERIALS
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com