Preparation method of Cu2O nanocrystalline cubes and hollow polyhedrons

A technology of cuprous oxide and cubes, which is applied in the field of preparation of cuprous oxide nanocrystalline cubes and hollow polyhedrons, can solve the problems of unsuitability for industrial production, environmental pollution of products, harsh reaction conditions, etc., and achieve environmental friendliness and high product purity , The effect of low preparation cost

Inactive Publication Date: 2018-04-24
QINGDAO UNIV
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the catalysts prepared by cuprous oxide nanocrystalline cubes and hollow polyhedrons have excellent performance, but the above method is only used for theoretical research in experimental preparation, the reaction conditions are harsh, and the product pollutes the environment, so it is not suitable for industrial production. Therefore, industrial synthesis forms Cuprous oxide with controllable appearance size is still a research hotspot in this field

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of Cu2O nanocrystalline cubes and hollow polyhedrons
  • Preparation method of Cu2O nanocrystalline cubes and hollow polyhedrons
  • Preparation method of Cu2O nanocrystalline cubes and hollow polyhedrons

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0019] The preparation method of the cuprous oxide nanocrystal cube and the hollow polyhedron involved in the present embodiment is: firstly adopt copper acetate monohydrate (Cu(CH 3 COO) 2 ·H 2 O) and sodium hydroxide (NaOH) react first, then with sodium lauryl sulfate (C 12 h 25 SO 4Na) is a surfactant and a stabilizer, and then deionized water and hydrazine hydrate (N 2 h 4 ·H 2 (2) aqueous solution makes cuprous oxide nanocrystal cube and hollow polyhedron, and its specific technological process comprises the following steps:

[0020] (1) Dissolution: first weigh two portions of 0.87g sodium lauryl sulfate, dissolve them in 89ml and 69mL of deionized water solvent respectively, and stir until they are evenly dissolved;

[0021] (2) Add copper acetate: then add 5ml 0.1mol / L Cu(CH 3 COO) 2 Aqueous solution, stir vigorously until dissolved evenly;

[0022] (3) Add NaOH: Then keep the temperature of the water bath at 34°C, add 2ml of NaOH aqueous solution to the solu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of preparation of transition metal oxides and relates to a preparation method of Cu2O nanocrystalline cubes and hollow polyhedrons to be applied to preparation occasions of catalytic materials, antifouling paint, insecticides as well as various copper salts, analytical reagents, red glass, copper plating and copper plating alloy solutions. The problem about industrial preparation of Cu2O nanocrystalline cubes and hollow polyhedrons is solved, and synthesized nanocrystals have good photocatalytic performance, can quickly adsorb azo dyes, are easy toseparate and have a good detection effect on nitrobenzene in a Na2SO4 solution. Firstly, copper acetate monohydrate and sodium hydroxide are subjected to a reaction, sodium dodecyl sulfate is used asa surfactant and a stabilizer, deionized water and a hydrazine hydrate aqueous solution in different volume ratios are added, and the Cu2O nanocrystalline cubes and hollow polyhedrons are prepared. The preparation technology is simple, the principle is reliable, the preparation cost is low, and products are high in purity, good in performance, wide in application range and environmentally friendlyin use.

Description

Technical field: [0001] The invention belongs to the technical field of transition metal oxide preparation, and relates to a method for synthesizing hollow and solid nanocrystals with different shapes by using a water bath method, especially a method for preparing cuprous oxide nanocrystal cubes and hollow polyhedrons, which are used in catalysts , photocatalytic materials, electrocatalytic materials, manufacturing ship bottom antifouling paint, insecticides, and various copper salts, analytical reagents, red glass, and also used in the preparation of copper plating and copper alloy plating solutions. Background technique: [0002] Cuprous oxide is an important new inorganic chemical raw material, widely used in marine antifouling, photoelectric conversion, catalytic degradation, sensors and other fields, because the physical and chemical properties of cuprous oxide depend to a large extent on its crystal size and Therefore, the synthesis of cuprous oxide with controllable m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01G3/02B01J23/72
CPCB01J23/72C01G3/02C01P2002/72C01P2004/03C01P2004/04
Inventor 郭培志柳水波苑亚楠赵修松
Owner QINGDAO UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com