Building decoration material with formaldehyde purification function and preparation method of building decoration material

A building decoration material and formaldehyde purification technology, applied in the field of air purification, can solve the problems that cannot be eliminated, achieve the effect of enhancing the ability to remove formaldehyde, improving efficiency, and the preparation process is simple and easy

Active Publication Date: 2018-04-24
秦素洁
View PDF11 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the above-mentioned formaldehyde-removing building materials can only achieve the adsorption of formaldehyde, but cannot achieve the purpose of elimination

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Building decoration material with formaldehyde purification function and preparation method of building decoration material
  • Building decoration material with formaldehyde purification function and preparation method of building decoration material
  • Building decoration material with formaldehyde purification function and preparation method of building decoration material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Example 1: Preparation of gypsum material with formaldehyde purification function.

[0039] 1) Using a ball mill, 2 g of polyvinylpyrrolidone and 1 g of polyethylene glycol were ball milled and mixed at a speed of 300 rpm for 60 minutes to obtain mixture A;

[0040]2) Add 1g of titanium dioxide, 1g of tin dioxide, 1g of silicon dioxide, 2g of magnesium oxide, 1g of activated carbon, 1g of calcium chloride, 1g of sodium carbonate and 4g of 1,2-dimethylaminoethanol to the mixture obtained in step 1) In A, ball mill and mix for 120 minutes at a speed of 300 rpm to obtain mixture B, which is filtered through a 200-mesh filter screen to obtain a formaldehyde scavenger;

[0041] 3) Using a mixer, mix 100g of gypsum powder and 0.5g of modified starch to obtain a mixture C;

[0042] 4) Using mechanical stirring, 1 g of polyvinyl alcohol, 0.6 g of lignocellulose, 65 g of water and 1 g of the formaldehyde scavenger obtained in step 2) were evenly stirred to obtain a mixture D; ...

Embodiment 2

[0044] Example 2: Preparation of putty material with formaldehyde purification function.

[0045] 1) Using a ball mill, 10 g of polyvinylpyrrolidone and 6 g of polyacrylamide were ball milled and mixed at a speed of 800 rpm for 30 minutes to obtain mixture A;

[0046] 2) Add 7g of titanium dioxide, 7g of tin dioxide, 7g of silicon dioxide, 6g of magnesium oxide, 13g of activated carbon, 9g of calcium chloride, 13g of sodium sulfite and 42g of 2,3-dimethylaminopropanol to the mixture obtained in step 1) In A, ball mill and mix for 30 minutes at a speed of 800 rpm to obtain mixture B, which is filtered through a 200-mesh filter screen to obtain a formaldehyde scavenger;

[0047] 3) Using a mixer, mix 100g of putty powder and 1g of modified starch to obtain mixture C;

[0048] 4) Using mechanical stirring, 1.5 g of ethylene acetate, 1 g of lignocellulose, 75 g of water and 20 g of the formaldehyde scavenger obtained in step 2) were evenly stirred to obtain a mixture D;

[0049]...

Embodiment 3

[0050] Example 3: Preparation of clay material with formaldehyde purification function.

[0051] 1) Using a ball mill, 4 g of polyvinylpyrrolidone and 2 g of carboxymethyl cellulose were ball milled and mixed at a speed of 500 rpm for 40 minutes to obtain a mixture A;

[0052] 2) Add 6g of titanium dioxide, 6g of tin dioxide, 5g of silicon dioxide, 3g of magnesium oxide, 3g of activated carbon, 2g of calcium chloride, 3g of sodium bicarbonate and 10g of 1,2-diphenylaminoethanol to the obtained In mixture A, ball mill and mix at a speed of 500 rpm for 80 minutes to obtain mixture B, which is filtered through a 200-mesh filter to obtain a formaldehyde scavenger;

[0053] 3) Using a mixer, mix 100g clay and 0.8g modified starch to obtain mixture C;

[0054] 4) Using mechanical stirring, 1.2g of polyurethane, 0.8g of lignocellulose, 70g of water and 5g of the formaldehyde scavenger obtained in step 2) were evenly stirred to obtain mixture D;

[0055] 5) Add the mixture D obtaine...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of air purification, and relates to a building decoration material with the formaldehyde purification function and a preparation method of the building decoration material. The building decoration material is composed of the following components in parts by weight: 1-20 parts of a formaldehyde scavenger, 100 parts of a base material, 0.5-1 part of modified starch, 1-1.5 parts of a binder, 0.6-1 part of lignocellulose, 0.01-0.1 part of a foaming agent and 65-75 parts of water, wherein the formaldehyde scavenger is composed of the following componentsin parts by weight: 2-10 parts of polyvinylpyrrolidone, 1-6 parts of a water-soluble polymer compound, 4-42 parts of a chiral amino alcohol, 1-7 parts of titanium dioxide, 1-7 parts of tin dioxide, 1-7 parts of silicon dioxide, 2-6 parts of magnesium oxide, 1-13 parts of activated carbon, 1-9 parts of calcium chloride and 1-13 parts of a soluble weak acid salt. The building decoration material provided by the invention can quickly, stably, and highly efficiently purify formaldehyde, and is suitable for large-scale promotion and application.

Description

technical field [0001] The invention belongs to the technical field of air purification, and relates to a building decoration material with formaldehyde purification function and a preparation method thereof. Background technique [0002] Formaldehyde is a protoplasmic toxic substance that can combine with amino groups in proteins to form formylated proteins. The impact of formaldehyde on human health includes abnormal sense of smell, respiratory tract irritation, abnormal lung function, central nervous system impact, abnormal immune function, and damage to genetic material in cells. The harm is serious and cannot be ignored. Therefore, my country's standard stipulates that the concentration of formaldehyde in indoor air should not be greater than 0.08mg / m 3 , and the concentration of formaldehyde in the air of public places shall not exceed 0.12mg / m 3 . [0003] At present, indoor formaldehyde pollution has become the most important indoor air pollution problem in my cou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B38/02C04B24/26C04B24/38C04B28/14C04B26/02C04B28/00B01D53/86B01D53/72
CPCB01D53/8668B01D2255/20707B01D2255/2094B01D2255/30C04B26/02C04B28/001C04B28/14C04B40/0039C04B24/008C04B24/26C04B22/06C04B22/066C04B22/02C04B22/124C04B22/10C04B24/02C04B24/38C04B18/26C04B24/40C04B38/02C04B24/2652C04B22/14C04B14/042C04B24/045C04B24/20C04B24/383C04B24/124C04B24/282
Inventor 秦素洁
Owner 秦素洁
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com