Anode sizing agent, anode pole piece and lithium ion battery

A technology of positive electrode slurry and positive active material, which is applied in the direction of battery electrodes, secondary batteries, circuits, etc., can solve the problems of increasing the cost of lithium-ion batteries, poor lithium surface structure in the bulk phase, and failure to achieve performance, and achieve improved storage Life and high-temperature cycle stability, easy industrialization, and the effect of improving production efficiency

Active Publication Date: 2018-04-24
NINGDE AMPEREX TECH
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Such as increasing the sintering temperature or increasing the atmosphere purge, but this will lead to particle size increase or too much Li volatilization, resulting in insufficient lithium content in the positive electrode active material, and ultimately fail to achieve the designed performance
[0005] In addition, for NCM and NCA materials with high alkalinity (that is, high pH value), water washing or pickling is often used to reduce the pH of the surface, but water or acid is a strong polar substance, on the one hand, it will cause the positive active material The dissolution of certain ions on the surface, such as Li, Ni, Co, Mn, etc., will destroy the surface structure of the positive electrode active material. On the other hand, a small amount of residual water molecules will diffuse into the interior of the particle, which is not easy to remove. To completely eliminate it, it is necessary to Sintering at high temperature again will lead to the precipitation of a part of Li, forming a small amount of Li on the surface. 2 CO 3 and other substances, leading to lithium depletion in the bulk phase and changes in the surface structure
The second method is to strictly control the water content of each auxiliary material to the ppm level during stirring, and place the slurry at a lower ambient humidity, but this method is costly, and will greatly increase lithium in the absence of large-scale production capacity. The cost of ion batteries
The third method is to add cyclic ketones to improve the gel degree of the slurry during the stirring process. Adding cyclic ketones has the least impact on the performance of lithium-ion batteries, but cyclic ketones are highly carcinogenic and relatively Strong volatility will affect the safety of operators, so it has been gradually abandoned

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anode sizing agent, anode pole piece and lithium ion battery
  • Anode sizing agent, anode pole piece and lithium ion battery
  • Anode sizing agent, anode pole piece and lithium ion battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] The positive electrode active material is lithium nickel cobalt aluminate Li 1.05 Ni 0.80 co 0.15 al 0.05 o 2 (commercialized NCA product, D50=12 μm, pH=11.95), conductive agent is acetylene black (SP) and carbon nanotube (CNT), and bonding agent is polyvinylidene fluoride (PVDF), and the weight ratio of each component is NCA:SP:CNT:PVDF=96:1.5:0.5:2, additive is compound 1, and the quality of additive is 0.3% of the quality of NCA, and solvent is N-methylpyrrolidone (NMP), and solid content is in positive electrode slurry 60%.

[0053] The specific operation is as follows: mix SP and PVDF dry powder, and dry-mix for 10 minutes with the stirring parameters of revolution 20rpm and rotation 1000rpm; add CNT pre-dispersion (solid content is 20%) and 40% volume of NMP, and stir for 10 minutes; add NCA, Pre-kneading and stirring for 90 minutes with 25 rpm of revolution and 2000 rpm of rotation; add the remaining 60% volume of NMP and compound 1, and stir for 30 minutes;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an anode sizing agent, an anode pole piece and a lithium ion battery. The anode sizing agent comprises an anode active material, a conductive agent and a binding agent; the anode active material comprises a first anode active material grain of which pH value is not less than 11.5. The binding agent comprises fluorine-containing polymer. The anode sizing agent further comprises additive. The anode sizing agent has good mobility and stability, and can effectively solve the gel, jelly, and agglomeration problems during the processing of the anode pole piece, improving the production efficiency, ensuring the consistence of the lithium ion battery while improving the storage life and high-temperature circulatory stability of the lithium ion battery under the high voltage.

Description

technical field [0001] The invention relates to the technical field of batteries, in particular to a positive electrode slurry, a positive electrode sheet and a lithium ion battery. Background technique [0002] Compared with other traditional secondary batteries, lithium-ion batteries have many advantages such as small size, high voltage, and high energy density, and have made a series of great progress in the fields of consumer electronics such as mobile phones and notebooks. With the vigorous development of the new energy industry, more and more researchers are actively developing lithium-ion batteries with high power density, high cycle stability, and high safety, hoping to use them as power batteries for electric vehicles. Among the many positive electrode active materials used in lithium-ion batteries, layered lithium nickel cobalt manganese (NCM) and lithium nickel cobalt aluminum (NCA) are considered to be the future driving forces due to their high discharge capacit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/36H01M4/505H01M4/525H01M4/58H01M4/62H01M4/131H01M4/136H01M10/0525
CPCH01M4/131H01M4/136H01M4/364H01M4/505H01M4/525H01M4/58H01M4/62H01M4/623H01M4/625H01M10/0525Y02E60/10
Inventor 郎野徐中领高旭光徐磊敏
Owner NINGDE AMPEREX TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products