Method for preparing lithium-sulfur battery anode based on catalysis of active MnO2

A lithium-sulfur battery and sulfur electrode technology, applied in electrode manufacturing, battery electrodes, lithium batteries, etc., can solve the problems of high ratio of mass and volume of inactive substances, affecting the practical application of lithium-sulfur batteries, reducing the advantages of lithium-sulfur batteries, etc. , to achieve the effect of suppressing the shuttle effect, facilitating high-rate discharge, and avoiding the loss of active material sulfur

Active Publication Date: 2018-04-06
天津赫维科技有限公司
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although the above method inhibits the dissolution of polysulfides and improves the cycle life of the sulfur electrode, the method is complicated, and the mass and volume ratio of inactive materials is very high, which seriously reduces the advantages of lithium-sulfur batteries in terms of specific energy. Affected the practical application of lithium-sulfur batteries

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing lithium-sulfur battery anode based on catalysis of active MnO2
  • Method for preparing lithium-sulfur battery anode based on catalysis of active MnO2

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Preparation of active manganese dioxide: Weigh 108.79g manganese dioxide (produced in Hunan, battery grade, purity 91%), 0.51g Fe(NO 3 ) 3 9H 2 O (Tianjin Chemical Reagent Factory, analytically pure, purity 98.5%), 0.51g Ni(NO 3 ) 2 ·6H 2 O (Tianjin Chemical Reagent Factory, analytically pure, purity 98%) and 25.25 g of anhydrous LiNO 3 (Shanghai Zhongli, analytically pure, content 99%), put it in a ball mill tank, the ratio of ball to material is 3:1, the speed is 300 rpm, take it out after ball milling for 3 hours, and then put the powder in the sintering furnace at 1°C Raise the temperature to 350°C / min, keep it for 6 hours, take it out after cooling down to room temperature, and then ball mill it to 325 mesh to obtain active manganese dioxide powder.

[0013] Weigh 85g of nano-sulfur powder (Shanghai Yaotian New Material Technology Co., Ltd.), 10g of active manganese dioxide powder (self-made), 1g of 6mm chopped carbon fiber (Shanghai Lishuo Composite Material ...

Embodiment 2

[0017] Preparation of active manganese dioxide: same as Example 1.

[0018] Weigh 90g of nano-sulfur powder (Shanghai Yaotian New Material Technology Co., Ltd.), 5g of active manganese dioxide powder (self-made), 1g of 10mm chopped carbon fiber (Shanghai Lishuo Composite Material Technology Co., Ltd.) and 1g of multi-walled carbon nanotubes (Jiangsu Xianfeng Nano Material Technology Co., Ltd.), put it into a mortar, grind it evenly, pour it into a beaker, and add 97g of absolute ethanol, stir it with a glass rod to form a slurry, and then add 8.33g of 60% mass concentration Polytetrafluoroethylene emulsion, continue to stir to form a paste, use a scraper to spread the paste evenly on a 0.3mm thick hydrophilic carbon fiber cloth (Shanghai Lishuo Composite Material Technology Co., Ltd.), coating load 8mg / cm 2 . Then put it in an oven, heat to 120° C. to dry for 20 minutes under the condition of nitrogen protection, cool down, take it out, and obtain a sulfur electrode. On the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing a lithium-sulfur battery anode based on catalysis of active MnO2. The method comprises the following steps: uniformly mixing nano-sulfur simple substance powder, activated manganese dioxide powder, carbon fibers and carbon nano-tubes in a proportion (mass ratio) of (85-90) to (5-10) to 1 to 1, adding absolute ethyl alcohol which has equal mass with the mixture, stirring to obtain a slurry, adding a certain amount of polytetrafluoroethylene (PTFE) emulsion, stirring to obtain paste, uniformly smearing carbon fiber cloth with the paste, heating to120 DEG C under the protection of nitrogen, and heating for 20 minutes, so as to obtain a sulfur electrode. By activating manganese dioxide, the surface of manganese dioxide is adsorbed with particlesof Fe, Ni and the like, and the oxidation reduction of sulfur is integrally catalyzed, so that the charge and discharge electric current densities of the sulfur electrode are increased, high-rate discharging is promoted, more importantly, the unit area capacity of the sulfur electrode can be increased, and a foundation is provided for the preparation of a lithium-sulfur battery with specific energy higher than 700Wh / kg.

Description

technical field [0001] The present invention relates to a kind of active MnO-based 2 The invention discloses a method for preparing a positive electrode of a catalyzed lithium-sulfur battery, which belongs to the technical field of chemical power source energy storage. Background technique [0002] Lithium-sulfur batteries are a chemical power source with great development potential. The theoretical capacity of the sulfur cathode is as high as 1670mAh / g, and the theoretical specific energy of the lithium-sulfur battery reaches 2600Wh / kg. At the same time, lithium-sulfur batteries have little impact on the environment, and sulfur resources are very rich, cheap, and easy to mine. These advantages have prompted researchers to pay more and more attention to the development of lithium-sulfur batteries. [0003] The advantages of lithium-sulfur batteries are obvious, but there are still many problems to be solved urgently, mainly due to the poor conductivity and low utilization ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/62H01M4/139H01M4/04H01M10/052
CPCH01M4/0404H01M4/0471H01M4/139H01M4/62H01M4/628H01M10/052Y02E60/10
Inventor 郝德利叶丽光
Owner 天津赫维科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com