Environment-friendly polypropylene material with continuous fragrance and preparation method of environment-friendly polypropylene material

A polypropylene material, environmentally friendly technology, applied in the polymer field, to achieve the effect of simplifying the process flow

Inactive Publication Date: 2018-04-24
遂宁市明川零贰零科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the existing aromatic plastics are made by in-situ polymerization. Due to the limitation of materials, the materials contain toxic and harmful substances such as formaldehyde and stupid.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Environmentally friendly self-aromatic and continuously volatile polypropylene, which is prepared from the following components by weight:

[0033] 75 parts of random polypropylene,

[0034] 15 parts of modified expanded vermiculite,

[0035] 2 parts of polypropylene grafted maleic anhydride,

[0036] Fragrant masterbatch 10 parts,

[0037] 0.15 parts of silane coupling agent,

[0038] Polyacetamide 0.1 part,

[0039] Antioxidant 1 part,

[0040] Lubricant calcium stearate 0.2 parts,

[0041] Lubricant polyethylene wax 0.3 parts.

[0042] The preparation method of environment-friendly self-fragrance and continuous volatile polypropylene specifically comprises the following steps:

[0043] (1), take the dried expanded vermiculite, and use the ethanol solution of bis(γ-triethoxysilylpropyl)tetrasulfide with a concentration of 0.6% by weight to stir and reflux at a low speed for 30min, and let it stand at room temperature for 12h. Vacuum filtration, placed in an el...

Embodiment 2

[0047] Environmentally friendly self-aromatic and continuously volatile polypropylene, which is prepared from the following components by weight:

[0048] 80 parts of random polypropylene,

[0049] 15 parts of modified expanded vermiculite,

[0050] 2 parts of polypropylene grafted maleic anhydride,

[0051] 3 parts aromatic masterbatch,

[0052] 0.15 parts of silane coupling agent,

[0053] 0.2 parts of polyacetamide,

[0054] Antioxidant 0.2 parts,

[0055] Lubricant calcium stearate 0.2 parts,

[0056] Lubricant polyethylene wax 0.3 parts.

[0057] The preparation method of the environmentally friendly self-aromatic and persistently volatile polypropylene is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of graftingaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly polypropylene material with continuous fragrance and a preparation method of the environment-friendly polypropylene material. The environment-friendly polypropylene material with continuous fragrance is prepared from components in parts by weight as follows: 70-80 parts of polypropylene, 10-15 parts of modified expanded vermiculite, 2.0-3.0 parts ofpolypropylene grafted maleic anhydride, 3-10 parts of fragrant masterbatch, 0.1-0.3 parts of a silane coupling agent, 0.1-0.2 parts of polyacetamide, 0.2-1 part of an antioxidant and 0.5-1 part of a lubricant. The defects that fragrance of the traditional fragrant material cannot last for a long time and essence contains toxins are overcome, the technological flow for foaming and pore opening of aself-fragrant material is simplified, and little influence is produced on material performance. The prepared polypropylene material has the characteristics of environmental protection, continuously emitted self-fragrance and the like, and half-year weight loss ratio of a fragrance in a standard environment is not higher than 5%; the polypropylene material can be widely applied to the fields of home appliance functional materials, automobile decorative materials, children's toys and the like.

Description

technical field [0001] The invention relates to the technical field of polymers, in particular to an environment-friendly polypropylene material with persistent fragrance and a preparation method thereof. Background technique [0002] With the development of the economy, people have higher and higher requirements for environmental protection, safety, comfort, etc., and pay more attention to the ecological environment and the value of life. Most of the existing aromatic plastics are made by in-situ polymerization. Due to the limitation of materials, the materials contain toxic and harmful substances such as formaldehyde and stupid. As people pay more and more attention to health, environment and ecological protection, people's environmental protection standards and environmental standards for materials used are becoming increasingly strict. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a kind of environment-fri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L51/06C08L77/02C08L23/06C08K13/06C08K9/06C08K7/26C08K5/098C08K7/14
CPCC08L23/12C08L2205/035C08L2207/14C08L51/06C08L77/02C08L23/06C08K13/06C08K9/06C08K7/26C08K5/098C08K7/14
Inventor 张成华吴中阳
Owner 遂宁市明川零贰零科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com