Indoor lightless flat sand-textured powder coating having skin tactility and specially used for IT products

A technology of powder coating and smooth surface, which is applied in the direction of powder coating, polyester coating, epoxy resin coating, etc. It can solve the problems of poor surface scratch resistance, poor human body fit, cold surface touch, etc., and achieve strong decoration , comfort and softness tight, the surface feels warm and soft to the touch

Active Publication Date: 2018-04-20
广东华彩粉末科技有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, most of the appearance of sand grains on the market is obtained by adding sand grain agents, and most of the common indoor matt flat powder coatings are obtained by adding chemical matting agent XG603-1A, which do not show sand grains. Moreover, the scratch resistance of the surface is poor, which may cause irreversible damage to the product during packaging and transportation, and the surface feels relatively "cold", and the fit with the human body is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A kind of IT product special-purpose indoor matte plane sand texture skin touch powder coating formula is as follows:

[0048] Carboxylated polyester resin 14%

[0049] Epoxy 40%

[0050] Acrylic Matting Agent 17%

[0051] Leveling agent 1.0%

[0052] Benzoin 0.4%

[0053] Brightener 0.8%

[0054] Special toughener 0.8%

[0055] Wear-resistant wax 0.8%

[0056] Catalyst 0.01%

[0057] Calcium Carbonate 10%

[0058] Dull barium 14.39%

[0059] Carbon black 0.8%.

[0060] In one embodiment, the glass transition temperature of the carboxy polyester resin is 56°C, the softening point of the carboxy polyester resin is 110°C, and the viscosity of the carboxy polyester resin at a temperature of 165°C is 40Pa. s, the acid value of the carboxyl polyester resin is 24 mgKOH / g.

[0061] In one embodiment, the epoxy resin is one-step E-12 epoxy resin.

[0062] In one embodiment, the matting agent is an indoor acrylic matting agent, and the epoxy equivalent of the matting...

Embodiment 2

[0067] A kind of IT product special-purpose indoor matte plane sand texture skin touch powder coating formula is as follows:

[0068] Carboxylated polyester resin 13%

[0069] Epoxy 42%

[0070] Acrylic matting agent 17.5%

[0071] Leveling agent 1.0%

[0072] Benzoin 0.5%

[0073] Brightener 0.8%

[0074] Special toughener 1.0%

[0075] Wear-resistant wax 1.0%

[0076] Catalyst 0.02%

[0077] Calcium Carbonate 9%

[0078] Extinct Barium 13.38%

[0079] Carbon black 0.8%.

[0080]In one embodiment, the glass transition temperature of the carboxy polyester resin is 57°C, the softening point of the carboxy polyester resin is 105°C, and the viscosity of the carboxy polyester resin at a temperature of 165°C is 43Pa. s, the acid value of the carboxy polyester resin is 25 mgKOH / g.

[0081] In one embodiment, the epoxy resin is one-step E-12 epoxy resin.

[0082] In one of the embodiments, the matting agent is an indoor acrylic matting agent, and the epoxy equivalent of t...

Embodiment 3

[0087] A kind of IT product special-purpose indoor matte plane sand texture skin touch powder coating formula is as follows:

[0088] Carboxylated polyester resin 14.5%

[0089] Epoxy 41%

[0090] Acrylic Matting Agent 18%

[0091] Leveling agent 1.0%

[0092] Benzoin 0.5%

[0093] Brightener 0.8%

[0094] Special toughener 1.3%

[0095] Wear Wax 1.2%

[0096] Catalyst 0.03%

[0097] Calcium Carbonate 8%

[0098] Dull barium 12.87%

[0099] Carbon black 0.8%.

[0100] In one embodiment, the glass transition temperature of the carboxy polyester resin is 59°C, the softening point of the carboxy polyester resin is 118°C, and the viscosity of the carboxy polyester resin at a temperature of 165°C is 45Pa. s, the acid value of the carboxy polyester resin is 25 mgKOH / g.

[0101] In one embodiment, the epoxy resin is one-step E-12 epoxy resin.

[0102] In one embodiment, the matting agent is an indoor acrylic matting agent, and the epoxy equivalent of the matting agent is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
softening pointaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses an indoor lightless flat sand-textured powder coating having skin tactility and specially used for IT products. The powder coating comprises carboxyl polyester resin, epoxy resin, an acrylic flatting agent, a leveling agent, benzoin, a brightener, a special toughening agent, wear-resistant wax, a catalyst, extinction barium sulfate, calcium carbonate and carbon black. The flat sand-textured powder coating having skin tactility is prepared by matching the carboxyl polyester resin, the acrylic flatting agent and the special toughening agent, shows an extremely fine sand texture state and a strong sand feeling under a naked eye viewing condition, but has a flat tactility and strong soft skin tactility, so the powder coating is suitable for being applied to IT electronic information products and indoor furniture products, and the soft skin tactility of the powder coating is close to the fit degree, the comfort and the softness of human skins; and the powder coatingalso has excellent mechanical properties and excellent scratch resistance under a low gloss condition, and is functional new functional having the advantage of convenience in material drawing, convenience in preparation and low cost.

Description

technical field [0001] The invention relates to the field of chemical powder coatings, in particular to an indoor matte plane sand grain skin touch powder coating specially used for IT products. Background technique [0002] Powder coating is a 100% solid powder that does not contain organic solvents. It is different from oil-based paints and water-based paints. It does not use solvent or water as a dispersion medium when coating, but uses air as a dispersion medium to evenly coat the workpiece. The surface is a new type of environmentally friendly paint that forms a special-purpose coating film after heating. Powder coating has the characteristics of no VOC, environmental protection, energy saving, high construction efficiency and wide application range. [0003] At present, most of the appearance of sand grains on the market is obtained by adding sand grain agents, and most of the common indoor matt flat powder coatings are obtained by adding chemical matting agent XG603-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D167/00C09D5/03C09D7/61C09D7/63C09D7/65
CPCC08K2003/265C08K2003/3045C08L2205/035C09D5/033C09D163/00C08L67/00C08L91/06C08L61/02C08K13/02C08K3/26C08K3/04C08K5/09C08K3/30
Inventor 文佳军
Owner 广东华彩粉末科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com